Synthesis and Rietveld refinements of new ceramics Sr2CaFe2WO9 and Sr2PbFe2TeO9 perovskites

2018 ◽  
Vol 33 (2) ◽  
pp. 134-140 ◽  
Author(s):  
Abdelhadi El Hachmi ◽  
Y. Tamraoui ◽  
Bouchaib Manoun ◽  
R. Haloui ◽  
M.A. Elaamrani ◽  
...  
Keyword(s):  
Room Temperature ◽  
Rietveld Analysis ◽  
Double Perovskites ◽  
Unit Cell Parameters ◽  
Rietveld Refinements ◽  
X Ray ◽  
Cell Parameters ◽  
State Technique ◽  
Xrpd Patterns ◽  
Polycrystalline Form

Ceramics of Sr2CaFe2WO9 and Sr2PbFe2TeO9 double perovskites have been prepared in polycrystalline form by solid-state technique, in the air. The crystalline structure was analyzed using X-ray powder diffraction (XRPD) at room temperature. Rietveld analysis of XRPD patterns show that both compounds adopt a tetragonal structure with space group I4/m, with unit cell parameters a = 5.5453(1) Å, c = 7.8389(1) Å for Sr2CaFe2WO9, and a = 5.5994(15) Å, c = 7.8979(30) Å for Sr2PbFe2TeO9. A certain degree of anti-site disordering of W and/or Te and Fe on the B –sites have been detected, indicating the presence of a partial amount of W and/or Te at Fe positions and vice versa.

Crystallochemistry and structural studies of two newly CaSb0.50Fe1.50(PO4)3 and Ca0.50SbFe(PO4)3 Nasicon phases

2006 ◽  
Vol 21 (1) ◽  
pp. 45-51 ◽  
Author(s):  
Abderrahim Aatiq ◽  
My Rachid Tigha ◽  
Rabia Hassine ◽  
Ismael Saadoune
Keyword(s):  
Solid State ◽  
Room Temperature ◽  
Rietveld Analysis ◽  
Structural Studies ◽  
Hexagonal Cell ◽  
Conventional Solid State Reaction ◽  
Space Group ◽  
X Ray ◽  
Cell Parameters ◽  
Crystallographic Structures

Crystallographic structures of two new orthophosphates Ca0.50SbFe(PO4)3 and CaSb0.50Fe1.50(PO4)3 obtained by conventional solid state reaction techniques at 900 °C, were determined at room temperature from X-ray powder diffraction using Rietveld analysis. The two compounds belong to the Nasicon structural family. The space group is R3 for Ca0.50SbFe(PO4)3 and R3c for CaSb0.50Fe1.50(PO4)3. Hexagonal cell parameters for Ca0.50SbFe(PO4)3 and CaSb0.50Fe1.50(PO4)3 are: a=8.257(1) Å, c=22.276(2) Å, and a=8.514(1) Å, c=21.871(2) Å, respectively. Ca2+ and vacancies in {[Ca0.50]3a[◻0.50]3b}M1SbFe(PO4)3 are ordered within the two positions, 3a and 3b, of M1 sites. Structure refinements show also a quasi-ordered distribution of Sb5+ and Fe3+ ions within the Nasicon framework. Thus, in {[Ca0.50]3a[◻0.50]3b}M1SbFe(PO4)3, each Ca(3a)O6 octahedron shares two faces with two Fe3+O6 octahedra and each vacancy (◻(3b)O6) site is located between two Sb5+O6 octahedra. In [Ca]M1Sb0.50Fe1.50(PO4)3 compound (R3c space group), all M1 sites are occupied by Ca2+ and the Sb5+ and Fe3+ ions are randomly distributed within the Nasicon framework.

Heterobimetallische 3d-4f-Komplexe mit Bis(1,2-dithiooxalato)nickelat(II) als planarem Brückenbaustein / Heterobimetallic 3d-4f-Complexes with Bis(1,2-dithiooxalato)nickelate(II) as Planar Bridging Block

2005 ◽  
Vol 60 (11) ◽  
pp. 1149-1157 ◽  
Author(s):  
Matthias Siebold ◽  
Alexandra Kelling ◽  
Uwe Schilde ◽  
Peter Strauch
Keyword(s):  
Room Temperature ◽  
Magnetic Moments ◽  
Lanthanide Ions ◽  
Water Molecules ◽  
Unit Cell Parameters ◽  
Ionic Radii ◽  
X Ray ◽  
Cell Parameters ◽  
Heterobimetallic Complexes ◽  
The Individual

