Development and Characterization of Active Native and Cross-Linked Pearl Millet Starch-Based Film Loaded with Fenugreek Oil

In this study, cross-linked pearl millet starch and fenugreek oil was used to develop active starch edible films to overcome the limitations of native starch and to substitute artificial preservatives with natural one. The starch was cross-linked at three levels (1%, 3% and 5%) using sodium trimetaphosphate (STMP), and physicochemical properties were studied. Moreover, a comparative study was conducted among four samples of films prepared using native starch, cross-linked starch, and native and cross-linked starch loaded with fenugreek oil for physical, thermal, mechanical, morphological, and antibacterial properties. The solubility, swelling, and amylose content of native and modified starch varied from 11.25–12.75%, 12.91–15.10 g/g, and 8.97–16.55%, respectively. The values of these parameters were reduced as the concentration of STMP increased. Cross-linked starch films showed lower moisture, solubility, water vapor permeability(WVP), and elongation at break (EB) values while having higher thickness, opacity, thermal, and tensile strength values. The microscopic images of cross-linked starch films showed smooth surfaces and the absence of ridges, pores, and cracks. The films loaded with fenugreek oil showed different results; the moisture content, water solubility, and tensile strength were decreased while thickness, opacity, WVP, and EB were increased. The onset temperature and peak temperature were lower, while enthalpy of gelatinization was increased to a greater extent than films without oil. The addition of fenugreek oil to films showed a good inhibition area of 40.22% for native+oil films and 41.53% for cross-linked+oil films % against Escherichia coli. This study confirmed the successful utilization of fenugreek oil as a very effective antimicrobial agent in preparing edible films.

Effect of Cross-Linking Modification on Structural and Film-Forming Characteristics of Pearl Millet (Pennisetum glaucum L.) Starch

Pearl millet starch was modified using epichlorohydrin (EPI) at different concentrations (0.1%; 0.3%; 0.5%; and 0.8%) and evaluated for physicochemical, rheological, in vitro digestibility, and film-forming characteristics. The degree of cross-linking was observed at higher levels (0.5% and 0.8%) of EPI. Upon cross-linking, breakdown and setback viscosity reduced whereas pasting temperature was increased. Storage modulus (G′) and loss modulus (G″) value of cross-linked (CL) starches ranged between 2877 to 5744 Pa and 168 to 237 Pa, respectively, during the frequency sweep test. A drastic decrease was observed for steady shear (yield stress and consistency index) characteristics of CL starches. Resistant starch (RS) content was increased after starch modification, which imparts its nutritional values and starch modified at 0.8% had the highest RS content. Modifications of starch at different levels had significant effects on the moisture, opacity, solubility and mechanical properties of films. Outcomes of this study will be helpful to understand the properties of native and CL starches for their potential applications in preparation of edible films.

Development and Characterization of Physical Modified Pearl Millet Starch-Based Films

Pearl millet is an underutilized and drought-resistant crop that is mainly used for animal feed and fodder. Starch (70%) is the main constituent of the pearl millet grain; this starch may be a good substitute for major sources of starch such as corn, rice, potatoes, etc. Starch was isolated from pearl millet grains and modified with different physical treatments (heat-moisture (HMT), microwave (MT), and sonication treatment (ST)). The amylose content and swelling capacity of the starches decreased after HMT and MT, while the reverse was observed for ST. Transition temperatures (onset (To), peak of gelatinization (Tp), and conclusion (Tc)) of the starches ranged from 62.92–76.16 °C, 67.95–81.05 °C, and 73.78–84.50 °C, respectively. After modification (HMT, MT, and ST), an increase in the transition temperatures was observed. Peak-viscosity of the native starch was observed to be 995 mPa.s., which was higher than the starch modified with HMT and MT. Rheological characteristics (storage modulus (G′) and loss modulus (G′′)) of the native and modified starches differed from 1039 to 1730 Pa and 83 to 94 Pa; the largest value was found for starch treated with ST and HMT. SEM showed cracks and holes on granule surfaces after HMT as well as MT starch granules. Films were prepared using both native and modified starches. The modification of the starches with different treatments had a significant impact on the moisture, transmittance, and solubility of films. The findings of this study will provide a better understanding of the functional properties of pearl millet starch for its possible utilization in film formation.