Preparation and antibacterial properties of an AgBr@SiO2/GelMA composite hydrogel

Pure gelatin hydrogels lack antibacterial function and have poor mechanical properties, which restrict their application in wound dressings. In this study, nanosized silver bromide-doped mesoporous silica (AgBr@SiO2) microspheres with hollow structures were prepared by a modified Stober method. The novel microspheres can not only release silver ions to treat bacteria but also release drugs to treat skin wound. Furthermore, AgBr@SiO2 microspheres were modified with propyl methacrylate, incorporated into methacrylated gelatin (GelMA), and crosslinked by UV light to prepare AgBr@SiO2/GelMA dressings consisting of composite hydrogels. The results showed that the AgBr@SiO2 microspheres could enhance the mechanical properties of the hydrogels. With the increase in the AgBr@SiO2 concentration from 0.5 to 1 mg/mL, the dressings demonstrated effective antimicrobial activity against both Staphylococcus aureus and Escherichia coli. Furthermore, full-thickness skin wounds in vivo wound healing studies with Sprague–Dawley rats were evaluated. When treated with AgBr@SiO2/GelMA containing 1 mg/mL AgBr@SiO2, only 15% of the wound area left on day 10. Histology results also showed the epidermal and dermal layers were better organized. These results suggest that AgBr@SiO2/GelMA-based dressing materials could be promising candidates for wound dressings.

Biomimetic Growth of Hydroxyapatite on SiO2 Microspheres to Improve Its Biocompatibility and Gentamicin Loading Capacity

The interest in multifunctional biomaterials to be implanted are also able to release drugs that reduce pain and inflammation or prevent a possible infection has increased. Bioactive materials such as silica (SiO2) containing surface silanol groups contribute to the nucleation and growth of hydroxyapatite (HAp) in a physiological environment. Regarding biocompatibility, the spherical shape of particles is the desirable one, since it does not cause mechanical damage to the cell membrane. In this work, the synthesis of SiO2 microspheres was performed by the modified Stöber method and they were used for the biomimetic growth of HAp on their surface. The effect of the type of surfactant (sodium dodecyl sulphate (SDS), cetyltrimethylammonium bromide (CTAB), and polyethylene glycol (PEG)), and heat treatment on the morphology and size of SiO2 particles was investigated. Monodisperse, spherical-shaped SiO2 microparticles with an average particle size of 179 nm, were obtained when using PEG (SiO2-PEG). The biomimetic growth of HAp was performed on this sample to improve its biocompatibility and drug-loading capacity using gentamicin as a model drug. Biomimetic growth of HAp was confirmed by FTIR-ATR, SEM-EDX and TEM techniques. SiO2-PEG/HAp sample had a better biocompatibility in vitro and gentamicin loading capacity than SiO2-PEG sample.

Hydrolytic Modification of SiO2 Microspheres with Na2SiO3 and the Performance of Supported Nano-TiO2 Composite Photocatalyst

Modified microspheres (SiO2-M) were obtained by the hydrolytic modification of silicon dioxide (SiO2) microspheres with Na2SiO3, and then, SiO2-M was used as a carrier to prepare a composite photocatalyst (SiO2-M/TiO2) using the sol-gel method; i.e., nano-TiO2 was loaded on the surface of SiO2-M. The structure, morphology, and photocatalytic properties of SiO2-M/TiO2 were investigated. Besides, the mechanism of the effect of SiO2-M was also explored. The results show that the hydrolytic modification of Na2SiO3 coated the surface of SiO2 microspheres with an amorphous SiO2 shell layer and increased the quantity of hydroxyl groups. The photocatalytic performance of the composite photocatalyst was slightly better than that of pure nano-TiO2 and significantly better than that of the composite photocatalyst supported by unmodified SiO2. Thus, increasing the loading capacity of nano-TiO2, improving the dispersion of TiO2, and increasing the active surface sites are essential factors for improving the functional efficiency of nano-TiO2. This work provides a new concept for the design of composite photocatalysts by optimizing the performance of the carrier.