Термоэлектрические и мемристивные особенности структур Sb-=SUB=-2-=/SUB=-Te-=SUB=-3-=/SUB=-/Sb-=SUB=-2-=/SUB=-S-=SUB=-3-=/SUB=-/Sb-=SUB=-2-=/SUB=-Te-=SUB=-3-=/SUB=- и Ag/Sb-=SUB=-2-=/SUB=-Te-=SUB=-3-=/SUB=-/Ag

Single-layer Sb2Te3 films and three-layer Sb2Te3/Sb2S3/Sb2Te3 structures are obtained by thermal vacuum deposition. Their thermoelectric characteristics have been investigated in a wide temperature range (5350 K). It is shown that the conductivity of Sb2Te3/Sb2S3/Sb2Te3 has a semiconductor behavior, the resistivity is an order of magnitude higher than the resistivity of the Sb2Te3 film; the Seebeck coefficient of Sb2Te3/Sb2S3/Sb2Te3 is 1.5 and 3 times higher than the Seebeck coefficient of the film and single-crystal Sb2Te3, respectively. The currentvoltage characteristics of the Sb2Te3 film exhibit memristive properties with unipolar resistive switching, whereas Sb2Te3/Sb2S3/Sb2Te3 can be considered as a memristor with a parallel connected capacitance.

Влияние водорода на оптическую прозрачность слоев палладия

The optical transparency of palladium layers within the wavelength region from 0.5 to 1.1 μm in air and in gaseous mixtures containing hydrogen in the range of 0.1 to 100 vol.% has been studied. The thermal-vacuum deposition method was used to prepare palladium layers on glass substrate. Buger’s law is implemented for layers thickness of order 450 Å. Pd layers of more than 1200 Å are damaged in 100% hydrogen medium. At some hydrogen concentration between 1-10 vol.% a sharp increase in Pd layer transparency is observed that is intrinsic for the first-order phase transition. The layer transparency change speed increases linearly with increasing the hydrogen concentration in gas medium.

Fabrication of Electroosmotic Flow Pump on Polymethylemethacrylate Substrate Using Hot Embossing

Improved fabrication processes of a micro electroosmotic flow pump using hot embossing are described. The microchannels in the micropump were fabricated by hot embossing on a polymethylmethacrylate (PMMA) substrate. A silicon micromachined mold was pressed into the PMMA substrate at a temperature of 145 °C to form microchannel patterns on the substrate. The depth and width of the microchannels were 50 μm and 100 μm, respectively. Aluminum electrodes were deposited using thermal vacuum deposition. A UV ozone treatment was performed to improve adhesion between the PMMA substrate and a PMMA capping layer. This UV ozone treatment enhanced adhesion and resulted in the reduction of the adhesion temperature as low as 70 °C, and nearly no deformation of the microchannels was observed. As a result, the electroosmotic flow pump exhibited the flow rate of 0.5 μl/min when a voltage of 50 V was given between the electrodes separated 8 mm each other.