Aging Behavior of Intercritically Quenched Ductile Iron

Although extensive aging and strain aging (bake hardening, BH) studies have been carried out on dual-phase steels, the aging behavior of the dual matrix structure (DMS) ductile iron (DI), as a potential way to improve its mechanical properties, has not been addressed until now. This research was designed to study the aging behavior of DI with a ferrite-martensite matrix structure. DMS-DI with a martensite volume fraction of 30% was produced by intercritical austenitizing at 785 °C followed by quenching in water to room temperature. Aging treatments were carried out without pre-straining at aging temperatures of 140, 170, and 220 °C for 2–10,000 min. DMS-DI was investigated by light optical microscopy (LOM) for unaged samples and scanning electron microscopy (SEM) for selected samples after aging treatments. The effect of aging conditions on the mechanical properties were investigated. Microhardness measurements for ferrite and martensite were also examined as a function of aging conditions. The increase in yield strength due to aging was determined. The results indicate that the aging conditions have a small effect on the ultimate tensile strength UTS. It is shown that the yield strength increased to a maximum value of 45 MPa (~11% increase) after aging for particular time, which is found to be dependent on the aging temperature. The peak aging response is followed by a decrease in yield strength, which is observed to be attributed to martensite tempering as confirmed by microhardness measurements.

Optimization of the Continuous Galvanizing Heat Treatment Process in Ultra-High Strength Dual Phase Steels Using a Multivariate Model

The main process variables to produce galvanized dual phase (DP) steel sheets in continuous galvanizing lines are time and temperature of intercritical austenitizing (tIA and TIA), cooling rate (CR1) after intercritical austenitizing, holding time at the galvanizing temperature (tG) and finally the cooling rate (CR2) to room temperature. In this research work, the effects of CR1, tG and CR2 on the ultimate tensile strength (UTS), yield strength (YS), and elongation (EL) of cold rolled low carbon steel were investigated by applying an experimental central composite design and a multivariate regression model. A multi-objective optimization and the Pareto Front were used for the optimization of the continuous galvanizing heat treatments. Typical thermal cycles applied for the production of continuous galvanized AHSS-DP strips were simulated in a quenching dilatometer using miniature tensile specimens. The experimental results of UTS, YS and EL were used to fit the multivariate regression model for the prediction of these mechanical properties from the processing parameters (CR1, tG and CR2). In general, the results show that the proposed multivariate model correctly predicts the mechanical properties of UTS, YS and %EL for DP steels processed under continuous galvanizing conditions. Furthermore, it is demonstrated that the phase transformations that take place during the optimized tG (galvanizing time) play a dominant role in determining the values of the mechanical properties of the DP steel. The production of hot-dip galvanized DP steels with a minimum tensile strength of 1100 MPa is possible by applying the proposed methodology. The results provide important scientific and technological knowledge about the annealing/galvanizing thermal cycle effects on the microstructure and mechanical properties of DP steels.