Smooth surface of Bi-Sr-Ca-Cu-O thin films on the Y3Al5O12 (YAG) substrate

1994 ◽  
Vol 9 (5) ◽  
pp. 1104-1111 ◽  
Author(s):  
Nobuhiko Kubota ◽  
Yuh Shiohara ◽  
Shoji Tanaka
Keyword(s):  
Thin Films ◽  
Chemical Vapor Deposition ◽  
Single Crystal ◽  
Vapor Deposition ◽  
Smooth Surface ◽  
Chemical Vapor ◽  
Organic Chemical ◽  
Axis Orientation ◽  
Metal Organic ◽  
Organic Chemical Vapor Deposition

We prepared the superconducting Bi-Sr-Ca-Cu-O thin films on Y3Al5O12 (YAG) single crystal substrates by metal-organic chemical vapor deposition (MOCVD). This film of 50 nm thickness on a YAG substrate showed c-axis orientation clearly, and the zero-resistivity (Tc-zero) was achieved at 66 K. The film has the advantageous property of surface smoothness compared with the film fabricated on MgO and SrTiO3 single-crystal substrates. The surface property of the YAG substrate seems to influence the film quality.

Transparent conducting indium oxide thin films grown by low-temperature metal organic chemical vapor deposition

2007 ◽  
Vol 515 (5) ◽  
pp. 2921-2925 ◽  
Author(s):  
Chunyu Wang ◽  
Volker Cimalla ◽  
Genady Cherkashinin ◽  
Henry Romanus ◽  
Majdeddin Ali ◽  
...  
Keyword(s):  
Thin Films ◽  
Chemical Vapor Deposition ◽  
Low Temperature ◽  
Indium Oxide ◽  
Vapor Deposition ◽  
Chemical Vapor ◽  
Organic Chemical ◽  
Transparent Conducting ◽  
Metal Organic ◽  
Organic Chemical Vapor Deposition

Study on ZrO2:Er Thin Films Fabricated by Metal-Organic Chemical Vapor Deposition

2003 ◽  
Vol 42 (Part 1, No. 5A) ◽  
pp. 2839-2842 ◽  
Author(s):  
Jeong Hoon Park ◽  
Kug Sun Hong ◽  
Woon Jo Cho ◽  
Jang-Hoon Chung
Keyword(s):  
Thin Films ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Chemical Vapor ◽  
Organic Chemical ◽  
Metal Organic ◽  
Organic Chemical Vapor Deposition

Crack-free high quality 2 μm-thick Al0.5Ga0.5N grown on a Si substrate with a superlattice transition layer

CrystEngComm ◽  
2020 ◽  
Vol 22 (7) ◽  
pp. 1160-1165 ◽  
Author(s):  
Yingnan Huang ◽  
Jianxun Liu ◽  
Xiujian Sun ◽  
Xiaoning Zhan ◽  
Qian Sun ◽  
...  
Keyword(s):  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Transition Layer ◽  
Smooth Surface ◽  
Chemical Vapor ◽  
Organic Chemical ◽  
Si Substrate ◽  
High Quality ◽  
Metal Organic ◽  
Organic Chemical Vapor Deposition

We reported the successful growth of a crack-free high-quality 2 μm-thick Al0.5Ga0.5N film with a smooth surface grown on planar Si by metal–organic chemical vapor deposition.

Metal-organic chemical vapor deposition of ZrO2 films using Zr(thd)4 as precursors

1994 ◽  
Vol 9 (7) ◽  
pp. 1721-1727 ◽  
Author(s):  
Jie Si ◽  
Seshu B. Desu ◽  
Ching-Yi Tsai
Keyword(s):  
Thin Films ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Chemical Vapor ◽  
Film Deposition ◽  
Organic Chemical ◽  
Deposition Rates ◽  
Metal Organic ◽  
Organic Chemical Vapor Deposition ◽  
Deposited Films

Synthesis of zirconium tetramethylheptanedione [Zr(thd)4] was optimized. Purity of Zr(thd)4 was confirmed by melting point determination, carbon, and hydrogen elemental analysis and proton nuclear magnetic resonance spectrometer (NMR). By using Zr(thd)4, excellent quality ZrO2 thin films were successfully deposited on single-crystal silicon wafers by metal-organic chemical vapor deposition (MOCVD) at reduced pressures. For substrate temperatures below 530 °C, the film deposition rates were very small (⋚1 nm/min). The film deposition rates were significantly affected by (i) source temperature, (ii) substrate temperature, and (iii) total pressure. As-deposited films are carbon free. Furthermore, only the tetragonal ZrO2 phase was identified in as-deposited films. The tetragonal phase transformed progressively into the monoclinic phase as the films were subjected to a high-temperature post-deposition annealing. The optical properties of the ZrO2 thin films as a function of wavelength, in the range of 200 nm to 2000 nm, were also reported. In addition, a simplified theoretical model which considers only a surface reaction was used to analyze the deposition of ZrO2 films. The model predicated the deposition rates well for various conditions in the hot wall reactor.

Sign in / Sign up

Export Citation Format

Share Document