Detailed Determination of Mechanical Fracture Parameters of Concrete after Fire Experiments

2018 ◽  
Vol 272 ◽  
pp. 220-225 ◽  
Author(s):  
Hana Šimonová ◽  
Tomáš Trčka ◽  
Michal Bejček ◽  
Iva Rozsypalová ◽  
Petr Daněk ◽  
...  
Keyword(s):  
Statistical Dependence ◽  
Crack Model ◽  
Mechanical Fracture ◽  
Three Point Bending ◽  
Fracture Parameters ◽  
Fracture Tests ◽  
Detailed Determination ◽  
Bending Fracture ◽  
Fire Experiments

The aim of this paper is to describe the procedure of determining the mechanical fracture parameters of selected concrete specimens taken from panels after the fire experiments. The records (in form load vs displacement diagrams) of three-point bending fracture tests of these specimens with initial stress concentrators was first advanced corrected and subsequently evaluated using the Effective Crack Model and the work-of-fracture method. The increasing temperatures during the fire experiments ranging between 550 to 1000 °C led to a decrease of modulus of elasticity and fracture toughness values and to the increase of fracture energy value. The 2D laser profile scanner was used to estimate the degree of complexity of fracture surfaces; its statistical dependence on the mechanical fracture parameters proved to be moderate – the absolute value of the correlation coefficient was about 0.5°[–].

Evaluation of Three-Point Bending Fracture Tests of Selected Concrete: Mechanical Fracture Parameters

2017 ◽  
Vol 259 ◽  
pp. 64-69
Author(s):  
Hana Šimonová ◽  
Petr Daněk ◽  
David Lehký ◽  
Zbyněk Keršner ◽  
Lubos Pazdera
Keyword(s):  
Fracture Energy ◽  
Modulus Of Elasticity ◽  
Crack Model ◽  
Mechanical Fracture ◽  
Three Point Bending ◽  
Fracture Parameters ◽  
Fracture Tests ◽  
Specific Fracture ◽  
Bending Fracture ◽  
Work Of Fracture

In this paper, authors focus attention on mechanical fracture parameters obtained from records of three-point bending fracture tests on concrete specimens with initial notch. Total eight sets of specimens were tested. Three specimens at the age of 28 days were tested in each set. Concrete was different in dosage of Portland cement CEM I 42.5 R and amount of used superplasticizer. The Effective Crack Model (ECM) was used to evaluate the load vs deflection diagrams to obtain modulus of elasticity and effective fracture toughness; specific fracture energy was determined using work-of-fracture method. Modulus of elasticity, tensile strength and fracture energy were also subject of identification via inverse analysis based on artificial neural network, which aim is to transfer the input data obtained from the fracture test to the desired material parameters.

Fracture Resistance of AAAS Composites with Ceramic Precursor

2021 ◽  
Vol 322 ◽  
pp. 54-59
Author(s):  
Iva Rozsypalová ◽  
Petr Daněk ◽  
Pavla Rovnaníková ◽  
Zbyněk Keršner
Keyword(s):  
Mouth Opening ◽  
Crack Model ◽  
Arithmetic Means ◽  
Mechanical Fracture ◽  
Three Point Bending ◽  
Static Modulus ◽  
Fracture Parameters ◽  
Ceramic Precursors ◽  
Static Modulus Of Elasticity

