scholarly journals Direct synthesis of carbon nanotube aerogel using floating catalyst chemical vapor deposition: effect of gas flow rate

2020 ◽  
Vol 74 (10) ◽  
pp. 3359-3365
Author(s):  
Hayder B. Abdullah ◽  
Ramli Irmawati ◽  
Ismayadi Ismail ◽  
Nor Azah Yusof
Keyword(s):  
Chemical Vapor Deposition ◽  
Carbon Nanotube ◽  
Flow Rate ◽  
Vapor Deposition ◽  
Gas Flow ◽  
Direct Synthesis ◽  
Chemical Vapor ◽  
Gas Flow Rate ◽  
Deposition Effect ◽  
Catalyst Chemical Vapor Deposition

Synthesize of N-doped Carbon nanotube according to gas flow rate by Chemical Vapor Deposition

2011 ◽  
Author(s):  
J. B. Kim ◽  
C. D. Kim ◽  
S. J. Kong ◽  
J. H. Kim ◽  
B. K. Min ◽  
...  
Keyword(s):  
Chemical Vapor Deposition ◽  
Carbon Nanotube ◽  
Flow Rate ◽  
Vapor Deposition ◽  
Gas Flow ◽  
Chemical Vapor ◽  
Gas Flow Rate

Effects of Reaction Conditions on MoS2 Thin Film Formation Synthesized by Chemical Vapor Deposition using Organic Precursor

MRS Advances ◽  
2016 ◽  
Vol 2 (29) ◽  
pp. 1533-1538 ◽  
Author(s):  
S. Ishihara ◽  
Y. Hibino ◽  
N. Sawamoto ◽  
T. Ohashi ◽  
K. Matsuura ◽  
...  
Keyword(s):  
Thin Film ◽  
Chemical Vapor Deposition ◽  
Low Temperature ◽  
Flow Rate ◽  
Vapor Deposition ◽  
Gas Flow ◽  
Film Formation ◽  
Chemical Vapor ◽  
Gas Flow Rate ◽  
Axis Orientation

ABSTRACTMolybdenum disulfide (MoS2) thin films were fabricated by two-step chemical vapor deposition (CVD) using (t-C4H9)2S2 and the effects of temperature, gas flow rate, and atmosphere on the formation were investigated in order to achieve high-speed low-temperature MoS2 film formation. From the results of X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) investigations, it was confirmed that c-axis orientation of the pre-deposited Mo film has a significant involvement in the crystal orientation after the reaction low temperature sulfurization annealing and we successfully obtained 3 nm c-axis oriented MoS2 thin film. From the S/Mo ratios in the films, it was revealed that the sulfurization reaction proceeds faster with increase in the sulfurization temperature and the gas flow rate. Moreover, the sulfurization under the H2 atmosphere promotes decomposition reaction of (t-C4H9)2S2, which were confirmed by XPS and density functional theory (DFT) simulation.

Structural and Optical Properties of ZnO Nanotetrapods Deposited by Thermal Chemical Vapor Deposition with Different Gas Flow Rate

2015 ◽  
Vol 1109 ◽  
pp. 456-460
Author(s):  
Najwa Ezira Ahmed Azhar ◽  
Shafinaz Sobihana Shariffudin ◽  
Aimi Bazilah Rosli ◽  
A.K.S. Shafura ◽  
Mohamad Rusop
Keyword(s):  
Optical Properties ◽  
Chemical Vapor Deposition ◽  
Flow Rate ◽  
Vapor Deposition ◽  
Gas Flow ◽  
Chemical Vapor ◽  
Gas Flow Rate ◽  
Structural And Optical Properties ◽  
Thermal Chemical Vapor Deposition ◽  
Yellow Orange

ZnO nanotetrapod with different oxygen flow rate was prepared by thermal chemical vapor deposition. We have successfully deposited ZnO nanotetrapod on synthesis Zn powder using double furnace with argon (Ar) and oxygen (O2) gas as source material. In this study, we report the effect of different gas flow rate (5 sccm to 15 sccm) on structural and optical properties of the ZnO nanotetrapod. The morphology of ZnO nanotetrapods were analyzed by field emission scanning electron microscope (FE-SEM). It exhibits the length of the nanotetrapods arm decrease with increased of flow rate and diameter of nanotetrapod in range 30 nm to 90 nm. The optical properties were determined through XRD and photoluminescence with 2θ (30o to 80o) and wavelength 350 nm to 620 nm respectively. PL spectra show that the UV emission centred at 380 nm while yellow-orange emission centred at 540 nm.

