Abstract
17-4 PH stainless steel alloy has been widely used in the field of defense industry such as weapon equipment, aerospace, nuclear energy and so on because of its high strength, high toughness, high temperature resistance and corrosion resistance. In order to meet the flexible manufacturing requirements of multi-variety small batch complex structure products with lower cost and higher efficiency, Selective laser melted 17-4PH stainless steel alloy has become the focus of research in the field of rapid alloy manufacturing in recent years. This paper studied the density characteristics and the distribution characteristics of holes and spheroidization phenomena of 17-4 PH pre-alloyed powder subjected to multidimensional temperature conduction under selective laser melting, and the mechanism of defect generation under temperature conduction is proposed. Finally, the optimal selection of the combination of different process parameters waere carried out by orthogonal test, and it was found that the comprehensive mechanical behaviour of the 17-4 PH stainless steel alloy after formed exceeded the ASTM A564 standard (the yield strength is 1132 MPa, the tensile strength is 1323 MPa, the elongation is 16.6%).
A high-strength silicide phase in a stainless steel alloy designed for wear-resistant applications