Paper 7 The effect of fibre diameter on the strength and stiffness of glass fibre reinforced polymeric resins

The paper discusses the mechanical and physical behaviour of hybrid glass fibre reinforced plastic (GFRP). Hybrid GFRP was fabricated by three different types of glass fibre, namely, 3D, woven, and chopped, which were selected and combined with mixture of polyester resin and hardener. The hybrid GFRP was investigated by varying three parameters which were the composite volume fractions, hybrid GFRP arrangement, and single type fibre. The hybrid GFRP was fabricated by using open mould hand lay-up technique. Mechanical testing was conducted by tensile test for strength and stiffness whereas physical testing was performed using water absorption and hardness. These tests were carried out to determine the effect of mechanical and physical behaviour over the hybrid GFRP. The highest volume fraction of 0.5 gives the highest strength and stiffness of 73 MPa and 821 MPa, respectively. Varying hybrid fibre arrangement which is the arrangement of chopped-woven-3D-woven-chopped showed the best value in strength of 66.2 MPa. The stiffness is best at arrangement of woven-chopped-woven-chopped-woven at 690 MPa. This arrangement also showed the lowest water absorption of 4.5%. Comparing the single fibre type, woven had overtaken the others in terms of both mechanical and physical properties.

Download Full-text

A microstructural approach for modelling flexural properties of long glass fibre reinforced polyamide6.6

Journal of Composite Materials ◽

10.1177/0021998316637664 ◽

2016 ◽

Vol 51 (1) ◽

pp. 3-16 ◽

Cited By ~ 4

Author(s):

E Lafranche ◽

A Coulon ◽

P Krawczak ◽

JP Ciolczyk ◽

E Gamache

Keyword(s):

Flexural Strength ◽

Glass Fibre ◽

Flexural Modulus ◽

Processing Condition ◽

Fibre Diameter ◽

Fibre Length ◽

Fibre Content ◽

Distribution Model ◽

Second Phase ◽

Glass Fibre Reinforced

This paper focuses on the development and the validation of flexural modulus and flexural strength predictive models of long glass fibre reinforced polyamide 6.6 (PA66). Based on previous injection moulding optimization of 40 wt% long glass fibre PA66, a microstructure analysis was investigated on glass fibre reinforced PA66 by varying the parameters of the material (fibre length, fibre content, fibre diameter). In a first phase, analytical models established within the framework of the processing condition limits previously determined have been elaborated. These models lead to a good experimental/calculation correlation but remain limited to a mould and part design. In a second phase the flexural modulus and maximal flexural stress have been then estimated from structural models based on a five layer morphological description of the composites (local residual fibre length, local fibre content and fibre orientations). The long glass fibre PA66 composites were characterized in terms of fibre content distribution model and fibre orientation model through the part thickness. The experimental/model correlation was achieved whatever the process variability is (mould, material and processing conditions) both for the flexural modulus or flexural strength. The models have been then validated with an industrial part. Finally, a correlation between the two studied properties has been revealed depending on the nature of the composite matrix (PA66, PA6 or PP).