Effects of Material Composition on Corrosion Fatigue Crack Growth of Austenitic Stainless Steels in High Temperature Water

2012 ◽  
pp. 561-579 ◽  
Author(s):  
Norman Platts ◽  
David Tice ◽  
Kevin Mottershead ◽  
Laura Mcintyre ◽  
Fabio Scenini
Keyword(s):  
Fatigue Crack ◽  
High Temperature ◽  
Fatigue Crack Growth ◽  
Crack Growth ◽  
Corrosion Fatigue ◽  
Stainless Steels ◽  
Austenitic Stainless Steels ◽  
Corrosion Fatigue Crack ◽  
Corrosion Fatigue Crack Growth ◽  
Temperature Water

Corrosion-Fatigue Crack Growth in Age-Hardened Al Alloys: Examples of Failures and Explanations for Fractographic Observations

2014 ◽  
Vol 891-892 ◽  
pp. 248-253 ◽  
Author(s):  
Rohan Byrnes ◽  
Noel Goldsmith ◽  
Mark Knop ◽  
Stan Lynch
Keyword(s):  
Fatigue Crack ◽  
Fatigue Crack Growth ◽  
Crack Growth ◽  
Corrosion Fatigue ◽  
Compact Tension ◽  
Al Alloys ◽  
Corrosion Fatigue Crack ◽  
Crack Tips ◽  
Corrosion Fatigue Crack Growth ◽  
Additional Support

The characteristics of corrosion-fatigue in age-hardened Al alloys, e.g. brittle striations on cleavage-like facets, are described, with reference to two examples of component failure. Mechanisms of corrosion fatigue (and explanations for fracture-surface features) are then reviewed. New observations of corrosion-fatigue crack growth for 7050-T7451 alloy compact-tension specimens tested in aqueous environments using a constant (intermediate) ΔK value but different cycle frequencies are then described and discussed. These observations provide additional support for a hydrogen-embrittlement process involving adsorption-induced dislocation-emission from crack tips.