Predicting the mechanisms and crack growth rates of pipelines undergoing stress corrosion cracking at high pH

2009 ◽  
Vol 51 (11) ◽  
pp. 2657-2674 ◽  
Author(s):  
F.M. Song
Author(s):  
Bogdan Alexandreanu ◽  
Yiren Chen ◽  
Ken Natesan ◽  
Bill Shack

The objective of this work is to determine the cyclic and stress corrosion cracking (SCC) crack growth rates (CGRs) in a simulated PWR water environment for Alloy 690 heat affected zone (HAZ). In order to meet the objective, an Alloy 152 J-weld was produced on a piece of Alloy 690 tubing, and the test specimens were aligned with the HAZ. The environmental enhancement of cyclic CGRs for Alloy 690 HAZ was comparable to that measured for the same alloy in the as-received condition. The two Alloy 690 HAZ samples tested exhibited maximum SCC CGR rates of 10−11 m/s in the simulated PWR environment at 320°C, however, on average, these rates are similar or only slightly higher than those for the as-received alloy.


Author(s):  
Bruce C. Bunker ◽  
William H. Casey

Although dissolution reactions involving water can etch and decompose oxides, truly catastrophic failures of oxide structures usually involve fractures and mechanical failures. Geologists and geochemists have long recognized that water and ice both play key roles in promoting the fracture and crumbling of rock (see Chapter 17). Freezing and thawing create stresses that amplify the rate at which water attacks metal–oxygen bonds at the crack tip. The interplay between water and stressed oxides also leads to common failures in man-made objects, ranging from the growth of cracks from flaws in windshields to the rupture of optical fibers in communication systems. In this chapter, we outline how mechanical deformations change the reactivity of metal–oxygen bonds with respect to water and other chemicals, and how reactions on strained model compounds have been used to predict time to failure as a function of applied stress. The basic phenomenon of stress corrosion cracking is illustrated in Figure 16.1. Cracks can propagate through oxide materials at extremely fast rates, as anyone who has dropped a wine glass on the floor can attest. High-speed photography reveals that when glass shatters, cracks can spread at speeds of hundreds of meters per second, or half the speed of sound in the glass. At the other end of the spectrum, cracks in glass can grow from preexisting flaws so slowly that only a few chemical bonds are broken at the crack tip per hour. Because mechanical failures are associated with cracking, it is critical for design engineers to understand the factors that control crack growth rates for this enormous range of crack velocities (a factor of 1012). In addition, because it is difficult to measure crack velocities slower than 10−8 m/second, it is often necessary to make major extrapolations from measured data to predict the long-term reliability of glass and ceramic objects. Will an optical fiber under stress fail in 1 year or 10 years? Answering this question can require accurate extrapolations down to crack growth rates as low as 10−10 m/second.


Author(s):  
Haotian Sun ◽  
Wenxing Zhou ◽  
Jidong Kang

AbstractThis paper presents a review of four existing growth models for near-neutral pH stress corrosion cracking (NNpHSCC) defects on buried oil and gas pipelines: Chen et al.’s model, two models developed at the Southwest Research Institute (SwRI) and Xing et al.’s model. All four models consider corrosion fatigue enhanced by hydrogen embrittlement as the main growth mechanism for NNpHSCC. The predictive accuracy of these growth models is investigated based on 39 crack growth rates obtained from full-scale tests conducted at the CanmetMATERIALS of Natural Resources Canada of pipe specimens that are in contact with NNpH soils and subjected to cyclic internal pressures. The comparison of the observed and predicted crack growth rates indicates that the hydrogen-enhanced decohesion (HEDE) component of Xing et al.’s model leads to on average reasonably accurate predictions with the corresponding mean and coefficient of variation (COV) of the observed-to-predicted ratios being 1.06 and 61.2%, respectively. The predictive accuracy of the other three models are markedly poorer. The analysis results suggest that further research is needed to improve existing growth models or develop new growth models to facilitate the pipeline integrity management practice with respect to NNpHSCC.


Author(s):  
Meryl Hall, Jr

For 50 years, researchers have considered how time-dependent environmental effects can be included in cycle-dependent corrosion fatigue (CF) crack growth rate (CGR) models. Common assumptions are that cycle- and time-dependent contributions are separable, operate in parallel, are non-interacting and that total environmental CGR can be obtained by linear summation of cycle-dependent fatigue and time-dependent (SCC) CGRs. However, considered here are data and analyses that show that environmental CGRs may be greater than predicted by superposition models. A phenomenological model is developed to quantify the effect of crack-tip strain-rate due to fatigue stress-cycles on electrochemical activity at a crack tip and thereby synergistically increase crack growth rates by a cyclic-stress corrosion-cracking (C-SCC) mechanism.


