Clinical Evaluation of Monolithic Zirconia Crowns: A Short-Term Pilot Report

Abstract Background The present study aimed to quantitate the wear of the highly transparent Yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) ceramic monolithic zirconia crown on the enamel in vivo and discuss the prone position of the wear and the underlying mechanism. Methods A total of 43 patients with 43 posterior teeth were selected for full zirconia crown restoration and examined immediately, at 6 months, and at 1 year after restoration. During the follow-up visit, the fine impression of the patients’ monolithic zirconia crowns, the antagonist teeth, the corresponding contralateral natural teeth, the super plaster cast, and epoxy resin model was ontained. The model of epoxy resin was observed under a stereo microscope, and the microstructure parts were observed under a scanning electron microscope. Results After 1 year, the mean depth and volume of wearing of the monolithic zirconia crown were the smallest (all P < 0.01), while those of the antagonist teeth were significantly larger than those of the natural teeth (P < 0.0001), and no significant difference was found among the natural teeth (P = 0.3473, P = 0.6996). The amount of wear after one year was remarkably higher than that at 6 months (P < 0.0001). The microscopic observation revealed the tendency of wearing of the monolithic zirconia crown on the antagonist teeth at the protruding early contact points. Electron micrographs of tooth scars showed that the wearing mechanism of the monolithic zirconia crown on natural teeth was mainly abrasive and fatigue wear. Conclusions Although the self-wearing is insignificant, the monolithic zirconia crown can cause wear of the antagonist teeth via occlusal or early contact significantly; the amount of wearing is higher than that of natural teeth and increases over time. The wearing mechanism is mainly abrasive and fatigue wear.

Download Full-text

Evaluation of marginal fit and microleakage of monolithic zirconia crowns cemented by bio-active and glass ionomer cements: In vitro study

Brazilian Dental Science ◽

10.14295/bds.2020.v23i1.1824 ◽

2020 ◽

Vol 23 (1) ◽

Author(s):

Radwa Hamdy Aboelenen ◽

Ashraf Mokhtar ◽

Hanaa Zaghloul

Keyword(s):

Glass Ionomer Cement ◽

Glass Ionomer ◽

Marginal Gap ◽

Marginal Fit ◽

Group I ◽

Significant Difference ◽

Zirconia Crowns ◽

Monolithic Zirconia ◽

Ionomer Cement ◽

Gap Values

Objective: To evaluate the marginal fit and microleakage of monolithic zirconia crowns cemented with bioactive cement (Ceramir) compared to that cemented with glass ionomer cement and to evaluate the effect of thermocycling on marginal fit. Materials and methods: Twenty sound human molar teeth were prepared to receive a monolithic zirconia crowns. Teeth were divided randomly into two equal groups according to the type of luting cement. Group I: glass ionomer cement and group II: Ceramir cement. After cementation, the vertical marginal gap was assessed by using stereomicroscope before and after thermocycling. Twenty equidistant measurement points were taken for each crown. Leakage assessment was carried out using Fuchsin dye penetration followed by digital photography under a stereomicroscope. Data were analyzed by Mann-Whitney U test to compare between the two luting cements. Wilcoxon signed-rank test was used to evaluate the effect of thermocycling on the marginal fit (P ≤ 0.05) Results: Whether before or after thermocycling, the results showed no significant difference between the marginal gap values of the two tested groups. For both groups, there was a significant increase in marginal gap values after thermocycling. Also, there was no significant difference between leakage scores of the two tested groups. Conclusions: Similarity in the physical properties and chemical composition of the two cements result in a non- significant effect on the vertical marginal fit and the extent of microleakage of translucent zirconia crowns. Thermocycling had a negative impact on the vertical marginal gap of the two tested luting agents.