Influence of Ti3SiC2 content on tribological properties of NiAl matrix self-lubricating composites

The YBa2Cu3Ox/Ag and Bi2Sr2CaCu2Ox/Ag self-lubricating composites were prepared using powder metallurgic method. The crystal structure and morphology of the as-synthesized samples were characterized by XRD and SEM. The YBa2Cu3Ox/Ag and Bi2Sr2CaCu2Ox/Ag self-lubricating composites were found to compose of superconductor phase and Ag phase. The tribological properties from ultra-low temperature to room temperature of the composites were studied by pin-on-disk friction test. It was found that the friction coefficients of pure YBa2Cu3Ox(YBCO) and Bi2Sr2CaCu2Ox(BSCCO) were both dropped abruptly when the temperature cooled below the superconducting transition temperature. At room temperature, the friction coefficient of pure YBa2Cu3Oxis 0.68~0.95, when mixing 15wt% Ag, the friction coefficient of the sample decreased to the lowest value 0.11. The friction coefficient of pure Bi2Sr2CaCu2Ox is 0.15~0.17, When Ag content reach 10wt%, the coefficient was lowest (average value is 0.13). The addition of appropriate amount of Ag obviously improve the tribological property of YBCO, while only slightly meliorate that of BSCO. On the other hand, the YBCO/Ag composites exhibit better tribological properties than BSCCO/Ag composites at higher load under the same experimental condition.

Download Full-text

Tribological and physical properties of PTFE-NBR self-lubricating composites under water lubrication

Industrial Lubrication and Tribology ◽

10.1108/ilt-05-2020-0187 ◽

2020 ◽

Vol ahead-of-print (ahead-of-print) ◽

Author(s):

Wei Feng ◽

Lei Yin ◽

Yanfeng Han ◽

Jiaxu Wang ◽

Ke Xiao ◽

...

Keyword(s):

Physical Properties ◽

Peer Review ◽

Tribological Properties ◽

Water Lubrication ◽

Butadiene Rubber ◽

Friction Test ◽

Bearing Material ◽

Content Type ◽

Lubricating Film ◽

Self Lubricating Composites

Purpose This paper aims to explore the possibility of converting the nitrile butadiene rubber (NBR) water-lubricated bearing material into a self-lubricating bearing material by the action of polytetrafluoroethylene (PTFE) particles and water lubrication. Design/methodology/approach A group of experimental studies was carried out on a ring-on-block friction test. The physical properties, tribological properties and interface structure of PTFE-NBR self-lubricating composites filled with different percentages of PTFE particles were investigated. Findings The experimental results indicated that the reduction in friction and wear is a result of the formation of the lubricating film on the surface of the composites. The lubricating film was formed of a large amount of PTFE particles continuously supplied under water lubrication conditions and the PTFE particles here can greatly enhance the load capacity and lubrication performance. Originality/value In this study, the tribological properties of PTFE particles added to the NBR water-lubricated bearing materials under water lubrication were investigated experimentally, and the research was carried out by a ring-on-block friction test. It is believed that this study can provide some guidance for the application of PTFE-NBR self-lubricating. Peer review The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-05-2020-0187/