Evaluation of Internal Crack Growth of PPS Thrust Bearings under Rolling Contact Fatigue in Water

2021 ◽  
Vol 888 ◽  
pp. 77-81
Author(s):  
Shintaro Kanagawa ◽  
Takahiro Matsueda ◽  
Katsuyuki Kida ◽  
Yuji Kashima
Keyword(s):  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Internal Crack ◽  
Subsurface Crack ◽  
Direction Parallel ◽  
Thrust Bearings ◽  
Full Cross Section ◽  
Observation Method ◽  
Circular Cracks

In this study, in order to evaluate the progress of internal cracks in PPS thrust bearings under rolling contact fatigue in water, cracks were observed by a full-cross-section observation method using a lathe machining. “Main subsurface crack” initiated at the surface toward the inside, then grew in a direction parallel to the surface. They connected with many “Semi-circular cracks” initiating at the surface from the opposite side to the inside, to from a semi-ellipsoidal flaking damage. It was found that the “Semi-circular cracks” and the “Main subsurface crack” dominated the flaking destruction.

Observation of Surface and Subsurface Crack Propagation in PPS Thrust Bearings under Rolling Contact Fatigue in Water

2021 ◽  
Vol 1020 ◽  
pp. 120-125
Author(s):  
Syunsuke Mizozoe ◽  
Takahiro Matsueda ◽  
Katsuyuki Kida ◽  
Yuji Kashima
Keyword(s):  
Crack Propagation ◽  
Contact Area ◽  
Rolling Contact Fatigue ◽  
Rolling Direction ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Direction Parallel ◽  
Thrust Bearings ◽  
Subsurface Cracks ◽  
Circular Cracks

In this study, crack propagation in PPS thrust bearings under rolling contact fatigue (RCF) in water was observed in order to investigate the relation between cracks and flakings. RCF tests in water under loads of 700 N and 900 N were performed. The semi-circular cracks propagated in a direction perpendicular to the rolling direction were observed under a load of 700 N. The line cracks propagated in a direction parallel to the rolling direction at periphery of contact area and the semi-circular cracks were observed under a load of 900 N. To study the subsurface cracks, full section of rolling contact area was observed. It is concluded that the flaking mechanism in PPS thrust bearing has three features as follows: Initiation and propagation of surface cracks depend on the load; When load is 700N, the semi-circular cracks growing from the surface and the cracks branching from the main subsurface cracks join to form the flaking; When load is 900N the line cracks and the semi-circular cracks growing from the surface join to form the flaking.

Internal Shear Stress Distribution and Subsurface Cracks of PPS Thrust Bearings under Rolling Contact Fatigue in Water

2020 ◽  
Vol 858 ◽  
pp. 101-105
Author(s):  
Syunsuke Mizozoe ◽  
Katsuyuki Kida
Keyword(s):  
Shear Stress ◽  
Stress Distribution ◽  
Crack Propagation ◽  
Contact Stress ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Subsurface Crack ◽  
Thrust Bearings ◽  
Subsurface Cracks

In this study, crack propagation in PPS thrust bearings under rolling contact fatigue (RCF) in water was observed, and relation between subsurface crack and internal shear stress parallel to the surface was investigated. It was found the cause of flaking was subsurface crack. They were evaluated in terms of contact stress and friction between their faces. It was discovered that subsurface cracks distributed around shear stress peak, and flaking failure was dominated by subsurface shear stress.

Observation of Cracks of PEEK Polymer Thrust Bearings under Rolling Contact Fatigue in Water

2016 ◽  
Vol 703 ◽  
pp. 172-177 ◽  
Author(s):  
Xiao Chen Shi ◽  
Masaya Orito ◽  
Yuji Kashima ◽  
Koshiro Mizobe ◽  
Katsuyuki Kida
Keyword(s):  
Corrosion Resistance ◽  
Friction Coefficient ◽  
Cross Sections ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Light Weight ◽  
Low Friction ◽  
High Corrosion Resistance ◽  
Thrust Bearings

Considering the advantages on light weight, low friction coefficient, high corrosion resistance and electric insulation, polymer bearings are widely used under certain environments, where the toughness like metal bearings is not necessary. In our previous study, it was concluded that the main reason for PEEK thrust bearings failure in water was flaking due to surface crack propagation. In the present study, crack observations were made on groove surfaces and cross sections along both radial and rolling directions in order to find the relation between cracks and flaking failures.

