scholarly journals Efficacy of Fiber Post Bonding To Root Dentin after Different Obturation Techniques and Cementation Timings: In Vitro Study

2018 ◽  
Vol 6 (9) ◽  
pp. 1707-1711
Author(s):  
Rami M. Atia ◽  
Nada Omar ◽  
Haidy Nabil ◽  
Yousra Aly
Keyword(s):  
Bond Strength ◽  
Statistical Significance ◽  
Testing Machine ◽  
In Vitro Study ◽  
Resin Cement ◽  
Vitro Study ◽  
Endodontically Treated Teeth ◽  
Root Dentin ◽  
Push Out

OBJECTIVE: The aim of this in vitro study was to assess the effect of obturation technique and cementation timings on the bonding of fibre-reinforced posts to the root canal walls. METHODS: Twenty extracted teeth were randomly allocated to two groups according to the obturation technique and cementation timing. Central incisors with single canals were used after being decoronated. Every extracted tooth of the {vertical compaction group} (VC) group (n = 10) had been obturated using the {E & Q plus obturation system} with posts cemented in the same day; The other (CO) conventional group (n = 10) teeth were obturated using the conventional lateral compaction technique and posts cemented after one week. “SF“ Fiber posts were used after bonding and cementation using Rely X ARC resin cement with all the endodontically treated teeth. The push-out test was performed in a universal testing machine. Data were analysed by 2 way analysis of variance with Statistical significance was set to 0.05. RESULTS: Heat softened gutta percha group showed more push out the bond strength of the bonded posts than the conventional obturation group (p < 0.05). In the middle region, there was no statistical significance between the two groups while there was significance in the coronal and apical thirds. CONCLUSION: The vertical compaction technique and early cementation improved the bond strength of the resin posts in comparison to the conventional obturation technique with late cementation.

scholarly journals Effect of acidic environment and intracanal medicament on push-out bond strength of biodentine and mineral trioxide aggregate plus: an in vitro study

2019 ◽  
Author(s):  
Priyanka Jain ◽  
Zinnie Nanda ◽  
Rahul Deore ◽  
Amit Gandhi
Keyword(s):  
Bond Strength ◽  
Calcium Hydroxide ◽  
Testing Machine ◽  
Mineral Trioxide Aggregate ◽  
In Vitro Study ◽  
Vitro Study ◽  
Acidic Environment ◽  
Significant Difference ◽  
Push Out

Introduction. This in-vitro study aims to evaluate the effect of acidic environment and intracanal medicament on push out bond strength of Biodentine and Mineral Trioxide Aggregate Plus (MTA Plus) Method. Forty extracted single rooted teeth were sectioned below the cement-enamel junction. The root canals were instrumented using rotary files and then peeso reamer was used to obtain standardized root canal dimension. Specimens were randomly classified into following groups- Group 1: calcium hydroxide in the absence of acidic environment; Group 2: calcium hydroxide in the presence of acidic environment; Group 3: no intracanal medicament in the absence of acidic environment; Group 4: no intracanal medicament in the presence of acidic environment. Specimens were kept for 7 days at room temperature. Thereafter, specimens of each group were transversely sectioned into 1 mm thick slices and divided into 2 sub-groups according to the use of biodentine and MTA Plus. Using Universal Testing Machine, push out bond strength test was carried out and the data were analyzed statistically. Results. There was no statistically significant difference  in the bond strength of biodentine and MTA Plus (P>0.05). For both MTA Plus and biodentine, with or without calcium hydroxide, the push out bond strength was less in acidic environment and this difference was more pronounced without calcium hydroxide. In all the four groups, MTA plus showed comparable bond strength to biodentine. Conclusion. MTA Plus is a viable option for apexification. The push out bond strength of Biodentine and MTA Plus is impaired by acidic environment. Prior application of calcium hydroxide slightly increased the bond strength, though the difference was statistically  insignificant.    

scholarly journals The Influence of Crown Ferrule on Fracture Resistance of Endodontically Treated Maxillary Central Incisors

