Microstructures and mechanical properties of brazed 6063 aluminum alloy joint with Al-Cu-Si-Ni filler metal

2020 ◽  
Vol 64 (11) ◽  
pp. 1933-1938
Author(s):  
Chong Pei ◽  
Xin Wu ◽  
Guoqing Zhang ◽  
Yaoyong Cheng ◽  
Xinyu Ren ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Filler Metal ◽  
6063 Aluminum Alloy ◽  
Microstructures And Mechanical Properties

scholarly journals Microstructures and Mechanical Properties of a Laser-Welded Joint of Ti3Al-Nb Alloy Using Pure Nb Filler Metal

Metals ◽  
2018 ◽  
Vol 8 (10) ◽  
pp. 785 ◽  
Author(s):  
Lin Wang ◽  
Daqian Sun ◽  
Hongmei Li ◽  
Xiaoyan Gu ◽  
Chengjie Shen
Keyword(s):  
Mechanical Properties ◽  
Solid Solution ◽  
Base Metal ◽  
Joint Strength ◽  
Filler Metal ◽  
Weld Zone ◽  
Strengthening Effect ◽  
Joint Properties ◽  
Microstructures And Mechanical Properties ◽  
Welding System

Ti3Al-Nb alloy (Ti-24Al-15Nb) was welded by a pulsed laser welding system without and with pure Nb filler metal. The results indicated that pure Nb filler metal had profound effects on the microstructures and mechanical properties of the laser-welded joints. The joint without filler metal consisted of the weld zone (α’2 + B2), heat affected zone HAZ1 (α2 + B2), HAZ2 (α2 + O + B2) and base metal (α2 + O + B2), and gas pores were generated in the weld resulting in the deterioration of the joint strength (330 MPa) and elongation (1.9%). When the Nb filler metal was used, the weld microstructure (NbTi solid solution + O + B2) was obtained, and the joint properties were significantly improved, which was associated with the strengthening effect of the NbTi solid solution, O phase precipitation and the slip transmission between O and B2 phases, and the restraining of the formation of martensite (α’2) and gas pores in the weld. The strength (724 MPa) and elongation (5.1%) of the joint increased by 119.4% and 168.4% compared with those of the joint without filler metal, and the joint strength was able to reach 81.7% of the base metal strength (886 MPa). It is favorable to use pure Nb filler metal for improving the mechanical properties of laser-welded Ti3Al-Nb alloy joints.

Study on Microstructures and Mechanical Properties of Rheo-Die Casting Semi-Solid A356 Aluminum Alloy

2006 ◽  
Vol 116-117 ◽  
pp. 453-456 ◽  
Author(s):  
Yong Lin Kang ◽  
Yue Xu ◽  
Zhao Hui Wang
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Die Casting ◽  
A356 Alloy ◽  
Experimental Results ◽  
A356 Aluminum Alloy ◽  
Microstructures And Mechanical Properties ◽  
A356 Aluminum ◽  
Semi Solid

In this paper, with a newly self-developed rotating barrel rheomoulding machine(RBRM), microstructures and mechanical properties of rheo-die casting A356 alloy were studied. In order to clearly show the characteristic of rheo-die casting, liquid die casting and semi-solid casting were done too. The experimental results showed that microstructures of rheo-die casting were composed of solid grains, which were finer and rounder, and had fewer pores. In the three technologies, integrated mechanical properties of semi-solid rheo-die casting were the best.

Sign in / Sign up

Export Citation Format

Share Document