scholarly journals Oxidation and hot corrosion behaviors of Nb−Si based ultrahigh temperature alloys at 900 °C

2021 ◽  
Vol 31 (1) ◽  
pp. 207-221
Author(s):  
Jia-hua HE ◽  
Xi-ping GUO ◽  
Yan-qiang QIAO
Keyword(s):  
Hot Corrosion ◽  
Corrosion Behaviors ◽  
Ultrahigh Temperature

HOT-CORROSION BEHAVIOR OF THERMAL BARRIER COATED DZ125 SUPERALLOY EXPOSED TO ATOMIZED SEAWATER AND KEROSENE

2010 ◽  
Vol 24 (15n16) ◽  
pp. 3155-3160
Author(s):  
ZHIMING BAI ◽  
LE ZHOU ◽  
TIANQUAN LIANG ◽  
HONGBO GUO ◽  
SHENGKAI GONG
Keyword(s):  
Corrosion Resistance ◽  
Electron Beam ◽  
Thermal Barrier Coating ◽  
Corrosion Behavior ◽  
Bond Coat ◽  
Hot Corrosion ◽  
Thermal Barrier ◽  
Average Mass ◽  
Barrier Coating ◽  
Corrosion Behaviors

The bare superalloy DZ 125 alloy, the aluminide coated specimens and electron beam physical vapor deposited (EB-PVD) thermal barrier coating (TBC) consisting of yttria stabilizied zirconia (YSZ) topcoat and NiCoCrAlY bond coat specimens were exposed to atomized seawater and kerosene at 900°C and the cyclic hot-corrosion behaviors of the specimens were investigated. Disastrous spallation of the bare superalloy occurred within 50 h hot-corrosion. In contrast to this, after 100 h hot-corrosion, the average mass change for the aluminized and TBC coated specimens is 0.7 mg/cm2 and 0.63 mg/cm2, respectively, exhibiting excellent hot-corrosion resistance.

The effect of Nb and Si on the hot corrosion behaviors of TiAl coatings on a Ti-6Al-4V alloy

2020 ◽  
Vol 168 ◽  
pp. 108578 ◽  
Author(s):  
Jingjie Dai ◽  
Hongxia Zhang ◽  
Caixia Sun ◽  
Shouying Li ◽  
Chuanzhong Chen ◽  
...  
Keyword(s):  
Hot Corrosion ◽  
Corrosion Behaviors
Sign in / Sign up

Export Citation Format

Share Document