2017 ◽  
Vol 21 (1) ◽  
pp. 44-49
Author(s):  
Sasho Jovanovski ◽  
Julie Popovski ◽  
Alesh Dakskobler ◽  
Ljubo Marion ◽  
Peter Jevnikar
Keyword(s):  
Fracture Resistance ◽  
Testing Machine ◽  
In Vitro Study ◽  
Resin Cement ◽  
Vitro Study ◽  
Endodontically Treated Teeth ◽  
Failure Patterns ◽  
Group A ◽  
Group B

SummaryBackground: Prefabricated zirconia posts can contribute to increasing the fracture resistance of the endodontically treated teeth. Purpose. This in vitro study compared the fracture resistance of endodontically treated central maxillary incisors prepared with 2 mm ferrule length to the ones without ferrule.Material and methods: Twenty-four caries-free maxillary central incisors were divided into 2 groups of 12. In group A circumferential external dentin shoulders were prepared for 2 mm external dentin ferrule length. There was no ferrule preparation in Group B. Zirconia VALLPOST BO-S (Ø 1,6 mm), Ljubljana, Slovenia were used with retention forms in the coronary part. Core build-up was made of pressed ceramics (IPS e.max Press, Ivoclar, Liechtenstein). Crowns were manufactured from the same ceramic material (IPS e.max Press, Ivoclar). After root canal treatment and post space preparation, all posts were cemented with an adhesive resin cement (Multilink Automix, Ivoclar). The specimens were embedded in acrylic resin blocks (ProBase Polymer/Monomer, Ivoclar) and loaded at an angle of 45° to the long axis in an Instron Testing Machine 4301 (Instron Corp., USA) at a crosshead speed of 1 mm/min until fracture. Fracture patterns and loads were recorded. A significance level of p<0.05 was used for all comparisons. Two-way analysis of variance was used for statistical analysis. Failure patterns were analyzed with the optical microscope Stereo Discovery V.8 (Carl Zeiss, Germany) and compared using the chi-square nonparametric test.Results: The mean values (±SD) of fracture loads (N) for the Groups A and B were 664.63N (±49.14) and 519.36N (±71.65) recpectively. Significantly lower failure loads were recorded for the specimens in the group B. Failure patterns within the groups revealed non-catastrophic failure in 70% of the specimens for group A and 85% for group B.Conclusions: Within the limitations of this in vitro study, it can be concluded that zirconia VALLPOST BO-S (Ø 1,6 mm) with press-ceramic cores and crowns, can be used for restoration of endodontically treated teeth. The teeth prepared with 2 mm external dentin ferrule length were found to be more fracture resistant than teeth without ferrule.

scholarly journals Micro Push-Out Bond Strength of Resin Composite to Dentin in Primary Dentition Using Three Universal Adhesives with Different pH: An In Vitro Study

2021 ◽  
Vol 11 (14) ◽  
pp. 6349
Author(s):  
Regina María Del Río Carrillo ◽  
Pedro Molinero-Mourelle ◽  
Vicente Vera ◽  
Pablo Romero Villaba ◽  
Elizabeth Casañas ◽  
...  
Keyword(s):  
Bond Strength ◽  
Resin Composite ◽  
In Vitro Study ◽  
Primary Dentition ◽  
Vitro Study ◽  
Deciduous Tooth ◽  
Universal Adhesives ◽  
Type Of Failure ◽  
Push Out

To evaluate the bond strength of different universal adhesives on deciduous tooth dentineand their relationship with the composition and potential of hydrogen (pH). Methods: An in vitromicro push-out test on 150 samples (n = 50) per group per adhesive, namely, Adhese Universal(ADH; Ivoclar Vivadent), Futurabond U (FUT; Voco GmbH) (Test), and Scotchbond Universal withpre-conditioning (SCO; 3M) (Control), to record bond strength (BS) and type of adhesive failure.Results: The results of the different adhesives (megapascals (MPa)) varied, showing no statisticalsignificance. The corresponding averages are in MPa: ADH, 13.66 2.81; FUT, 14.48 2.88; SCO,14.98 3.96. Additionally, the frequency of type of failure was as follows: mixed (60.7%), adhesive(27.3%), and cohesive (12%). Conclusions: SCO, with a pH of 2.7, showed greater resistance tofracture, while FUT, with a pH of 2.3 and no pre-conditioning, approached the same values, being aone-step adhesive. No relationship was found between failure and type of adhesive.