Mechanically Tunable Spongy Graphene/Cellulose Nanocrystals Hybrid Aerogel by Atmospheric Drying and Its Adsorption Applications

For expanding applications of spongy graphene aerogels (GAs) cost-effectively, we report a marriage of the two-step hydrothermal reduction and atmospheric drying method to fabricate a spongy CNC-graphene aerogel (CNG) with oil/water selectivity and tunable mechanical strength by a low-cost and straightforward approach. The reduced graphene oxide (rGO) with CNC by the ice-templated method can give rise to forming the hierarchical structure of hybrid GAs within the PUS network. Meanwhile, the fractured structure of PUS with a pre-compressive step arouses more versatility and durability, involving its selective and high-volume absorbability (up to 143%). The enhanced elastic modulus and more significant swelling effect than pure sponge materials give it a high potential for durable wastewater treatment.

Highly Crystalline Ordered Cu-dopedTiO2Nanostructure by Paper Templated Method: Hydrogen Production and Dye Degradation under Natural Sunlight

A highly crystalline ordered Cu-TiO2 nanostructure was synthesized using a simple paper template method using cupric nitrate and titanium isopropoxide as precursors. The structural study by XRD confirmed the formation of highly crystalline anatase phase of Cu-TiO2. The broad diffraction peaks of Cu-TiO2 exhibit the nanocrystalline nature of the product. The optical study by UV-DRS indicated the red shift in absorption wavelength with an increase in Cu doping, i.e., towards the visible region. The FE-SEM and FE-TEM study validated the formation of spherical shaped nanoparticles of Cu-TiO2 having sizes in the range of 20–30 nm. Considering the absorption in the visible region, the photocatalytic study was performed for water splitting and rhodamine-B (RhB) dye degradation under natural sunlight. The 2% Cu-doped TiO2 showed the highest photocatalytic hydrogen evolution, i.e., 1400 µmol·g−1·h−1 from water, among the prepared compositions. The photocatalytic performance of Cu-TiO2 conferred complete degradation of RhB dye within 40 min. The higher activity in both cases was attributed to the formation of highly crystalline ordered nanostructure of Cu-doped TiO2. This synthesis approach has potential to prepare other highly crystalline ordered nanostructured semiconductors for different applications.

Salt-templated synthesis of 3D porous foam-like C3N4 towards high-performance photodegradation of tetracyclines

3D porous foam-like C3N4 is prepared by a salt-templated method, and it shows 64 times higher efficiency than bulk C3N4 in degrading tetracyclines.