Multi-scale microstructure observation and three dimensional finite element thermal analysis of AlSi10Mg alloy fabricated by selective laser melting (SLM) process were demonstrated in order to understand the microstructure formation process during SLM fabrication. The unique hierarchically microstructures were observed: (1) the “fish scale” microstructure corresponding to a part of molten pool consists of columnar and equiaxed grains and (2) these grains contain a substructure of α-Al surrounded by Si particles. It is revealed that a supersaturated Si concentration due to the predicted rapid cooling rate on the order of 106 oC/s. In addition, the base temperature during the fabrication increases gradually with some peak temperature of each laser path as the laser scan has proceeded on a powder layer. Although the thermal changes cause no melting of the AlSi10Mg except directly fused region by selective laser so called molten pool, those are capable of causing precipitation and/or clustering.
Effects of Structural Parameters on the Poisson's Ratio and Compressive Modulus of 2D Pentamode Structures Fabricated by Selective Laser Melting