Planar bis(1,2-dithiooxalato)nickelates(II) react in aqueous solutions of lanthanide ions to form pentanuclear, heterobimetallic complexes of the general composition [{Ln(H2O)n}2- {Ni(dto)2}3]・xH2O (Ln = Y3+, La3+, Ce3+, Pr3+, Nd3+, Sm3+, Eu3+, Gd3+, Tb3+, Dy3+, Ho3+, Er3+, Tm3+, Yb3+, Lu3+; n = 4 or 5; x = 9 - 12). With [{Nd(H2O)5}2{Ni(S2C2O2)2}3]・xH2O (x = 10 - 12) (1) and [{Er(H2O)4}2{Ni(S2C2O2)2}3]・xH2O (x = 9 - 10) (2) we were able to isolate two complexes of this series as single crystals, which were characterized by X-ray structure analysis. Depending on the individual ionic radii of the lanthanide ions, the compounds crystallize in two different crystal systems with the following unit cell parameters: 1, monoclinic in P21/c with a = 11.3987(13), b = 11.4878(8), c = 20.823(2) Å , β = 98.907(9)° and Z = 2; 2, triclinic in P1̅ with a = 10.5091(6), b = 11.0604(6), c = 11.2823(6) Å , α = 107.899(4)°, β = 91.436(4)°, γ = 112.918(4)° and Z = 1. The channels and cavities appearing in the packing of the molecules are occupied by uncoordinated water molecules. High magnetic moments up to 14.65 BM./f.u. have been observed at room temperature due to the combined moments of the individual lanthanide ions.

A new BaCa(CO3)2 polymorph

2019 ◽  
Vol 75 (3) ◽  
pp. 291-300
Author(s):  
Dominik Spahr ◽  
Lkhamsuren Bayarjargal ◽  
Victor Vinograd ◽  
Rita Luchitskaia ◽  
Victor Milman ◽  
...  
Keyword(s):  
Density Functional ◽  
Rietveld Analysis ◽  
Radioactive Isotopes ◽  
Synthesis Product ◽  
Monoclinic Space Group ◽  
Unit Cell Parameters ◽  
Functional Theory ◽  
Model Calculations ◽  
X Ray ◽  
Cell Parameters

A new polymorph of the double carbonate BaCa(CO3)2, `a C2 phase', has been synthesized. Its structure has been obtained by density-functional-theory-based (DFT-based) model calculations and has been refined by Rietveld analysis of X-ray powder diffraction data. The structure of the new polymorph differs significantly from those of the established polymorphs barytocalcite, paralstonite and alstonite. The unit-cell parameters of the new monoclinic (space group C2) compound are a = 6.6775 (5), b = 5.0982 (4), c = 4.1924 (3) Å, β = 109.259 (1)°. The new compound has been further characterized using Raman spectroscopy. This work shows that earlier studies have misidentified the products of an established synthesis route and that findings based on the incorrect identification of the synthesis product concerning the suitability of barytocalcite as a matrix for the retention of radioactive isotopes will need to be reconsidered.

Synthesis and structural characterization of ASnFe(PO4)3 (A=Na2,Ca,Cd) phosphates with the Nasicon type structure

2004 ◽  
Vol 19 (3) ◽  
pp. 272-279 ◽  
Author(s):  
Abderrahim Aatiq
Keyword(s):  
Room Temperature ◽  
Random Distribution ◽  
Rietveld Analysis ◽  
Type Structure ◽  
Conventional Solid State Reaction ◽  
X Ray ◽  
Cell Parameters ◽  
Nasicon Type ◽  
Cationic Distribution

The crystal structures of ASnFe(PO4)3 (A=Na2, Ca, Cd) phases, obtained by conventional solid state reaction techniques at (950–1000 °C), were determined at room temperature from X-ray powder diffraction (XRD) using Rietveld analysis. The three materials exhibit the Nasicon-type structure (R3c space group, Z=6) with a random distribution of Sn(Fe) within the framework. Hexagonal cell parameters when A=Na2, Ca and Cd are: a=8.628(1) Å, c=22.151(2) Å; a=8.569(1) Å, c=22.037(2) Å and a=8.587(1) Å, c=21.653(2) Å, respectively. Structural refinements show a partial occupancy of M1 (Na(1)) and M2 (Na(2)) sites in Na2SnFe(PO4)3 leading to the cationic distribution [Na1.22□1.78]M2[Na0.78□0.22]M1SnFe(PO4)3. Ca2+ ions are distributed only in the M1 site of [□3]M2[Ca]M1SnFe(PO4)3. From XRD data, it is difficult to unambiguously distinguish between Cd2+ and Sn4+ ions in CdSnFe(PO4)3. Nevertheless the overall set of cation–anion distances within the Nasicon framework clearly shows that the cationic distribution can be illustrated by the [□3]M2[Cd]M1SnFe(PO4)3 crystallographic formula. Distortion within the [Sn(Fe)(PO4)3] frameworks, in ASnFe(PO4)3 (A=Na2,Ca,Cd) phases, is shown to be related to the M1 site size. © 2004 International Centre for Diffraction Data.

