2073) Study on Shear Strength of Reinforced Concrete Beams with Opening(Structure)

This paper reports experimental data on the structural performance of disturbed regions in reinforced concrete beams with corrosion damage to the embedded steel stirrups. A total of 15 reinforced concrete beams were constructed and tested. The test beams were 350 mm deep, 125 mm wide, and 1850 mm long. The beams were tested in three-point bending under a simply supported span of 1500 mm. Nine beams had the embedded stirrups subjected to accelerated corrosion. The test variables were the corrosion damage level and the shear span-to-depth ratio. The test results indicated that the corroded beams exhibited reduced shear strength in comparison to the uncorroded control specimens. The shear strength reduction was up to 53%. Furthermore, the reduction in shear strength due to the corrosion was found to be greater at smaller shear span-to-depth ratios.

Download Full-text

Experimental Investigation of Shear Strength for Steel Fibre Reinforced Concrete Beams

The Open Construction and Building Technology Journal ◽

10.2174/1874836802115010081 ◽

2021 ◽

Vol 15 (1) ◽

pp. 81-92

Author(s):

Constantinos B. Demakos ◽

Constantinos C. Repapis ◽

Dimitros P. Drivas

Keyword(s):

Tensile Strength ◽

Compressive Strength ◽

Shear Strength ◽

Reinforced Concrete ◽

Steel Fibre ◽

Concrete Beams ◽

Reinforced Concrete Beams ◽

Fibre Reinforced Concrete ◽

Steel Fibres ◽

Steel Fibre Reinforced Concrete

Aims: The aim of this paper is to investigate the influence of the volume fraction of fibres, the depth of the beam and the shear span-to-depth ratio on the shear strength of steel fibre reinforced concrete beams. Background: Concrete is a material widely used in structures, as it has high compressive strength and stiffness with low cost manufacturing. However, it presents low tensile strength and ductility. Therefore, through years various materials have been embedded inside it to improve its properties, one of which is steel fibres. Steel fibre reinforced concrete presents improved flexural, tensile, shear and torsional strength and post-cracking ductility. Objective: A better understanding of the shear performance of SFRC could lead to improved behaviour and higher safety of structures subject to high shear forces. Therefore, the influence of steel fibres on shear strength of reinforced concrete beams without transverse reinforcement is experimentally investigated. Methods: Eighteen concrete beams were constructed for this purpose and tested under monotonic four-point bending, six of which were made of plain concrete and twelve of SFRC. Two different aspect ratios of beams, steel fibres volume fractions and shear span-to-depth ratios were selected. Results: During the experimental tests, the ultimate loading, deformation at the mid-span, propagation of cracks and failure mode were detected. From the tests, it was shown that SFRC beams with high volume fractions of fibres exhibited an increased shear capacity. Conclusion: The addition of steel fibres resulted in a slight increase of the compressive strength and a significant increase in the tensile strength of concrete and shear resistance capacity of the beam. Moreover, these beams exhibit a more ductile behaviour. Empirical relations predicting the shear strength capacity of fibre reinforced concrete beams were revised and applied successfully to verify the experimental results obtained in this study.