EFFECT OF THERMOMECHANICAL TREATMENT ON TOUGHENING OF Al-Li-Cu-Mg-Zr ALLOY AND ITS TOUGHNESS

4340 Ni-Cr-Mo alloy steel is widely used due to its good combination of strength and toughness. The mechanical property of 4340 steel can be improved by various thermal treatments. The influence of thermomechanical treatment (TMT) has been studied in a low carbon Ni-Cr-Mo steel having chemical composition closed to 4340 steel. TMT of 4340 steel is rarely examined up to now. In this study we obtain good improvement on the mechanical property of 4340 steel by TMT. The mechanism is explained in terms of TEM microstructures4340 (0.39C-1.81Ni-0.93Cr-0.26Mo) steel was austenitized at 950°C for 30 minutes. The TMTed specimen (T) was obtained by forging the specimen continuously as the temperature of the specimen was decreasing from 950°C to 600°C followed by oil quenching to room temperature. The thickness reduction ratio by forging is 40%. The conventional specimen (C) was obtained by quenching the specimen directly into room temperature oil after austenitized at 950°C for 30 minutes. All quenched specimens (T and C) were then tempered at 450, 500, 550, 600 or 650°C for four hours respectively.

Download Full-text

Microtwinning Evidence For The Apparent Five-Fold Symmetry in T2(Al6Li3Cu)

Proceedings, annual meeting, Electron Microscopy Society of America ◽

10.1017/s0424820100125178 ◽

1987 ◽

Vol 45 ◽

pp. 24-25

Author(s):

Kenneth S. Vecchio ◽

David B. Williams

Keyword(s):

Stable Equilibrium ◽

Equilibrium Phase ◽

Convergent Beam Electron Diffraction ◽

Icosahedral Structure ◽

Cubic Crystals ◽

Icosahedral Phases ◽

Heat Treated ◽

Zero Layer ◽

Convergent Beam ◽

Zr Alloy

Since the discovery in 1984 by Shechtman et al. of crystals which display apparent five-fold symmetry, extensive effort has been given to establishing a theoretical basis for the existence of icosahedral phases (eg.2.). Several other investigations have been centered on explaining these observations based on twinning of cubic crystals (eg.3.). Recently, the existence of a stable, equilibrium phase T2Al6 Li3Cu) possessing an icosahedral structure has been reported in the Al-Li-Cu system(4-6).In the present study an Al-2.6wt.%Li-l.5wt.%Cu-0.lwt.%Zr alloy was heat treated at 300°C for 100hrs. to produce large T2 precipitates. Convergent Beam Electron Diffraction (CBED) patterns were obtained from two-fold, three-fold, and apparent five-fold axes of T2 particles. Figure 1 shows the five-fold symmetric zero layer CBED pattern obtained from T2 particles.

Download Full-text

Deformation and fracture behavior of an Al-Li-Cu-Mg-Zr alloy 8090

Proceedings, annual meeting, Electron Microscopy Society of America ◽

10.1017/s0424820100178008 ◽

1990 ◽

Vol 48 (4) ◽

pp. 974-975

Author(s):

D.M. Jiang ◽

B.D. Hong

Keyword(s):

High Strength ◽

Deformation And Fracture ◽

Fracture Behaviors ◽

Aluminum Lithium ◽

Carbon Fiber Reinforced Composites ◽

Peak Aged ◽

Aluminum Lithium Alloys ◽

High Strength Aluminum Alloys ◽

Lithium Alloys ◽

Zr Alloy

Aluminum-lithium alloys have been recently got strong interests especially in the aircraft industry. Compared to conventional high strength aluminum alloys of the 2000 or 7000 series it is anticipated that these alloys offer a 10% increase in the stiffness and a 10% decrease in density, thus making them rather competitive to new up-coming non-metallic materials like carbon fiber reinforced composites.The object of the present paper is to evaluate the inluence of various microstructural features on the monotonic and cyclic deformation and fracture behaviors of Al-Li based alloy. The material used was 8090 alloy. After solution treated and waster quenched, the alloy was underaged (190°Clh), peak-aged (190°C24h) and overaged (150°C4h+230°C16h). The alloy in different aging condition was tensile and fatigue tested, the resultant fractures were observed in SEM. The deformation behavior was studied in TEM.

Download Full-text