X-ray powder diffraction data of anilinium trimolybdate tetrahydrate and anilinium trimolybdate dihydrate

1999 ◽  
Vol 14 (4) ◽  
pp. 280-283 ◽  
Author(s):  
A. Rafalska-Łasocha ◽  
W. Łasocha ◽  
M. Michalec
Keyword(s):  
Powder Diffraction ◽  
Diffraction Data ◽  
Room Temperature ◽  
Unit Cell ◽  
Powder Diffraction Data ◽  
Unit Cell Parameters ◽  
Space Group ◽  
X Ray ◽  
Cell Parameters ◽  
Diffraction Patterns

The X-ray powder diffraction patterns of anilinium trimolybdate tetrahydrate, (C6H5NH3)2Mo3O10·4H2O, and anilinium trimolybdate dihyhydrate, (C6H5NH3)2Mo3O10·2H2O, have been measured in room temperature. The unit cell parameters were refined to a=11.0670(7) Å, b=7.6116(8) Å, c=25.554(3) Å, space group Pnma(62) and a=17.560(2) Å, b=7.5621(6) Å, c=16.284(2) Å, β=108.54(1)°, space group P21(4) or P21/m(11) for orthorhombic anilinium trimolybdate tetrahydrate and monoclinic anilinium trimolybdate dihydrate, respectively.

Preparation and crystal structure of SbV1.50InIII0.50(PO4)3 and (SbV0.50InIII0.50)P2O7

2008 ◽  
Vol 23 (3) ◽  
pp. 232-240
Author(s):  
Abderrahim Aatiq ◽  
Rachid Bakri ◽  
Aaron Richard Sakulich
Keyword(s):  
Crystal Structure ◽  
Solid State ◽  
Room Temperature ◽  
Rietveld Method ◽  
Monoclinic Space Group ◽  
Unit Cell Parameters ◽  
Orthorhombic System ◽  
Space Group ◽  
X Ray ◽  
Cell Parameters

Synthesis and structure of two phosphates belonging to the ternary Sb2O5–In2O3–P2O5 system are realized. Structures of SbV1.50InIII0.50(PO4)3 and (SbV0.50InIII0.50)P2O7 phases, obtained by solid state reaction in air at 950 °C, were determined at room temperature from X-ray powder diffraction using the Rietveld method. SbV1.50InIII0.50(PO4)3 have a monoclinic (space group P21/n) distortion of the Sc2(W O4)3-type framework. Its structure is constituted by corner-shared SbO6 or InO6 octahedra and PO4 tetrahedra. Monoclinic unit cell parameters are a=11.801(2) Å, b=8.623(1) Å, c=8.372(1) Å, and β=90.93(1)°. (Sb0.50In0.50)P2O7 is isotypic with (Sb0.50Fe0.50)P2O7 and crystallizes in orthorhombic system (space group Pna21) with a=7.9389(1) Å, b=16.0664(2) Å, and c=7.9777(1) Å. Its structure is built up from corner-shared SbO6 or InO6 octahedra and P2O7 groups (two group-types). Each P2O7 group shares its six vertices with three SbO6 and three InO6 octahedra, and each octahedron is connected to six P2O7 groups.

scholarly journals Synthesis, Characterization, and Crystal Structure of Negundoside (2′-p-Hydroxybenzoyl Mussaenosidic Acid)

2014 ◽  
Vol 2014 ◽  
pp. 1-6 ◽  
Author(s):  
Suresh Sharma ◽  
B. D. Gupta ◽  
Rajni Kant ◽  
Vivek K. Gupta
Keyword(s):  
Crystal Structure ◽  
Room Temperature ◽  
Direct Method ◽  
Monoclinic Crystal System ◽  
X Ray Diffraction ◽  
Unit Cell Parameters ◽  
Monoclinic Crystal ◽  
Full Matrix ◽  
X Ray ◽  
Cell Parameters

The structure of title compound Negundoside (2′-p-hydroxybenzoyl mussaenosidic acid) was established by spectral and X-ray diffraction studies. The compound crystallizes in the monoclinic crystal system with space group P21 having unit cell parameters: a=11.6201 (5) Å, b=9.2500 (4) Å, c=12.2516 (5) Å, β=97.793 (4)°, and Z=2. The crystal structure was solved by direct method using single crystal X-ray diffraction data collected at room temperature and refined by full-matrix least-squares procedures to a final R value of 0.0520 for 3389 observed reflections.

