Investigation of Electromagnetic Interference Shielding Effectiveness of Cement-Based Composites Filled with Carbon Materials

2010 ◽  
Vol 168-170 ◽  
pp. 1021-1024
Author(s):  
Guo Xuan Xiong ◽  
Zhi Bin Zhang ◽  
Min Deng ◽  
Yu Fen Zhou
Keyword(s):  
Carbon Fiber ◽  
Carbon Black ◽  
Electromagnetic Interference ◽  
Carbon Materials ◽  
Shielding Effectiveness ◽  
Nano Carbon ◽  
Electromagnetic Interference Shielding Effectiveness ◽  
Carbon Nano Tube ◽  
Relationship Of ◽  
The Relationship

The cement-based composite shielding materials filled with carbon materials such as ordinary carbon materials (graphite, coke and carbon black), carbon fiber and nano-carbon materials (carbon nano-tube and nano-carbon black) were prepared. The relationship of conductivity and shielding effectiveness in a frequency range of 100 KHz~1.5 GHz was studied. The electric properties of cement-based composites filled with carbon fiber is better than other carbon materials. With the contents of carbon fiber of 5.vol%, the average shielding effectiveness is about 37 dB and the maximum shielding effectiveness reaches 40 dB.

scholarly journals Robust Design of PC/ABS Filled with Nano Carbon Black for Electromagnetic Shielding Effectiveness and Surface Resistivity

Processes ◽  
2020 ◽  
Vol 8 (5) ◽  
pp. 616
Author(s):  
Wipoo Sriseubsai ◽  
Arsarin Tippayakraisorn ◽  
Jun Wei Lim
Keyword(s):  
Carbon Black ◽  
Electromagnetic Interference ◽  
Electrostatic Discharge ◽  
Acrylonitrile Butadiene Styrene ◽  
Surface Resistivity ◽  
Shielding Effectiveness ◽  
Electromagnetic Interference Shielding Effectiveness ◽  
Electromagnetic Shielding Effectiveness ◽  
Emi Se ◽  
Butadiene Styrene

This study focuses on the electromagnetic interference shielding effectiveness (EMI SE), dissipation of electrostatic discharge (ESD), and surface resistivity of polymer blends between polycarbonate (PC) and acrylonitrile–butadiene–styrene (ABS) filled with carbon black powder (CBp) and carbon black masterbatch (CBm). The mixtures of PC/ABS/CB composites were prepared by the injection molding for the 4-mm thickness of the specimen. The D-optimal mixture design was applied in this experiment. The EMI SE was measured at the frequency of 800 and 900 MHz with a network analyzer, MIL-STD-285. The result showed that the EMI SE was increased when the amount of filler increased. The surface resistivity of the composites was determined according to the ASTM D257. It was found that the surface resistivity of the plastic with no additives was 1012 Ω/ square. When the amount of fillers was added, the surface resistivity of plastic composites decreased to the range of 106–1011 Ω/square, which was suitable for the application without the electrostatic discharge. The optimization of multi-response showed using high amounts of PC and CB was the best mixture of this research.

Sign in / Sign up

Export Citation Format

Share Document