Abstract
A 316L stainless steel material is widely used in the design of impact-resistant structures. Using selective laser melting (SLM) technology to form 316L stainless steel to study its mechanical behavior under dynamic loading is vital to improve the service performance of this product. This study investigates the dynamic compression mechanical properties and the constitutive models of 316L stainless steel specimens formed at different scanning speeds. The quasi-static and dynamic compression mechanical properties of SLM316L stainless steel specimens formed at four scanning speeds were tested using an electro-hydraulic servo experimental system and split Hopkinson pressure bar experimental apparatus. Microstructure observation was used to analyze the differences in the mechanical properties of specimens with different forming parameters. Finally, the modified Johnson-Cook (J-C) constitutive model was established and compared with the experimental data to illustrate the applicability of the modified model in describing the dynamic mechanical properties of SLM316l stainless steel. In dynamic compression mechanics experiments, the results show that SLM316L stainless steel specimens exhibit typical viscoplastic characteristics and significant strain rate strengthening effects. Furthermore, the scanning speed significantly affects the stacking characteristics of SLM-formed specimens, and the yield strength in axial compression decreases with the loss of stacking characteristics. Finally, the modified J-C model can accurately describe the mechanical properties of SLM316l stainless steel. This study can provide a theoretical model and methodological support for the design and development of SLM316l stainless steel.
Dynamic mechanical properties and comparison of two constitutive models for martensitic stainless steel 0Cr17Ni4Cu4Nb