CoFe 2 O 4/ Pb ( Zr 0.53 Ti 0.47) O 3 (abbreviated as CFO/PZT) multiferroic composite thick films were successfully fabricated on alumina substrate with gold bottom electrode by screen printing method at a low-sintering temperature. The processing included the modification and dispersion of ferromagnetic CFO powder and ferroelectric PZT powder, the preparation of uniform pastes, and the selection of proper annealing temperature for composite thick films. Transmission electron microscopic pictures (TEM) indicated the submicron meter of particles size for both CFO and PZT particles. After annealing at 900°C for 1 h in air, tape test confirmed the quality of multiferroic thick films as well as pure CFO and PZT films. X-ray diffraction (XRD) showed a coexistence of CFO and PZT phases; furthermore, a smooth surface was observed through scanning electron microscopic (SEM) pictures along with the sharp cross-sectional picture, indicative of 100 μm of film thickness. Ferromagnetic and ferroelectric properties were observed in CFO/PZT films simultaneously at room temperature. Compared with the reported CFO/PZT multiferrroic thin films, the present ferromagnetic property was closing to that of the chemical sol-gel synthesized film and even that from the physical pulsed laser deposition technique. However, the ferroelectric property showed a degenerated behavior, possible reasons for this was discussed and further optimization was also proposed for the potential multifunctional application.
Luminescence Characteristics of ZnGa2O4Phosphor Thick Films Prepared by Screen Printing Method