High-temperature stability and leaching kinetics of the hexavalent chromium compound, chrome-hauyne (Ca4Al6CrO16)

2021 ◽  
Author(s):  
Dongming Liu ◽  
Shengqiang Song ◽  
Andrie Garbers-Craig ◽  
Zhengliang Xue ◽  
Mithun Nath ◽  
...  
Keyword(s):  
High Temperature ◽  
Hexavalent Chromium ◽  
Temperature Stability ◽  
Leaching Kinetics ◽  
High Temperature Stability ◽  
Chromium Compound ◽  
Kinetics Of

UNS N06455

Alloy Digest ◽  
1989 ◽  
Vol 38 (1) ◽  
Keyword(s):  
Corrosion Resistance ◽  
High Temperature ◽  
Stress Corrosion Cracking ◽  
Temperature Stability ◽  
Heat Treating ◽  
High Ductility ◽  
High Temperature Stability ◽  
Nickel Chromium ◽  
Long Time ◽  
Resistance To Stress

Abstract UNS NO6455 is a nickel-chromium-molybdenum alloy with outstanding high-temperature stability as shown by high ductility and corrosion resistance even after long-time aging in the range 1200-1900 F. The alloy also has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900 F. This datasheet provides information on composition, physical properties, hardness, elasticity, and tensile properties. It also includes information on corrosion resistance as well as forming, heat treating, machining, and joining. Filing Code: Ni-367. Producer or source: Nickel and nickel alloy producers.

UNS R54620

Alloy Digest ◽  
1987 ◽  
Vol 36 (7) ◽  
Keyword(s):  
Titanium Alloy ◽  
High Temperature ◽  
Time Use ◽  
Temperature Stability ◽  
High Strength ◽  
Heat Treating ◽  
High Temperature Stability ◽  
Beta Titanium Alloy ◽  
Beta Titanium ◽  
Long Time

Abstract UNS No. R54620 is an alpha-beta titanium alloy. It has an excellent combination of tensile strength, creep strength, toughness and high-temperature stability that makes it suitable for service to 1050 F. It is recommended for use where high strength is required. It has outstanding advantages for long-time use at temperatures to 800 F. This datasheet provides information on composition, physical properties, elasticity, tensile properties, and bend strength as well as creep. It also includes information on high temperature performance and corrosion resistance as well as forming, heat treating, machining, joining, and surface treatment. Filing Code: Ti-86. Producer or source: Titanium alloy mills.

Study on leaching kinetics of hexavalent chromium from aged calcium-free chromium slag

2021 ◽  
pp. 1-13
Author(s):  
Quan Qi ◽  
Liang Li ◽  
Liangyu Wei ◽  
Baoming Hu ◽  
Zheng Liu ◽  
...  
Keyword(s):  
Hexavalent Chromium ◽  
Resource Utilization ◽  
Scientific Basis ◽  
Diffusion Reaction ◽  
Leaching Kinetics ◽  
Leaching Rate ◽  
Chromium Slag ◽  
Leaching Solution ◽  
Main Components ◽  
Kinetics Of

To provide a scientific basis for the resource utilization of chromium slag, this article studies the release law of hexavalent chromium in the aged calcium-free chromium slag. XRD (X-ray diffractometer) and MLA (Mineral Liberation Analyzer) were used to analyze the composition of the chromium slag; using sulfuric acid-nitric acid as the leaching solution, the release law of hexavalent chromium in chromium slag and the leaching kinetics were studied. The results show that main components of the chromium slag are magnesioferrite, chromite, hematite, hydrargillite, and spinel; chromium is mainly present in chromite and magnesioferrite; the leaching rate of hexavalent chromium increases with the increase of temperature or the decrease of pH. The analysis of leaching kinetics shows the leaching rate is controlled by the internal diffusion reaction, and the apparent activation energy is 11.93 kJ·mol–1. The chromium slag is aged in high temperature seasons, which is conducive to the precipitation of hexavalent chromium in the chromium slag, can increase the yield of chromate in the roasting kiln, and is conducive to resource utilization; chromium slag should be stored in order to prevent acid rain erosion which leads to environmental pollution risk (e.g. drinking water).

La2O3 Doped Y2O3 Stabilized ZrO2 TBC Prepared by EB-PVD

2006 ◽  
Vol 317-318 ◽  
pp. 501-504 ◽  
Author(s):  
Mineaki Matsumoto ◽  
Norio Yamaguchi ◽  
Hideaki Matsubara
Keyword(s):  
Thermal Conductivity ◽  
High Temperature ◽  
High Resistance ◽  
Thermal Transport ◽  
Temperature Stability ◽  
High Temperature Stability ◽  
Microstructural Observation ◽  
Low Thermal Conductivity ◽  
Ysz Coating

Effect of La2O3 addition on thermal conductivity and high temperature stability of YSZ coating produced by EB-PVD was investigated. La2O3 was selected as an additive because it had a significant effect on suppressing densification of YSZ. The developed coating showed extremely low thermal conductivity as well as high resistance to sintering. Microstructural observation revealed that the coating had fine feather-like subcolumns and nanopores, which contributed to limit thermal transport. These nanostructures were thought to be formed by suppressing densification during deposition.