Laser bed powder fusion (LPBF) is an additive manufacturing technology for the fabrication of semi-finished components directly from computer-aided design modelling, through melting and consolidation, layer upon layer, of a metallic powder, with a laser source. This manufacturing technique is particularly indicated for poor machinable alloys, such as Alloy 625. However, the unique microstructure generated could modify the resistance of the alloy to environment assisted cracking. The aim of this work was to analyze the stress corrosion cracking (SCC) and hydrogen embrittlement resistance behavior of Alloy 625 obtained by LPBF, both in as-built condition and after a standard heat treatment (grade 1). U-bend testing performed in boiling magnesium chloride at 155 and 170 °C confirmed the immunity of the alloy to SCC. However, slow strain rate tests in simulated ocean water on cathodically polarized specimens highlighted the possibility of the occurrence of hydrogen embrittlement in a specific range of strain rate and cathodic polarization. The very fine grain size and dislocation density of the thermally untreated specimens appeared to increase the hydrogen diffusion and embrittlement effect on pre-charged specimens that were deformed at the high strain rate. Conversely, heat treatment appeared to mitigate hydrogen embrittlement at high strain rates, however at the slow strain rate all the specimens showed a similar behavior.

Download Full-text

Effects of Cold Working and Heat Treatment on Caustic Stress Corrosion Cracking of Alloy 800M

Key Engineering Materials ◽

10.4028/www.scientific.net/kem.297-300.993 ◽

2005 ◽

Vol 297-300 ◽

pp. 993-998 ◽

Cited By ~ 1

Author(s):

Chun Bo Huang ◽

Guang Fu Li ◽

Zhan Peng Lu ◽

Jian Min Zeng ◽

Wu Yang

Keyword(s):

Heat Treatment ◽

Residual Stress ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Cold Working ◽

Corrosion Cracking ◽

Caustic Solution ◽

Surface Films ◽

Microstructure Examination ◽

Increasing Temperature

The effects of cold working and heat treatment on caustic stress corrosion cracking (SCC) of mill annealed (MA) alloy 800M in boiling solution of 50%NaOH+0.3%SiO2+0.3%Na2S2O3 were investigated by means of microstructure examination, tensile test, X-ray stress analysis, SCC testing of C-rings, Auger electron spectroscopy (AES), scanning electron microscopy (SEM) and metallography. The microstructure of alloy 800M under tested conditions was austenite. With a train of 25% by cold working, the grains of alloy 800M became longer, yield strength (YS) and ultimate tensile strength (UTS) increased, elongation (δ ) decreased, residual stress and the susceptibility to SCC increased. With increasing temperature of heat treatment of alloy 800M with cold working, the grains became bigger , residual stress, YS and UTS decreased and δ increased, the susceptibility to SCC of alloy 800M decreased. In boiling caustic solution, SCC cracks on the surfaces of C-ring specimens polarized potentiostatically at –20mV/SCE initiated from pitting and propagated along grain boundaries. AES analysis indicated that the surface films on MA alloy 800M were enriched in nickel and depleted in iron and chromium.