Growth Promotion and Etching of Carbon Nanotubes by Carbon Dioxide in Chemical Vapor Deposition using Methane Gas

2007 ◽  
Vol 1057 ◽  
Author(s):  
Yoshiyuki Suda ◽  
Junichi Takayama ◽  
Takeshi Saito ◽  
Atsushi Okita ◽  
Junji Nakamura ◽  
...  
Keyword(s):  
Chemical Vapor Deposition ◽  
Flow Rate ◽  
Vapor Deposition ◽  
Gas Flow ◽  
Growth Promotion ◽  
Chemical Vapor ◽  
Gas Flow Rate ◽  
Preferential Growth ◽  
Ar Gas ◽  
Walled Cnts

ABSTRACTWe report the effect of CO2 addition to CO4 gas on carbon nanotube (CNT) growth by chemical vapor deposition. CO2 gas was introduced during the growth of CNTs on Fe0.05Mo0.025MgO0.925 and Ni0.05Mo0.025MgO0.925 catalysts by CO4 gas at a temperature of 800–850°C, and its concentration in a fraction of the gas flow rate was varied from 5×10−3 to 50%. In the experimental condition of the preferential growth of multi-walled CNTs, the carbon yield and the G/D ratio in the Raman spectra of the CNTs grown in 10%-CO2/CO4 were slightly higher than that grown in CO4 only. However, CNTs hardly grew when the CO2 concentration was more than 10%. We then prepared CO2 gas diluted with Ar gas (CO2/Ar) and varied its flow rate between 0 and 10 sccm. As the CO2/Ar gas flow rate was increased, the number of RBM peaks decreased even though the G/D ratio gradually decreased. The decrease in the RBM intensities of CNTs on the FeMoMgO catalyst was more significant than that of NiMoMgO.

Synthesis of InN nanowires grown on droplets formed with Au and self-catalyst on Si(111) by using metalorganic chemical vapor deposition

2010 ◽  
Vol 25 (9) ◽  
pp. 1778-1783 ◽  
Author(s):  
Seok-Hyo Yun ◽  
Suthan Kissinger ◽  
Don Wook Kim ◽  
Jun-Ho Cha ◽  
Yong-Ho Ra ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Chemical Vapor Deposition ◽  
Flow Rate ◽  
Vapor Deposition ◽  
Gas Flow ◽  
Metalorganic Chemical Vapor Deposition ◽  
Chemical Vapor ◽  
Chamber Pressure ◽  
Gas Flow Rate ◽  
Metalorganic Chemical

We demonstrated the growth of indium nitride (InN) nanowires on Si(111) substrates by metalorganic chemical vapor deposition without the use of any intermediate GaN or AlN buffer layer. The InN nanowires were grown by forming the Au + In droplets and In droplets on the Au- and In-coated Si substrate. The growth conditions such as chamber pressure, chamber temperature, reaction gas flow rate, and carrier gas flow rate were optimized to yield nanowires free from contamination. Depending on the growth parameters different growth regimes for the InN nanowires were identified. The strength of self-catalytic route has been highlighted. The morphology and microstructures of samples were characterized by x-ray diffraction and scanning electron microscopy (SEM). The transmission electron microscopy and SEM investigations showed that the InN nanowires are single crystals with diameters ranging from 40 to 400 nm, and lengths up to 3 µm. Photoluminescence spectra of the InN nanowires showed a strong broad emission peak at 0.77 eV.

Sign in / Sign up

Export Citation Format

Share Document