Experimental Investigation on the Tensile and Fracture Properties of Burst-Prone Coal under Quasistatic Condition

To study the tensile and fracture properties of the specimen under the quasistatic loading, the Brazilian disc splitting method and the notched semicircular bend (NSCB) method were used to test the tensile properties of coal specimens, and the fracture properties of NSCB specimens with different notch depths were tested and analyzed. The applicability of plane strain fracture toughness KIC and J-integral fracture toughness in evaluating the fracture properties of coal specimens was discussed. The influence of notch depth on the fracture toughness measurement of the NSCB specimen was studied. Combined with the surface strain monitoring of specimens during loading and the industrial CT scanning image of damaged specimens, the deformation characteristics of coal specimen under loads and the distribution law of crack after failure were analyzed. The results show that the NSCB test is suitable for measuring the tensile strength of a coal specimen; when the dimensionless notch depth is β = 0.28, the dispersion of plane strain fracture toughness KIC of the NSCB specimen is the smallest. Besides, the plane strain fracture toughness of coal is obviously affected by the notch depth and dimensionless stress intensity factor. The J-integral fracture toughness can be used to effectively evaluate the fracture performance of specimens.

Influence of Vacuum Heat Treatments on Microstructure and Mechanical Properties of M35 High Speed Steel

Towards the end of the last century, vacuum heat treatment of high speed steels was increasingly used in the fabrication of precision cutting tools. This study investigates the influence of vacuum heat treatments at different pressures of quenching gas on the microstructure and mechanical properties of taps made of M35 high speed steel. Taps were characterized by optical microscopy, scanning electron microscopy with energy dispersive spectroscopy, X-ray diffraction, apparent grain size and Vickers hardness measurements, and scratch tests. Failure analysis after tapping tests was also performed to determine the main fracture mechanisms. For all taps, the results showed that microstructures and the values of characteristics of secondary carbides, retained austenite, apparent grain size and Vickers hardness were comparable to previously reported ones for vacuum heat treated high speed steels. For taps vacuum heat treated at six bar, the highest plane strain fracture toughness was due to a higher content of finer small secondary carbides. In contrast, the lowest plane strain fracture toughness of taps vacuum heat treated at eight bar may be due to an excessive amount of finer small secondary carbides, which may provide a preferential path for crack propagation. Finally, the predominant fracture mechanism of taps was quasi-cleavage.