The paper deals with selected alkali-activated aluminosilicate (AAAS) composites based on ceramic precursors in terms of their characterization by mechanical fracture parameters. Composites made of brick dust as a precursor and an alkaline activator with a silicate modulus of Ms = 0.8, 1.0, 1.2, 1.4 and 1.6 were investigated. The filler employed with one set of composites was quartz sand, while for the other set it was crushed brick. The test specimens had nominal dimensions of 40 × 40 × 160 mm and were provided with notches at midspan of up to 1/3 of the height of the specimens after 28 days. 6 samples from each composite were tested. The specimens were subjected to three-point bending tests in which force vs. displacement (deflection at midspan) diagrams (F–d diagrams) and force vs. crack mouth opening (F–CMOD) diagrams were recorded. After the correction of these diagrams, static modulus of elasticity, effective fracture toughness, effective toughness and specific fracture energy values were determined using the Effective Crack Model and the Work-of-Fracture method. After the fracture experiments, informative compressive strength values were determined from one of the parts. All of the evaluations included the determination of arithmetic means and standard deviations. The silicate modulus values and type of filler of the AAAS composites significantly influenced their mechanical fracture parameters.

Fracture Response of Fine-Grained Cement-Based Composite Specimens with Special Inclusions

2019 ◽  
Vol 292 ◽  
pp. 63-68 ◽  
Author(s):  
Michal Vyhlídal ◽  
Iva Rozsypalová ◽  
Tomáš Majda ◽  
Petr Daněk ◽  
Hana Šimonová ◽  
...  
Keyword(s):  
Transition Zone ◽  
Interfacial Transition Zone ◽  
Mechanical Fracture ◽  
Three Point Bending ◽  
Fine Grained ◽  
Fracture Parameters ◽  
Edge Notch ◽  
Fracture Tests ◽  
Materials Used ◽  
Bending Fracture

This paper concerns research into the importance of the interfacial transition zone around inclusions of selected materials in fine-grained cement-based composite. Tests were performed on eight sets of prismatic test specimens. The sets differed in the inclusion materials used, which were placed at midspan above the initial central edge notch. The first was a reference set without any inclusion, the second contained a steel inclusion, four more contained different types of rock inclusion, the seventh contained an inclusion of extruded polystyrene, and the last contained a space of the same dimensions as that occupied by the inclusions in sets 2 to 7. The test specimens were subjected to three-point bending fracture tests at the age of (usually) 28 days. The fracture response was analysed by means of fracture mechanics theory, and apparent mechanical fracture parameters (modulus of elasticity, fracture toughness and fracture energy) were evaluated. The conclusion shows that a possible relationship exists between the differences in the mechanical fracture parameters of specimens with/without an inclusion and the existence of the interfacial transition zone.

Mechanical Fracture Parameters of Mortars Modified by Burnt Clays

2014 ◽  
Vol 969 ◽  
pp. 241-244
Author(s):  
Eva Navrátilová ◽  
Hana Šimonová ◽  
Barbara Kucharczyková ◽  
Ivana Havlíková ◽  
Jan Bedáň ◽  
...  
Keyword(s):  
Hydrated Lime ◽  
The Other ◽  
Mechanical Fracture ◽  
Lime Mortar ◽  
Three Point Bending ◽  
Fracture Parameters ◽  
Brick Powder ◽  
Fracture Tests ◽  
Bending Fracture ◽  
Reference Mixture

This paper presents the results of three-point bending fracture tests. Specimens were made from lime mortar modified by brick powder or metakaolin. The first, reference mixture only used hydrated lime, while the other mixtures were enhanced by brick powder or metakaolin in amounts of 25, 50 and 100 % of the weight of hydrated lime.

scholarly journals Complex multilevel fracture tests of concrete: basic mechanical fracture parameters of standard size specimens

2020 ◽  
Vol 323 ◽  
pp. 01001 ◽  
Author(s):  
David Lehký ◽  
Hana Šimonová ◽  
Barbara Kucharczyková ◽  
Petr Daněk
Keyword(s):  
Standard Test ◽  
Experimental Program ◽  
Standard Size ◽  
Mechanical Fracture ◽  
Three Point Bending ◽  
Multiple Test ◽  
Fracture Parameters ◽  
Different Depths ◽  
Fracture Tests

