Innovative double-sided welding is expected to improve the fatigue resistance of rib-to-deck welded joints of orthotropic steel decks (OSDs). Welding crack-like defects are the crucial issue affecting the fatigue performance of rib-to-deck double-sided welded joints. This study presents a numerical simulation of three-dimensional (3D) mixed mode fatigue crack growth behavior of rib-to-deck double-sided welded joints of OSDs. Maximum tensile stress theory and equivalent stress intensity factor (SIF) were used to simulate mixed mode fatigue cracks growth. The Paris law model was employed to predict the fatigue life. Fatigue cracks of rib-to-deck double-sided welded joints were characterized by the presence of mixed mode cracks of modes I (open), mode II (shear), and mode III (tear), which was dominated by mode I. The equivalent SIF was found to be complex at the growth stage with the maximum value at the two ends of the crack front and the minimum value at the midpoint of the crack front. The crack shape became flatter in the later phase of the crack growth. The fatigue crack surface underwent deflections during crack growth, making the final crack shape exhibiting the characteristic of a spatial curved surface. The initial crack geometry showed a significant impact on the fatigue life.
Impact of high-frequency peening and marine atmosphere on the cyclic life of t-welded joints with surface fatigue cracks