Crystal-structure analysis of four mineral samples of anhydrite, CaSO4, using synchrotron high-resolution powder X-ray diffraction data

2011 ◽  
Vol 26 (4) ◽  
pp. 326-330 ◽  
Author(s):  
Sytle M. Antao
Keyword(s):  
Crystal Structure ◽  
High Resolution ◽  
Unit Cell Volume ◽  
Crystal Structure Analysis ◽  
Unit Cell ◽  
X Ray Diffraction ◽  
Unit Cell Parameters ◽  
Rietveld Refinements ◽  
X Ray ◽  
Cell Parameters

The crystal structures of four samples of anhydrite, CaSO4, were obtained by Rietveld refinements using synchrotron high-resolution powder X-ray diffraction (HRPXRD) data and space group Amma. As an example, for one sample of anhydrite from Hants County, Nova Scotia, the unit-cell parameters are a = 7.00032(2), b = 6.99234(1), c = 6.24097(1) Å, and V = 305.487(1) Å3 with a > b. The eight-coordinated Ca atom has an average <Ca-O> distance of 2.4667(4) Å. The tetrahedral SO4 group has two independent S-O distances of 1.484(1) to O1 and 1.478(1) Å to O2 and an average <S-O> distance of 1.4810(5) Å. The three independent O-S-O angles [108.99(8) × 1, 110.38(3) × 4, 106.34(9)° × 1; average <O-S-O> [6] = 109.47(2)°] and S-O distances indicate that the geometry of the SO4 group is quite distorted in anhydrite. The four anhydrite samples have structural trends where the a, b, and c unit-cell parameters increase linearly with increasing unit-cell volume, V, and their average <Ca-O> and <S-O> distances are nearly constant. The grand mean <Ca-O> = 2.4660(2) Å, and grand mean <S-O> = 1.4848(3) Å, the latter is longer than 1.480(1) Å in celestite, SrSO4, as expected.

X-ray powder diffraction data of lapatinib ditosylate monohydrate

2009 ◽  
Vol 24 (3) ◽  
pp. 250-253 ◽  
Author(s):  
Peter Varlashkin
Keyword(s):  
Breast Cancer ◽  
Powder Diffraction ◽  
Diffraction Data ◽  
Room Temperature ◽  
Powder Diffraction Data ◽  
X Ray Diffraction ◽  
Unit Cell Parameters ◽  
X Ray ◽  
Cell Parameters ◽  
Diffraction Structure

The room temperature powder pattern of lapatinib ditosylate monohydrate (active ingredient in Tykerb used to treat refractory breast cancer) was indexed and the cell from the single crystal X-ray diffraction structure was refined using the experimental capillary data. Unit-cell parameters for the orthorhombic compound with space group Pbca refined from powder diffraction data are a=9.6850±0.0009 Å, b=29.364±0.003 Å, and c=30.733±0.003 Å, α=β=γ=90°, z=8, V=8740.1 Å3. Values of 2θ, d, I, and Miller indices are reported.

scholarly journals Umbite Type Zirconium Germanates for Cs Removal

MRS Advances ◽  
2017 ◽  
Vol 2 (13) ◽  
pp. 729-734 ◽  
Author(s):  
Ryan George ◽  
Joseph A. Hriljac
Keyword(s):  
Rietveld Analysis ◽  
Parent Material ◽  
High Yield ◽  
Synthesis Methods ◽  
X Ray Diffraction ◽  
Unit Cell Parameters ◽  
Natural Mineral ◽  
X Ray ◽  
Cell Parameters ◽  
Defect Sites

ABSTRACTPure and Nb-doped zirconium germanate materials of composition K2-xZr1-xNbxGe3O9.H2O where x = 0, 0.1, 0.2 and 0.3 with the structure of the natural mineral umbite have been prepared in high yield using hydrothermal synthesis methods. The parent material displays virtually no ion exchange of the K+ for Cs+ but the doped materials show rapidly enhanced exchange with replacement of ca. 70% of the K+ by Cs+ for the 30% doped material. Rietveld analysis of the powder X-ray diffraction data is consistent with no change in the unit cell parameters or K+ bonding prior to the exchange, hence we propose the improved property is due to the creation of cation defect sites within the pores of the material that facilities greater cation mobility and leads to exchange.