In-situ reaction synthesis of composite coating on titanium alloy for improving high temperature oxidation resistance

2017 ◽  
Vol 729 ◽  
pp. 970-977 ◽  
Author(s):  
Wenbo Du ◽  
Shasha Zhang ◽  
Xixi Luo ◽  
Xuewei Tao ◽  
Chao Fang ◽  
...  
Keyword(s):  
Titanium Alloy ◽  
High Temperature ◽  
Composite Coating ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Reaction Synthesis ◽  
Temperature Oxidation ◽  
In Situ Reaction

scholarly journals High-temperature oxidation resistance of VCps-reinforced Fe-matrix composites using an in-situ reaction

AIP Advances ◽  
2019 ◽  
Vol 9 (1) ◽  
pp. 015319
Author(s):  
Pinghu Chen ◽  
Ruiqing Li ◽  
Ripeng Jiang ◽  
Songsheng Zeng ◽  
Yun Zhang ◽  
...  
Keyword(s):  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Matrix Composites ◽  
Temperature Oxidation ◽  
In Situ Reaction

ENHANCING HIGH-TEMPERATURE OXIDATION RESISTANCE OF TITANIUM ALLOY WITH KF110-B4C-Ag THROUGH LASER TECHNOLOGY

2021 ◽  
Author(s):  
ZHAO ZHANG ◽  
JIANING LI ◽  
ZHIYUN YE ◽  
CAINIAN JING ◽  
MENG WANG ◽  
...  
Keyword(s):  
Titanium Alloy ◽  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Mass Gain ◽  
Temperature Oxidation ◽  
Laser Technology ◽  
X Ray ◽  
Ta15 Titanium Alloy ◽  
Oxidation Resistant

In this paper, the high-temperature oxidation resistant coating on the TA15 titanium alloy by laser cladding (LC) of the KF110-B4C-Ag mixed powders was analyzed in detail. The scanning electron microscope (SEM) and energy dispersive X-ray spectrometer (EDS) images indicated that a good metallurgy bond between the fabricated coating/TA15 was formed; also the fine/compact microstructure was produced after a cladding process. The oxidation mass gain of TA15 was higher than that of the coating after LC process, which were 3.72 and 0.91[Formula: see text]mg[Formula: see text]cm[Formula: see text], respectively, at 60[Formula: see text]h, greatly enhancing the high temperature oxidation resistance.

Effect of B on the Microstructures and High Temperature Oxidation Resistance of a Nb-Si System In Situ Composite

2007 ◽  
Vol 546-549 ◽  
pp. 1489-1494 ◽  
Author(s):  
Ai Qin Liu ◽  
Shu Suo Li ◽  
Lu Sun ◽  
Ya Fang Han
Keyword(s):  
High Temperature ◽  
Oxide Scale ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Temperature Oxidation ◽  
X Ray ◽  
Solid Solution Strengthening ◽  
Arc Melting ◽  
The Matrix

Nb-16Si-24Ti-6Cr-6Al-2Hf-xB(x=0, 0.5, 1, 2, 4, 6) in situ composites were prepared by arc-melting. Microstructure and the effect of boron on 1250C oxidation resistance of the composites were investigated by scanning electron microscopy(SEM) and X-ray energy disperse spectrum(EDS) as well as X-ray diffraction(XRD). The experimental results showed that the high temperature oxidation resistance of the alloy was remarkably improved by adding proper amount of boron. This may be resulted from several beneficial roles of boron, i.e., boron improves the resistance of Nb5Si3 by solid solution strengthening, inhibits the diffusion of oxygen in the matrix, improves the adherence between the oxide scale and the substrate and increases the cracking resistance of the oxide scale.

Study on Properties of Al2TiO5 Coating on Ti-6Al-4V Titanium Alloy

2013 ◽  
Vol 575-576 ◽  
pp. 348-351
Author(s):  
Nian Suo Xie ◽  
Jin Wang
Keyword(s):  
Corrosion Resistance ◽  
Titanium Alloy ◽  
Sulfuric Acid ◽  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Acid Corrosion ◽  
Temperature Oxidation ◽  
Micro Arc Oxidation ◽  
Sulfuric Acid Corrosion

The Al2TiO5Coating was deposited on Ti-6Al-4V alloy substrate by homemade micro-arc oxidation system. The microstructure of Ti-6Al-4V titanium alloy, the phase of coating, the bonding force of the coating and matrix, sulfuric acid corrosion resistance and high-temperature oxidation resistance were study by inverted microscope model, Xray diffract meter, scanning electron microscopy, the coating adhesion automatic scratch tester, box-type furnace. The results show that the phase of coating is composed of Al2TiO5and Al2SiO5, and Al2TiO5.is the main component, the coating surface consists of discharging pit and flange which are unequal in size, rough and overlap and micro-arc oxidation pit diameter increases with the voltage. When micro-arc oxidation voltage is constant, the longer micro-arc oxidation time, the greater the Ti-6Al-4V alloy coating and the substrate binding force. The corrosion resistance of Ti-6Al-4V alloy was improved in sulfuric acid due to micro-arc oxidation; the sulfuric acid corrosion resistance of the coated samples was improved 11 times when the micro-arc oxidation time increased from 5min to 60min. the high-temperature oxidation resistance of Ti-6Al-4V alloy with micro-arc oxidation coatings is higher than Ti-6Al-4V alloy without micro-arc oxidation coating.

Sign in / Sign up

Export Citation Format

Share Document