Zn (1-x) Ga x O thin films (x = 0.01, 0.03, 0.05, 0.07 named as GZO1, GZO2, GZO3, GZO4, respectively) were deposited on glass substrates by RF magnetron sputtering. The crystal structure, electrical, thermoelectric and magneto-thermoelectric properties of GZO films were investigated. It is found that all the GZO films are polycrystalline and preferentially oriented in the c-axis. The electrical resistivity of GZO films decreased first with increasing Ga doping content before it reached a minimum at x = 0.05, and then increased with further increasing Ga doping content. The magnetic fields (B) ranging from 0 to 1.5 T are perpendicularly applied to the films to study the magneto-thermoelectric properties. It is observed that the absolute values of Seebeck coefficients (|S|) of GZO1, GZO2, GZO3 show marked variation with magnetic field and obtain the maximum value at B = 0.5 T. Whereas the |S| value of GZO4 fluctuates slightly with magnetic field and reaches its peak at B = 1.0 T. The magneto-thermoelectric properties are analyzed and we propose that this behavior is mainly attributed to the effect of magnetic field on the electron transport.
Thermoelectric Properties of Zn0.98Al0.02O Thin Films Prepared by RF Magnetron Sputtering