Effects of Two Polypropylene Fibers on the Properties of High Strength Concrete

2013 ◽  
Vol 357-360 ◽  
pp. 1328-1331
Author(s):  
Bai Rui Zhou ◽  
Dong Dong Han ◽  
Jian Hua Yang ◽  
Yi Liang Peng ◽  
Guo Xin Li
Keyword(s):  
Portland Cement ◽  
Modulus Of Elasticity ◽  
High Strength Concrete ◽  
Polypropylene Fiber ◽  
High Strength ◽  
Polypropylene Fibers ◽  
Strength Concrete ◽  
Reticular Fiber ◽  
Binder Ratio ◽  
Water To Binder Ratio

Portland cement, crushed stone, sand and superplasticizer were used to obtain a high strength concrete with a low water to binder ratio. A reticular polypropylene fiber and a single polypropylene fiber were used to improve the strength of the high strength concrete, but the effects of the two fibers on the slump and strengths were quite different. The reasons of the differences were the surface area and the modulus of elasticity of the fibers. The results show the reticular fiber was better to used in high strength concretes.

Performance Deterioration of High Strength Concrete under Mixed Erosion and Freeze-Thaw Cycling

2010 ◽  
Vol 163-167 ◽  
pp. 1655-1660
Author(s):  
Jian Zhang ◽  
Bo Diao ◽  
Xiao Ning Zheng ◽  
Yan Dong Li
Keyword(s):  
Compressive Strength ◽  
Elastic Modulus ◽  
Mass Loss ◽  
Modulus Of Elasticity ◽  
Dynamic Modulus ◽  
High Strength Concrete ◽  
High Strength ◽  
Freeze Thaw ◽  
Strength Concrete ◽  
Dynamic Modulus Of Elasticity

The mechanical properties of high strength concrete(HSC) were experimentally investigated under mixed erosion and freeze-thaw cycling according to ASTM C666(Procedure B), the erosion solution was mixed by weight of 3% sodium chloride and 5% sodium sulfate. The mass loss, relative dynamic modulus of elasticity, compressive strength, elastic modulus and other relative data were measured. The results showed that with the increasing number of freeze-thaw cycles, the surface scaled more seriously; the mass loss, compressive strength and elastic modulus continued to decrease; the relative dynamic modulus of elasticity increased slightly in the first 225 freeze-thaw cycles, then decreased in the following 75 cycles; the corresponding strain to peak stress decreased with the increase of freeze-thaw cycles. After 200 cycles, the rate of deterioration of concrete accelerated obviously.

Properties of High Strength Concrete with Calcined Diatomaceous Earth as Cement Replacement under Compression

2020 ◽  
Vol 402 ◽  
pp. 7-13
Author(s):  
Muttaqin Hasan ◽  
Aris Muyasir ◽  
Taufiq Saidi ◽  
Husaini ◽  
Raudha Azzahra
Keyword(s):  
Compressive Strength ◽  
Modulus Of Elasticity ◽  
High Strength Concrete ◽  
Diatomaceous Earth ◽  
High Strength ◽  
Compression Load ◽  
Strength Concrete ◽  
Cement Replacement ◽  
Concrete Mixtures ◽  
Compressive Strength Of Concrete

In this research, calcined diatomaceous earth from Aceh Besar, Indonesia was used as cement replacement in producing high strength concrete. Four concrete mixtures in which the percentage of cement replacement of 0%, 5%, 10% and 15% by weight were studied. Four cylinder-specimens with 100 mm diameter and 200 mm high were prepared for each mixture. The compression load was applied on the specimens at the age of 28 days until the specimens failed. The mixture without calcined diatomaceous earth was more workable than that with diatomaceous earth. The compressive strength of concrete with diatomaceous earth in this study was almost the same for all mixture. However, those compressive strength was lower than the compressive strength of concrete without calcined diatomaceous earth for about 14.6%. Modulus of elasticity of high strength concrete decreased with increasing of cement replacement percentage.

scholarly journals Fire Performance of Heavyweight Self-Compacting Concrete and Heavyweight High Strength Concrete

Materials ◽  
2019 ◽  
Vol 12 (5) ◽  
pp. 822 ◽  
Author(s):  
Farhad Aslani ◽  
Fatemeh Hamidi ◽  
Qilong Ma
Keyword(s):  
Compressive Strength ◽  
Mass Loss ◽  
Modulus Of Elasticity ◽  
High Strength Concrete ◽  
Elevated Temperatures ◽  
High Strength ◽  
Self Compacting Concrete ◽  
Strength Concrete ◽  
Magnetite Content ◽  
Hardened State

In this study, the fresh and hardened state properties of heavyweight self-compacting concrete (HWSCC) and heavyweight high strength concrete (HWHSC) containing heavyweight magnetite aggregate with 50, 75, and 100% replacement ratio, and their performance at elevated temperatures were explored experimentally. For fresh-state properties, the flowability and passing ability of HWSCCs were assessed by using slump flow, T500 mm, and J-ring tests. Hardened-state properties including hardened density, compressive strength, and modulus of elasticity were evaluated after 28 days of mixing. High-temperature tests were also performed to study the mass loss, spalling of HWSCC and HWHSC, and residual mechanical properties at 100, 300, 600 and 900 °C with a heating rate of 5 °C/min. Ultimately, by using the experimental data, rational numerical models were established to predict the compressive strength and modulus of elasticity of HWSCC at elevated temperatures. The results of the flowability and passing ability revealed that the addition of magnetite aggregate would not deteriorate the workability of HWSCCs and they retained their self-compacting characteristics. Based on the hardened densities, only self-compacting concrete (SCC) with 100% magnetite content, and high strength concrete (HSC) with 75 and 100% magnetite aggregate can be considered as HWC. For both the compressive strength and elastic modulus, decreasing trends were observed by introducing magnetite aggregate to SCC and HSC at an ambient temperature. Mass loss and spalling evaluations showed severe crack propagation for SCC without magnetite aggregate while SCCs containing magnetite aggregate preserved up to 900 °C. Nevertheless, the mass loss of SCCs containing 75 and 100% magnetite content were higher than that of SCC without magnetite. Due to the pressure build-up, HSCs with and without magnetite showed explosive spalling at high temperatures. The residual mechanical properties analysis indicated that the highest retention of the compressive strength and modulus of elasticity after exposure to elevated temperatures belonged to HWSCC with 100% magnetite content.