Investigation on the effect of cold drawing process on mechanical properties and structure of seamless steel (Ck60) tube

The cold drawing process is one of the precise metal forming techniques which have attracted attention by many researchers with respect to the given properties such as potential for improvement of mechanical properties of the material, achieving of accurate dimensional tolerances and rise of quality at final surface so that different studies are conducted on properties of various materials in the course of analysis of its effect. Using cold drawing and also exertion of special heat treatment cycle in this investigation, initially the seamless steel tube Ck60 has been produced and then effect of cold drawing has been assessed on the mechanical properties and structure of steel. The production process of seamless steel tube includes two phases of cold drawing which was followed by surface reduction levels 15.1% and 13.7% respectively. In order to analyze mechanical properties, tensile test and hardnesstesting was used and metallography test was also employed to observe the structure. The given results indicate that the seamless steel tube Ck60 produced by means of this production process has ultimate tensile strength (1021 MPa), yield strength (950 MPa) and elongation (9%). Moreover, the value of hardness mean was 312 for the final tube in Vickers Hardness Test. The images taken from optical microscopy also show that the final structure of tube is uniform and as perlite ferrite.

Investigation on the effect of cold drawing process on mechanical properties and structure of seamless steel (Ck60) tube

The cold drawing process is one of the precise metal forming techniques which have attracted attention by many researchers with respect to the given properties such as potential for improvement of mechanical properties of the material, achieving of accurate dimensional tolerances and rise of quality at final surface so that different studies are conducted on properties of various materials in the course of analysis of its effect. Using cold drawing and also exertion of special heat treatment cycle in this investigation, initially the seamless steel tube Ck60 has been produced and then effect of cold drawing has been assessed on the mechanical properties and structure of steel. The production process of seamless steel tube includes two phases of cold drawing which was followed by surface reduction levels 15.1% and 13.7% respectively. In order to analyze mechanical properties, tensile test and hardness-testing was used and metallography test was also employed to observe the structure. The given results indicate that the seamless steel tube Ck60 produced by means of this production process has ultimate tensile strength (1021 MPa), yield strength (950 MPa) and elongation (9%). Moreover, the value of hardness mean was 312 for the final tube in Vickers Hardness Test. The images taken from optical microscopy also show that the final structure of tube is uniform and as perlite ferrite.

Investigation on the effect of cold drawing process on mechanical properties and structure of seamless steel (Ck60) tube

The cold drawing process is one of the precise metal forming techniques which have attracted attention by many researchers with respect to the given properties such as potential for improvement of mechanical properties of the material, achieving of accurate dimensional tolerances and rise of quality at final surface so that different studies are conducted on properties of various materials in the course of analysis of its effect. Using cold drawing and also exertion of special heat treatment cycle in this investigation, initially the seamless steel tube Ck60 has been produced and then effect of cold drawing has been assessed on the mechanical properties and structure of steel. The production process of seamless steel tube includes two phases of cold drawing which was followed by surface reduction levels 15.1% and 13.7% respectively. In order to analyze mechanical properties, tensile test and hardness-testing was used and metallography test was also employed to observe the structure. The given results indicate that the seamless steel tube Ck60 produced by means of this production process has ultimate tensile strength (1021 MPa), yield strength (950 MPa) and elongation (9%). Moreover, the value of hardness mean was 312 for the final tube in Vickers Hardness Test. The images taken from optical microscopy also show that the final structure of tube is uniform and as perlite ferrite.

Investigation on the Effect of Cold Drawing Process on Mechanical Properties and Structure of Seamless Steel (Ck60) Tube

The cold drawing process is one of the precise metal forming techniques which have attracted attention by many researchers with respect to the given properties such as potential for improvement of mechanical properties of the material, achieving of accurate dimensional tolerances and rise of quality at final surface so that different studies are conducted on properties of various materials in the course of analysis of its effect. Using cold drawing and also exertion of special heat treatment cycle in this investigation, initially the seamless steel tube Ck60 has been produced and then effect of cold drawing has been assessed on the mechanical properties and structure of steel. The production process of seamless steel tube includes two phases of cold drawing which was followed by surface reduction levels 15.1% and 13.7% respectively. In order to analyze mechanical properties, tensile test and hardness-testing was used and metallography test was also employed to observe the structure. The given results indicate that the seamless steel tube Ck60 produced by means of this production process has ultimate tensile strength (1021 MPa), yield strength (950 MPa) and elongation (9%). Moreover, the value of hardness mean was 312 for the final tube in Vickers Hardness Test. The images taken from optical microscopy also show that the final structure of tube is uniform and as perlite ferrite.

Evaluation of accuracy of seamless steel tube scanning by industrial computed tomography

Measurement by computed tomography is very useful in evaluation of dimensions and internal structure. There are still some problems which need to be solved. Scanning accuracy depends, among other things, on the part´s material. Metal parts have high density and their scanning leads many times to failure. This paper deals with evaluation of accuracy of seamless steel tube scanning by industrial computed tomography. This method of scanning can lead to substitution of destructive method for measurement,but it is necessary to have knowledge if the scan has required accuracy. The tube with different diameters in length is scanned by X-Ray beam and it is evaluated inner and outer diameter, concentricity and wall thickness in 8 sections. The accuracy of scan is compared with reference values achieved by coordinate measuring machine in the same sections.