The aim of the current research is to develop a complex multilevel approach for the experimental–computational determination of mechanical fracture parameters of concrete as a typical quasi-brittle material. This includes testing, advanced evaluation and soft computing-based identification of specimens of multiple sizes in multiple test configurations and analyses of fracture processes using multiscale modelling approaches. The evaluation of a part of an extensive experimental program is presented in this paper. The basic mechanical fracture parameters of the investigated concrete determined on standard test specimens with nominal dimensions of 100 × 100 × 400 mm subjected to the standard three-point bending fracture test are introduced. The results of three different sets of specimens provided with different depths of the initial notch are compared in terms of absolute values of the selected mechanical fracture parameters. The results indicate different sensitivity of particular mechanical fracture parameters in relation to the depth of the initial notch.

Pilot Fracture Tests of Special Fine-Grained Composites

2021 ◽  
Vol 322 ◽  
pp. 3-8
Author(s):  
Iva Rozsypalová ◽  
Emília Bystrianska ◽  
Ondřej Koutný ◽  
Petr Daněk ◽  
Petr Frantík ◽  
...  
Keyword(s):  
Tensile Strength ◽  
Crack Model ◽  
Mechanical Fracture ◽  
Bending Tests ◽  
Test Configuration ◽  
Three Point Bending ◽  
Fine Grained ◽  
Fracture Parameters ◽  
Nominal Size ◽  
Fracture Tests

Mechanical fracture parameters were obtained for special fine-grained cement-based composites from three-point bending tests. A total of four sets of composite specimens were tested. All of the sets of composites were based on a general recipe and differ in the amount of high-strength aggregate and/or dispersed steel fibres present. Standardized prism specimens with a nominal size of 40 × 40 × 160 mm were used for the fracture tests after 131 days of curing. An initial notch was cut in the centre of the prisms with a depth approximately equal to one third of the specimen’s height. Three specimens from each set of composites were tested in the three-point bending fracture test configuration. Load versus midspan deflection diagrams were recorded. Experimentally obtained load vs displacement diagrams were corrected and analysed using the Effective Crack Model, the Work-of-Fracture method and an independent identification technique using numerical modelling. The most important mechanical fracture parameters, such as static modulus of elasticity, effective fracture toughness, specific fracture energy and effective tensile strength, were determined. Compressive and splitting tensile strength values were obtained from the halves of the specimens left over after the bending tests.

Effect of Concrete Mixture Composition on Acoustic Emission and Fracture Parameters Obtained from Three-Point Bending Test

2015 ◽  
Vol 1100 ◽  
pp. 152-155
Author(s):  
Libor Topolář ◽  
Hana Šimonová ◽  
Petr Misák
Keyword(s):  
Acoustic Emission ◽  
Bending Test ◽  
Mixture Composition ◽  
Three Point Bending ◽  
Concrete Mixtures ◽  
Fracture Parameters ◽  
Fracture Tests ◽  
Stress Behaviour ◽  
Bending Fracture ◽  
Fracture Processes

This paper reports the analysis of acoustic emission signals captured during three-point bending fracture tests of concrete specimens with different mixture composition. Acoustic emission is an experimental tool well suited for monitoring fracture processes in material. The typical acoustic emission patterns were identified in the acoustic emission records for three different concrete mixtures to further describe the under-the-stress behaviour and failure development. An understanding of microstructure–performance relationships is the key to true understanding of material behaviour. The acoustic emission results are accompanied by fracture parameters determined via evaluation of load versus deflection diagrams recorded during three-point bending fracture tests.

