scholarly journals Effect of heat treatment on the microstructure and mechanical properties of AZ80M magnesium alloy fabricated by wire arc additive manufacturing

2021 ◽  
Author(s):  
Yangyang Guo ◽  
Gaofeng Quan ◽  
Mert Celikin ◽  
Lingbao Ren ◽  
Yuhang Zhan ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Additive Manufacturing ◽  
Magnesium Alloy ◽  
Microstructure And Mechanical Properties ◽  
Wire Arc Additive Manufacturing

scholarly journals Characterisation of a High-Performance Al–Zn–Mg–Cu Alloy Designed for Wire Arc Additive Manufacturing

Materials ◽  
2020 ◽  
Vol 13 (7) ◽  
pp. 1610 ◽  
Author(s):  
Paulo J. Morais ◽  
Bianca Gomes ◽  
Pedro Santos ◽  
Manuel Gomes ◽  
Rudolf Gradinger ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Additive Manufacturing ◽  
High Performance ◽  
Mechanical Performance ◽  
Fluorescence Analysis ◽  
Cold Metal Transfer ◽  
Direction Parallel ◽  
X Ray ◽  
Wire Arc Additive Manufacturing

Ever-increasing demands of industrial manufacturing regarding mechanical properties require the development of novel alloys designed towards the respective manufacturing process. Here, we consider wire arc additive manufacturing. To this end, Al alloys with additions of Zn, Mg and Cu have been designed considering the requirements of good mechanical properties and limited hot cracking susceptibility. The samples were produced using the cold metal transfer pulse advanced (CMT-PADV) technique, known for its ability to produce lower porosity parts with smaller grain size. After material simulations to determine the optimal heat treatment, the samples were solution heat treated, quenched and aged to enhance their mechanical performance. Chemical analysis, mechanical properties and microstructure evolution were evaluated using optical light microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray fluorescence analysis and X-ray radiography, as well as tensile, fatigue and hardness tests. The objective of this research was to evaluate in detail the mechanical properties and microstructure of the newly designed high-performance Al–Zn-based alloy before and after ageing heat treatment. The only defects found in the parts built under optimised conditions were small dispersed porosities, without any visible cracks or lack of fusion. Furthermore, the mechanical properties are superior to those of commercial 7xxx alloys and remarkably independent of the testing direction (parallel or perpendicular to the deposit beads). The presented analyses are very promising regarding additive manufacturing of high-strength aluminium alloys.

Microstructure and Mechanical Properties of TiB2/ Al-Si Composites Fabricated by TIG Wire and Arc Additive Manufacturing

2019 ◽  
Vol 944 ◽  
pp. 64-72
Author(s):  
Qing Feng Yang ◽  
Cun Juan Xia ◽  
Ya Qi Deng
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Additive Manufacturing ◽  
Yield Strength ◽  
Filler Wire ◽  
T6 Heat Treatment ◽  
Microstructure And Mechanical Properties ◽  
Before And After

Bulky sample was made by using TIG wire and arc additive manufacturing (WAAM) technology, in which Ф1.6 mm filler wire of in-situ TiB2/Al-Si composites was selected as deposition metal, following by T6 heat treatment. The microstructure and mechanical properties of the bulky sample before and after heat treatment were analyzed. Experimental results showed that the texture of the original samples parallel to the weld direction and perpendicular to the weld direction was similar consisting of columnar dendrites and equiaxed crystals. After T6 heat treatment, the hardness of the sample was increased to 115.85 HV from 62.83 HV, the yield strength of the sample was 273.33 MPa, the average tensile strength was 347.33 MPa, and the average elongation after fracture was 7.96%. Although pore defects existed in the fracture, yet the fracture of the sample was ductile fracture.