Experimental investigation and characterization of brass – AlN composites synthesized using powder metallurgy technique

2020 ◽  
Vol 21 ◽  
pp. 164-168 ◽  
Author(s):  
B. Stalin ◽  
M. Ravichandran ◽  
S. Jasper ◽  
J. Vairamuthu
2015 ◽  
Vol 819 ◽  
pp. 309-313 ◽  
Author(s):  
M.S. Syaza Nabilla ◽  
C.D. Zuraidawani ◽  
M.N. Derman

Magnesium (Mg) has a great potential to be used in various field of work since it is lightweight and has low density properties. However, its application is limited due to its poor properties for Mg has a relatively low strength. Improvement is made by mixing Mg with calcium (Ca) as composite element for it is lightweight and non-toxic. In this research, Mg is prepared with different weight percentage (0, 0.5, 1, 1.5, 2 wt. %) of Ca with pure Mg as reference prepared by powder metallurgy (PM) method to study the mechanical properties. Morphological analysis carried out by optical microscope shows increase grain refinement with the increase of calcium content in Mg-Ca composites. The phase transition upon addition of Ca is determined using XRD method detects formation of Mg2Ca. Range from 1.78 g/cm3to 1.83 g/cm3, the density of each sample composite increase. While porosity profiles show inverse characteristics upon addition of Ca. Microhardness strengths also intensifies up to 193.20 MPa as more Ca content added in.


Materials ◽  
2005 ◽  
Author(s):  
C. S. Goh ◽  
J. Wei ◽  
M. Gupta

Magnesium nanocomposites with 0.1, 0.2, 0.3 and 0.4 volume percentages of MgO were synthesized using the powder metallurgy technique. The nanocomposite billets obtained were subsequently hot extruded at a temperature of 350 °C with an extrusion ratio of 20.25:1. The extruded nanocomposites were characterized for their microstructural, physical and mechanical properties. The microstructures of the nanocomposites showed individual particles of MgO uniformly distributed in the magnesium matrix. The thermomechanical analysis results revealed that a more thermally stable magnesium nanocomposite could be obtained with a threshold amount of MgO. The tensile properties results indicated that the yield strength peaks at 0.3 vol.% of reinforcement incorporated, with an improvement of approximately 17%. An attempt is made to correlate the volume fraction of the MgO with the resultant physical and mechanical properties of the magnesium nanocomposites.


2021 ◽  
Vol 26 (4) ◽  
Author(s):  
Mayara Ribeiro Masseli ◽  
Bruna Horta Bastos Kuffner ◽  
Lucas Victor Benjamim Vasconcelos ◽  
Gilbert Silva ◽  
Daniela Sachs

ABSTRACT The hydroxyapatite calcium phosphate based ceramic (Hap) is widely used for bone repair, as it is a biocompatible biomaterial and because it has osteoconductive and osteoinductive properties. However, the low mechanical strength of Hap may limit its applicability. Thus, the present work aims to improve the mechanical properties of Hap, associating it with alumina (Al2O3), using the powder metallurgy technique, which consists in the milling of the precursor powders in a planetary ball mill, uniaxial pressing and sintering. The microstructure and mechanical strength of the sintered samples were evaluated using density, microhardness, compressive strength and wettability tests. It was concluded that the use of Al2O3 in the composite improves the mechanical properties of Hap, while decreases its hydrophilic potential. Thus, the composition with 40% Hap / 60% Al2O3 was considered the best for biomedical applications.


2014 ◽  
Vol 984-985 ◽  
pp. 124-128 ◽  
Author(s):  
R. Anish ◽  
M.S. Pragash ◽  
G. Robert Singh

In this study AZ31B Mg alloy is developed by powder metallurgy route followed by hot extrusion. The extruded materials were characterized for microstructure, X-ray diffraction (XRD), density, porosity and mechanical properties such as tensile, compression, impact and micro hardness. The SEM analysis of fractured surface of AZ31B Mg alloy showed quasi-cleavage fracture mode.