1999 ◽  
Vol 556 ◽  
Author(s):  
F. King ◽  
C. D. Litke ◽  
B. M. Ikeda

AbstractThe extent of stress corrosion cracking (SCC) of copper nuclear waste containers is being predicted on the basis of a “limited propagation” argument. In this argument, it is accepted that crack initiation may occur, but it is argued that the environmental conditions and material properties required for a through-wall crack to propagate will not be present.In this paper, the effect of one environmental parameter, the supply of oxidant (Jox), on the crack growth rate is examined. Experiments have been conducted on two grades of Cu in NaNO2 environments using two loading techniques. The supply of oxidant has been varied either electrochemically in bulk solution using different applied current densities or by embedding the loaded test specimens in compacted buffer material containing O2 as the oxidant. Measured and theoretical crack growth rates as a function of Jox are compared with the predicted oxidant flux to the containers in a disposal vault and an estimate of the maximum crack depth on a container obtained.


1992 ◽  
Vol 114 (2) ◽  
pp. 171-177
Author(s):  
P. S. Maiya ◽  
B. K. Pai

The intergranular stress corrosion cracking (IGSCC) of sensitized Type 304 stainless steel (SS) has been investigated by slow strain rate tests (SSRTs) in 289°C water containing sulfate impurity. Both smooth and circumferentially notched specimens were used to assess the effects of strain concentrations on stress corrosion cracking (SCC). Experiments were conducted over a range of nominal strain rates of 10−5 to 10−7 s−1. A comparison of the results observed for the smooth and notched specimens suggests that the estimated growth rates of small cracks in SSRT specimen geometry is influenced by the presence of strain concentrations. In particular, the average crack growth rates estimated from tests performed at the same nominal strain rate are observed to increase with the notch depth, and power-law relationships exist between strain rate and SCC parameters such as failure time and crack growth rate. The strain concentration factors at the notch roots of Type 304 specimens subjected to axial load have been estimated by finite-element elastic-plastic stress analyses, as well as by Neuber’s rule. The nominal and crack-tip strain rate effects on SCC in both smooth and notched specimens are interpreted in terms of a model based on elastic-plastic fracture mechanics and film-rupture mechanisms that invoke diffusion-controlled SCC growth kinetics.


Author(s):  
Hamid Niazi ◽  
Shidong Wang ◽  
Lyndon Lamborn ◽  
Reg Eadie ◽  
Weixing Chen ◽  
...  

Author(s):  
Frank Y. Cheng

A thermodynamic model was developed to determine the interactions of hydrogen, stress and anodic dissolution at the crack-tip during near-neutral pH stress corrosion cracking in pipelines. By analyzing the free-energy of the steel in the presence and absence of hydrogen and stress, it is demonstrated that a synergism of hydrogen and stress promotes the cracking of the steel. The enhanced hydrogen concentration in the stressed steel significantly accelerates the crack growth. The quantitative prediction of the crack growth rate in near-neutral pH environment is based on the determination of the effect of hydrogen on the anodic dissolution rate in the absence of stress, the effect of stress on the anodic dissolution rate in the absence of hydrogen, the synergistic effect of hydrogen and stress on the anodic dissolution rate at the crack-tip and the effect of the variation of hydrogen concentration on the anodic dissolution rate.


Author(s):  
Frederick W. Brust ◽  
Paul M. Scott

There have been incidents recently where cracking has been observed in the bi-metallic welds that join the hot leg to the reactor pressure vessel nozzle. The hot leg pipes are typically large diameter, thick wall pipes. Typically, an inconel weld metal is used to join the ferritic pressure vessel steel to the stainless steel pipe. The cracking, mainly confined to the inconel weld metal, is caused by corrosion mechanisms. Tensile weld residual stresses, in addition to service loads, contribute to PWSCC (Primary Water Stress Corrosion Cracking) crack growth. In addition to the large diameter hot leg pipe, cracking in other piping components of different sizes has been observed. For instance, surge lines and spray line cracking has been observed that has been attributed to this degradation mechanism. Here we present some models which are used to predict the PWSCC behavior in nuclear piping. This includes weld model solutions of bimetal pipe welds along with an example calculation of PWSCC crack growth in a hot leg. Risk based considerations are also discussed.