By careful control of the electron beam it is possible to simultaneously induce and observe the phase transformation from monomer to polymer in certain solid-state polymcrizable diacetylenes. The continuous change in the crystal structure from DCHD diacetylene monomer (a=1.76 nm, b=1.36 nm, c=0.455 nm, γ=94 degrees, P2l/c) to polymer (a=1.74 nm, b=1.29 nm, c=0.49 nm, γ=108 degrees, P2l/c) occurs at a characteristic dose (10−4C/cm2) which is five orders of magnitude smaller than the critical end point dose (20 C/cm2). Previously we discussed the progress of this phase transition primarily as observed down the [001] zone (the chain axis direction). Here we report on the associated changes of the dark field (DF) images and selected area electron diffraction (SAED) patterns of the crystals as observed from the side (i.e., in the [hk0] zones).High resolution electron micrographs (HREM), DF images, and SAED patterns were obtained on a JEOL 4000 EX HREM operating at 400 kV.
Classification of Phase Transition in Perovskite-Type Dielectric Material According to Its Cubic Crystal Structure