Influence of coating thickness on rolling contact fatigue of alumina ceramics thermally sprayed on steel roller

2006 ◽  
Vol 39 (11) ◽  
pp. 1447-1453 ◽  
Author(s):  
Masahiro Fujii ◽  
Jiabin Ma ◽  
Akira Yoshida ◽  
Sadato Shigemura ◽  
Kazumi Tani
Keyword(s):  
Coating Thickness ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Alumina Ceramics ◽  
Steel Roller ◽  
Thermally Sprayed

Rolling contact fatigue of alumina ceramics sprayed on steel roller under pure rolling contact condition

2006 ◽  
Vol 39 (9) ◽  
pp. 856-862 ◽  
Author(s):  
Masahiro Fujii ◽  
Akira Yoshida ◽  
Jiabin Ma ◽  
Sadato Shigemura ◽  
Kazumi Tani
Keyword(s):  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Contact Condition ◽  
Rolling Contact ◽  
Alumina Ceramics ◽  
Steel Roller ◽  
Pure Rolling

scholarly journals Influence of Crowning on Rolling Contact Fatigue Strength and Failure Mode of Steel Roller

2007 ◽  
Vol 73 (728) ◽  
pp. 1222-1229 ◽  
Author(s):  
Masahiro FUJII ◽  
Seesregdorj BAYASGALAN ◽  
Akira YOSHIDA ◽  
Kenji HAMADA ◽  
Kiyoji MINEGISHI ◽  
...  
Keyword(s):  
Fatigue Strength ◽  
Failure Mode ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Steel Roller ◽  
Contact Fatigue Strength

Influence of TiN coating thickness on the rolling contact fatigue resistance of austempered ductile iron

Wear ◽  
2016 ◽  
Vol 350-351 ◽  
pp. 82-88 ◽  
Author(s):  
Diego Alejandro Colombo ◽  
María Dolores Echeverría ◽  
Ricardo Cesar Dommarco ◽  
Juan Miguel Massone
Keyword(s):  
Fatigue Resistance ◽  
Coating Thickness ◽  
Ductile Iron ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Austempered Ductile Iron ◽  
Tin Coating ◽  
Contact Fatigue Resistance

Rolling Contact Fatigue Life of Thermally Sprayed WC Cermet Coatings - A Review

2009 ◽  
Vol 2 (2) ◽  
pp. 115-129 ◽  
Author(s):  
Dewan Nuruzzaman ◽  
Akira Nakajima ◽  
Toshifumi Mawatari ◽  
Mohammad Chowdhury
Keyword(s):  
Fatigue Life ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Cermet Coatings ◽  
Contact Fatigue Life ◽  
Thermally Sprayed

Damage in Thermal-Sprayed WC-Co Coatings by Repeated Load

1997 ◽  
Author(s):  
T. Tajiri ◽  
N. Sakoda ◽  
S. Yamamoto ◽  
S. Watanabe
Keyword(s):  
Fatigue Test ◽  
Fatigue Cracks ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Medium Carbon Steel ◽  
Rolling Contact ◽  
Surface Damages ◽  
Load Tests ◽  
Repeated Load ◽  
Thermally Sprayed

Abstract Two types of WC-12wt%Co powders, each manufactured by a different process, were thermally sprayed on a medium carbon steel by HVOF, and repeated load tests (rolling contact fatigue test and high cycles fatigue test) were carried out. The surface damages for the two types of coatings were investigated. It has been clear that the coating damages depend on the types of powders. It has been found that in rolling contact fatigue, there are the coatings, in which damage is characterized by delamination, and by a mixture of delamination and cracks. And it has also been found that in high cycles fatigue, there are the coatings, in which damage is characterized by net-like fatigue cracks, and by linear fatigue cracks.

Rolling Contact Fatigue of Alumina Ceramics Sprayed Roller

2003 ◽  
Vol 2003.41 (0) ◽  
pp. 283-284
Author(s):  
Akira Yoshida ◽  
Masahiro Fujii ◽  
Kenji Yuki ◽  
Sadato Shigemura ◽  
Kazumi Tani
Keyword(s):  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Alumina Ceramics

Influence of Crowning on Rolling Contact Fatigue of Steel Roller : Contact Stress Analysis

2004 ◽  
Vol 2004.42 (0) ◽  
pp. 403-404
Author(s):  
Masahiro FUJII ◽  
Akira YOSHIDA ◽  
Takahito TABUCHI ◽  
Kiyoji MINEGISHI ◽  
Jun TAMENAGA
Keyword(s):  
Stress Analysis ◽  
Contact Stress ◽  
Rolling Contact Fatigue ◽  
Contact Fatigue ◽  
Rolling Contact ◽  
Steel Roller
Sign in / Sign up

Export Citation Format

Share Document