This paper analyzes the indentation hardness and the indentation elastic modulus variation depending on the variation of the grind percentage of polymer, when the other factors that can influence the injection molding remain unchanged. The analyzed polymers were: acrylonitrile butadiene styrene ABS MAGNUM 3453, polyamide PA 6.6 TECHNYL AR218V30 Blak and polyoxymethylene POM EUROTAL C9 NAT. The samples that were studied had different compositions in new and grinding material. The G-Series Basic Hardness Modulus at a Depth method was used. The increase of the grind percentage of ABS (from 0 to 100 %) leads to insignificant changes in the indentation hardness, indentation modulus, and maximum force applied to samples of tested material. The maximum hardness (0.137 GPa) of PA 6.6 is recorded in the case of the sample with 80% grind content, and the maximum hardness of POM is recorded as well in the case of the sample with 80% grind content, as being 0.215 GPa. The variation of the grind content in the analyzed samples determines changes in the evaluated parameters, depending on the type of polymer. Combining the new material with grind in proportions experimentally established for each techno polymer leads to changes in their mechanical properties.
Morphology and strength of acrylonitrile butadiene styrene welds performed by robotic friction stir welding