In order to obtain stable superhydrophobicity, suitable hydrophobic treatment agents should be selected according to different material properties. In this paper, cotton and poly(ethylene terephthalate) (PET) fabrics were respectively coated with dodecyl methacrylate (LMA) via argon combined capacitively coupled plasma (CCP), and the surface hydrophobicity and durability of the treated cotton and polyester fabrics are also discussed. An interesting phenomenon happened, whereby the LMA-coated cotton fabric (Cotton-g-LMA) had better water repelling and mechanical durability properties than LMA-coated PET fabric (PET-g-LMA), and LMA-coated hydroxyl-grafted PET fabrics (PET fabrics were successively coated with polyethylene glycol (PEG) and LMA, PET-g-PEG & LMA) had a similar performance to cotton fabrics. The water contact angles of Cotton-g-LMA, PET-g-LMA and PET-g-PEG & LMA were 156°, 153° and 155°, respectively, and after 45 washing cycles or 1000 rubbing cycles, the corresponding water contact angles decreased to 145°, 88°, 134° and 146°, 127° and 143°, respectively. Additionally, thermoplastic polyurethane (TPU) and polyamides-6 (PA6) fabrics all exhibited the same properties as the PET fabric. Therefore, the grafting of hydroxyl can improve the hydrophobic effect of LMA coating and the binding property between LMA and fabrics effectively, without changing the wearing comfort.
Electrospun nanocomposite fibers from lignin and iron oxide as supercapacitor material