In this paper, carbon fiber reinforced resin matrix composites were produced by stacking eight pieces of carbon fiber woven plain fabric and subjected to accelerated ageing. Accelerated ageing was carried out in oven at 180°C for three different time intervals (60 hours, 120 hours and 180 hours). The influence of different ageing time intervals at 180°C on tensile properties of laminated composites was examined, compared with the composites without aging. The appearance and damage forms of these laminated composites were investigated. The results revealed that the tensile strength of the laminates declined significantly after long term accelerated aging at 180°C. The average tensile strengths of composite samples aged 60 hours, 120 hours, and 180 hours period of time at 180°C are 80.36%, 79.82%, 76.57% of average tensile strength of composite samples without aging, respectively. The high temperature accelerated aging makes the resin macromolecular structure in the composites changed, and then the adhesive force between fiber bundles and resin declines rapidly which result in the tensile strength of composites aged decrease. This research provides a useful reference for long term durability of laminated/epoxy resin composites.