scholarly journals Effect of coagulation bath temperature during preparation of PES hollow fiber supported liquid membrane for acetic acid removal

2017 ◽  
Vol 19 ◽  
pp. 118 ◽  
Author(s):  
Sathiya Sanmugam ◽  
Norlisa Harruddin ◽  
Syed M Saufi
Keyword(s):  
Aqueous Solution ◽  
Acetic Acid ◽  
Hollow Fiber ◽  
Liquid Membrane ◽  
Hollow Fiber Membrane ◽  
Bath Temperature ◽  
Supported Liquid Membrane ◽  
Coagulation Bath ◽  
Fiber Membrane ◽  
Coagulation Bath Temperature

<p>Acetic acid is a byproduct of acid hydrolysis of biomass during sugar recovery step in biofuel production. Acetic acid can inhibit the enzyme used during fermentation of sugar to the ethanol. Hollow fiber supported liquid membrane (SLM) was used in this study to remove acetic acid from aqueous solution. Liquid membrane was formulated using trioctylamine and 2-ethyl hexanol as a carrier and solvent, respectively. The hollow fiber membrane support was prepared from 15 wt.% polyethersulfone, 42.5 wt.% polyethyleneglycol 200 and 42.5 wt.% dimethylacetamide. The effect of coagulation bath temperature (CBT) at 30<sup>º</sup>C, 40<sup>º</sup>C and 50<sup>º</sup>C during hollow fiber membrane spinning process was investigated. The porosity of the membrane increased as the CBT increased. The porosity of the membrane prepared using CBT of 30ºC, 40<sup>º</sup>C and 50<sup>º</sup>C were 35.7%, 46.7% and 61.6%, respectively. SLM process using hollow fiber membrane prepared at 50ºC of coagulation bath was able to remove 52% of acetic acid from the aqueous solution.</p><p>Chemical Engineering Research Bulletin 19(2017) 118-122</p>

scholarly journals Temperature Coagulant Tub Variation Effect on the Characteristic of Hollow Fiber Dialyser from Cellulose Acetate Composite D-Glucose Monohydrate

2017 ◽  
Vol 31 ◽  
pp. 53-60
Author(s):  
Rizki Firsta Wahyuliswari ◽  
Siswanto ◽  
Prihartini Widiyanti
Keyword(s):  
Tensile Strength ◽  
Creatinine Clearance ◽  
Cellulose Acetate ◽  
Hollow Fiber ◽  
Bath Temperature ◽  
Hollow Fibers ◽  
Coagulation Bath ◽  
Temperature Variations ◽  
Swelling Rate ◽  
Coagulation Bath Temperature

Polysulfone is synthetic polymer widely used as basic material for dialyzer membrane and hydrophobic so it tends to cause fouling. Cellulose acetate is non-synthetic, hydrophilic polymer which has low tendency of fouling and has good thermal stability and permeability so it is considered as alternative material for hollow fiber dialyzer. A proper hollow fiber can be achieved by setting a proper temperature of coagulation bath along the spinning process. This research aims to understand the effect of coagulation bath temperature variations on the physical characteristic such as pore size, tensile strength, swelling rate and creatinine clearance of cellulose acetate – D-glucose monohydrate hollow fibers. Hollow fibers were fabricated using spinneret at temperature variations 5°C, 10°C, 15°C dan 20°C. Physical characteristics were estimated by doing morphology test using SEM, tensile test, swelling test towards Simulated Body Fluid (SBF) and filtration test towards creatinine. Result revealed that the hollow fibers from 5°C coagulation bath temperature gives the best characteristic and performance with tensile strength 27,421 N mm-2, pore size 0,0295–0,0858 nm, swelling rate 4,18%, elongation rate 4,4 %, flux rate 1,6032–1,7956 mL cm-2 min-1 and creatinine clearance rate 40,14–48,30% so it is potential to be applied as dialyzer membrane.

scholarly journals Concentration of ethanol from its aqueous solution by pervaporation using porous polypropylene hollow-fiber membrane.

MEMBRANE ◽  
1986 ◽  
Vol 11 (4) ◽  
pp. 231-238 ◽  
Author(s):  
Haruhiko OHYA ◽  
Hiroaki MATSUMOTO ◽  
Yohichi NEGISHI ◽  
Kanji MATSUMOTO
Keyword(s):  
Aqueous Solution ◽  
Hollow Fiber ◽  
Hollow Fiber Membrane ◽  
Fiber Membrane
Sign in / Sign up

Export Citation Format

Share Document