An anodic behaviour study of an analogical sintered system of austenitic stainless steel in H2SO4 solution

Abstract Tests at 21 C (69 F) show hydrogen enters and penetrates thin Type 310 stainless steel in H2SO4 solution under applied cathodic currents, first condition for hydrogen entry contributing to hydrogen embrittlement and stress corrosion cracking. When metal surface is passive permeation rate depends on applied current density; when active, rate depends on surface corrosion currents and applied current.

Download Full-text

Some aspects of the defect structure in an austenitic stainless steel

Proceedings, annual meeting, Electron Microscopy Society of America ◽

10.1017/s0424820100108714 ◽

1978 ◽

Vol 36 (1) ◽

pp. 314-315

Author(s):

R. Gonzalez ◽

L. Bru

Keyword(s):

Stainless Steel ◽

Austenitic Stainless Steel ◽

Cellular Structures ◽

Total Strain Amplitude ◽

Total Deformation ◽

Density Of Dislocations ◽

Planar Arrays ◽

Stacking Fault Tetrahedra ◽

Distribution Of Dislocations ◽

Very High

The analysis of stacking fault tetrahedra (SFT) in fatigued metals (1,2) is somewhat complicated, due partly to their relatively low density, but principally to the presence of a very high density of dislocations which hides them. In order to overcome this second difficulty, we have used in this work an austenitic stainless steel that deforms in a planar mode and, as expected, examination of the substructure revealed planar arrays of dislocation dipoles rather than the cellular structures which appear both in single and polycrystals of cyclically deformed copper and silver. This more uniform distribution of dislocations allows a better identification of the SFT.The samples were fatigue deformed at the constant total strain amplitude Δε = 0.025 for 5 cycles at three temperatures: 85, 293 and 773 K. One of the samples was tensile strained with a total deformation of 3.5%.

Download Full-text

A TEM microscopical investigation of the magnetic domain structure of a metastable austenitic stainless steel

Proceedings, annual meeting, Electron Microscopy Society of America ◽

10.1017/s0424820100171213 ◽

1994 ◽

Vol 52 ◽

pp. 696-697

Author(s):

G. Fourlaris ◽

T. Gladman

Keyword(s):

Tensile Strength ◽

Stainless Steel ◽

Austenitic Stainless Steel ◽

Cold Rolling ◽

Solution Treatment ◽

Magnetic Domain ◽

High Strength ◽

Medium Carbon Steel ◽

Magnetic Characteristics ◽

Metastable Austenitic Stainless Steel

Stainless steels have widespread applications due to their good corrosion resistance, but for certain types of large naval constructions, other requirements are imposed such as high strength and toughness , and modified magnetic characteristics.The magnetic characteristics of a 302 type metastable austenitic stainless steel has been assessed after various cold rolling treatments designed to increase strength by strain inducement of martensite. A grade 817M40 low alloy medium carbon steel was used as a reference material.The metastable austenitic stainless steel after solution treatment possesses a fully austenitic microstructure. However its tensile strength , in the solution treated condition , is low.Cold rolling results in the strain induced transformation to α’- martensite in austenitic matrix and enhances the tensile strength. However , α’-martensite is ferromagnetic , and its introduction to an otherwise fully paramagnetic matrix alters the magnetic response of the material. An example of the mixed martensitic-retained austenitic microstructure obtained after the cold rolling experiment is provided in the SEM micrograph of Figure 1.

Download Full-text