The development of technology for production of zeolites from fly-ash from Troitskaya power plant

The study examines the technology of processing fly ash from Troitskaya power plant for the production of zeolite. The paper presents the results of laboratory studies evaluating the suitability of fly ash from Troitskaya power plant for the production of zeolites and the development of the zeolite production process. Fly ash contains a small amount of heavy metals that can complicate processing, but contains a large amount of silicon oxide. The technology consists of high-temperature alkaline activation of fly ash and hydrochemical synthesis. The resulting powder has a specific surface area of 89.7 m2/g, determined by the BET method, and an average pore diameter of 0.345 μm. The static exchange capacity was 220 mg/g.

Ultrafast Hydro-Micromechanical Synthesis of Calcium Zincate: Structural and Morphological Characterizations

Calcium zincate is a compound with a large panel of application: mainly known as an advantageous replacement of zinc oxide in negative electrodes for air-zinc or nickel-zinc batteries, it is also used as precursor catalyst in biodiesel synthesis and as antifungal compound for the protection of limestone monuments. However, its synthesis is not optimized yet. In this study, it was elaborated using an ultrafast synthesis protocol: Hydro-Micromechanical Synthesis. Two other synthesis methods, Hydrochemical Synthesis and Hydrothermal Synthesis, were used for comparison. In all cases, the as-synthesized samples were analyzed by X-ray diffraction, scanning electron microscopy, and LASER diffraction particle size analysis. Rietveld method was used to refine various structural parameters and obtain an average crystallite size, on a Hydro-Micromechanical submicronic sample. X-ray single crystal structure determination was performed on a crystal obtained by Hydrochemical Synthesis. It has been shown that regardless of the synthesis protocol, the prepared samples always crystallize in the same crystal lattice, withP21/cspace group and only differ from their macroscopic textural parameters. Nevertheless, only the Hydro-Micromechanical method is industrially scalable and enables a precise control of the textural parameters of the obtained calcium zincate.