Mechanical Fracture Properties of Cement Mortars with Diatomite in Relation to their Microstructure

2015 ◽  
Vol 1124 ◽  
pp. 57-62
Author(s):  
Pavla Rovnaníková ◽  
Hana Šimonová ◽  
Pavel Schmid ◽  
Jana Zahálková ◽  
Patrik Bayer ◽  
...  
Keyword(s):  
Elasticity Modulus ◽  
Hardened Cement ◽  
Mechanical Fracture ◽  
Fracture Properties ◽  
Three Point Bending ◽  
Cement Mortars ◽  
Edge Notch ◽  
Fracture Tests ◽  
Specific Fracture ◽  
Bending Fracture

The paper is focused on the mechanical fracture properties of hardened cement mortars in which Portland cement is partially replaced by reactive admixtures. These properties are evaluated in relation to the mortars’ microstructure through the size and content of pores. The cement in the mortars was partially replaced by a diatomite that contains amorphous SiO2. The three-point bending fracture tests were performed on beams with a central edge notch. The investigated mechanical fracture properties of the aforementioned cement-based composites included flexural strength, compressive strength, elasticity modulus, effective fracture toughness and specific fracture energy.

scholarly journals Components of the Fracture Response of Alkali-Activated Slag Composites with Steel Microfibers

2019 ◽  
Vol 9 (9) ◽  
pp. 1754 ◽  
Author(s):  
Hana Šimonová ◽  
Petr Frantík ◽  
Zbyněk Keršner ◽  
Pavel Schmid ◽  
Pavel Rovnaník
Keyword(s):  
Mouth Opening ◽  
Crack Mouth Opening Displacement ◽  
Model Parameters ◽  
Crack Model ◽  
Mechanical Fracture ◽  
Alkali Activated Slag ◽  
Fracture Parameters ◽  
Fracture Tests ◽  
Activated Slag ◽  
Alkali Activated

Knowledge of the mechanical and primarily fracture parameters of composites with a brittle matrix is essential for the quantification of their resistance to crack initiation and growth, and also for the specification of material model parameters employed for the simulation of the quasi-brittle behavior of structures made from this type of composite. Therefore, the main target of this paper is to quantify the mechanical fracture parameters of alkali-activated slag composites with steel microfibers and the contribution of the matrix to their fracture response. The first alkali-activated slag composite was a reference version without fibers; the others incorporated steel microfibers amounting to 5, 10, 15 and 20% by weight of the slag. Prism specimens with an initial central edge notch were used to perform the three-point bending fracture tests. Load vs. displacement (deflection at midspan) and load vs. crack mouth opening displacement diagrams were recorded during the fracture tests. The obtained diagrams were employed as inputs for parameter identification, the aim of which was to transfer the fracture test response data to the desired material parameters. Values were also determined for fracture parameters using the effective crack model, work-of-fracture method and double-K fracture model. All investigated mechanical fracture parameters were improved by the addition of steel microfibers to the alkali-activated matrix. Based on the obtained results, the addition of 10 to 15% of microfibers by weight is optimal from the point of view of the enhancement of the fracture parameters of alkali-activated slag composite.

Alkali Activated Binders Based Concrete Specimens: Length Change and Fracture Tests

2016 ◽  
Vol 258 ◽  
pp. 623-626 ◽  
Author(s):  
Vlastimil Bílek Jr. ◽  
Hana Šimonová ◽  
Ivana Havlíková ◽  
Libor Topolář ◽  
Barbara Kucharczyková ◽  
...  
Keyword(s):  
Stress Concentrator ◽  
Length Change ◽  
Bending Test ◽  
Crack Model ◽  
Mechanical Fracture ◽  
Three Point Bending ◽  
Fracture Tests ◽  
Alkali Activated Binders ◽  
Work Of Fracture ◽  
Alkali Activated

The aim of this paper is to quantify mechanical fracture and length change parameters of the two types of concrete with alkali activated binder. The six beam specimens (75 × 75 × 295 mm) were made from each mixture. After demolding specimens were placed in air storage for 28 days. During this period length change (shrinkage) were recorded in accordance with ASTM C490 (2011). After that the three-point bending test was performed on these specimens with initial stress concentrator at the age of 28 days to obtain the mechanical fracture parameters. Records of fracture tests in form load versus deflection (F–d) diagrams were evaluated using effective crack model and work of fracture method.

Sign in / Sign up

Export Citation Format

Share Document