Observation of Fatigue Fracture on PEEK Shaft against Alumina Bearing’s Ball under One-Point Rolling Contact

2016 ◽  
Vol 878 ◽  
pp. 137-141 ◽  
Author(s):  
Hitonobu Koike ◽  
Genya Yamaguchi ◽  
Koshiro Mizobe ◽  
Yuji Kashima ◽  
Katsuyuki Kida
Keyword(s):  
Fatigue Fracture ◽  
Rolling Contact Fatigue ◽  
Rolling Direction ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Hertzian Contact ◽  
Subsurface Crack ◽  
Mechanical Elements ◽  
The One ◽  
Alumina Ball

Tribological fatigue failure of the machined PEEK shaft was investigated through the one-point type rolling contact fatigue test between a PEEK shaft and an alumina ball, in order to explore fatigue fracture mechanism of frictional parts working at high frequency in various mechanical elements. Due to Hertzian contact of cyclic compressive stress, the subsurface crack occurred within approximately 300 μm depth from thesurface and propagated along the rolling direction. After that, the subsurface crack propagation direction changed toward the surface. The flaking occurred on the raceway of the PEEK shaft when the subsurface crack reached to the PEEK shaft surface.

Effect of PTFE Retainer on Friction Coefficient in Polymer Thrust Bearings under Dry Contact

2013 ◽  
Vol 683 ◽  
pp. 90-93 ◽  
Author(s):  
Koshiro Mizobe ◽  
Takashi Honda ◽  
Hitonobu Koike ◽  
Edson Costa Santos ◽  
Yuji Kashima ◽  
...  
Keyword(s):  
Friction Coefficient ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Fatigue Tests ◽  
Rolling Contact ◽  
Low Friction ◽  
Friction Forces ◽  
Thrust Bearings ◽  
Dry Contact

Polyetheretherketone (PEEK) is a tough semi-crystalline thermoplastic polymer with excellent mechanical properties. While abilities of polyphenylenesulfide (PPS) are similar to PEEK, former material cost was lower than later. Polytetrafluoroethylene (PTFE) is well known because of its low friction coefficient and self lubrication ability. The objective of this study is to observe the friction coefficient of hybrid bearings, PTFE retainer sandwiched with PPS-races or PEEK-races. Rolling contact fatigue tests were performed and in situ friction forces wear measured. It is concluded that the PTFE retainer reduced friction coefficient.

Subsurface Stress Distribution and Failure of PPS Thrust Bearings under Rolling Contact Fatigue in Water

2019 ◽  
Vol 814 ◽  
pp. 152-156 ◽  
Author(s):  
Xiao Chen Shi ◽  
Akihiro Adachi ◽  
Katsuyuki Kida
Keyword(s):  
Fatigue Crack ◽  
Stress Distribution ◽  
Crack Propagation ◽  
Fatigue Crack Propagation ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Polymer Materials ◽  
Thrust Bearings ◽  
Subsurface Stress

In recent years, environments of bearings and polymer materials have been more and more attractive due to several advantages against ordinary metal material. However, there is still room for the further study about strength of polymer bearings. One of questions is the mechanism of fatigue crack propagation, which is the main cause of the damage of polymer bearings under rolling contact with lubricant, like water. In this study, subsurface stress distribution and failure of PPS thrust bearings under rolling contact fatigue in water are discussed to understand the detail of the crack propagation.

Observation of Wear in PEEK Race - PTFE Retainer Hybrid Polymer Bearings under Dry Contact

2012 ◽  
Vol 457-458 ◽  
pp. 557-562 ◽  
Author(s):  
Koshiro Mizobe ◽  
Edson Costa Santos ◽  
Takashi Honda ◽  
Hitonobu Koike ◽  
Katsuyuki Kida ◽  
...  
Keyword(s):  
Wear Track ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Wear Loss ◽  
Hybrid Polymer ◽  
Wear Properties ◽  
Thrust Bearings ◽  
Dry Contact ◽  
Materials Used

In order to establish an optimal combination of materials used for polymer thrust bearings, two types of components (polyetheretherketone (PEEK) races - polytetrafluoroethylene (PTFE) retainer and PEEK races – PEEK retainer) were tested by rolling contact fatigue. Their wear properties were investigated and it was concluded that using a PTFE retainer, the wear loss was improved due to PTFE wear debris attaching to the wear track and acting as a lubricant.

Effect of Rotation Speeds on Friction Coefficients of PPS Race-PTFE Retainer Hybrid Polymer Thrust Bearings under Dry Contact

2013 ◽  
Vol 418 ◽  
pp. 205-208 ◽  
Author(s):  
Xiao Chen Shi ◽  
Koshiro Mizobe ◽  
Yuji Kashima ◽  
Katsuyuki Kida
Keyword(s):  
Friction Coefficient ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Fatigue Tests ◽  
Rolling Contact ◽  
Wear Loss ◽  
Hybrid Polymer ◽  
Thrust Bearings ◽  
Dry Contact ◽  
Thrust Load

In the previous study on PPS race-PTFE retainer Hybrid polymer bearings, the relationship between thrust load, rotation speeds and wear loss under dry condition was investigated. It was found that the wear loss obviously changed under the thrust load ranging from 400N to 500N at the rotation speeds of 450rpm and 600rpm. The object of this study is to observe the friction coefficient at the rotation speeds ranging from 450rpm and 600N under thrust load of 400N. Rolling contact fatigue tests were performed and it was concluded that friction coefficient decreases with the rotation speeds.