Effect of Phosphate Ester Addition on Transverse Strength and Hardness of Heat Cured Acrylic Denture Base Material

2018 ◽  
Vol 30 (2) ◽  
pp. 5-9
Author(s):  
Zahraa Saad Abed Karkosh ◽  
Basima M. A. Hussien
Keyword(s):  
Base Material ◽  
Phosphate Ester ◽  
Denture Base ◽  
Transverse Strength

Effect of phosphate ester addition on transverse strength and hardness of heat cured acrylic denture base material

2018 ◽  
Vol 30 (2) ◽  
pp. 5-9
Author(s):  
Zahraa S. Abed karkosh ◽  
Basima M.A. Hussien
Keyword(s):  
Polymethyl Methacrylate ◽  
Testing Machine ◽  
Base Material ◽  
Hardness Test ◽  
Acrylic Resin ◽  
Control Group ◽  
Phosphate Ester ◽  
Denture Base ◽  
Hardness Tester ◽  
Transverse Strength

Background: acrylic resin denture base consider a common denture base material for its acceptable cost, aesthetic and easy processing but still has disadvantages including easy of fracture and low impact strength. Material and method: The experimental group was prepared by addition of 15% phosphoric acid 2-hydroxyethyl methacrylate ester (PA2HEME) with polymethyl methacrylate monomer; the experimental groups was compared with the control one. The specimens were prepared according to ADA specification No. 12 with dimension 65 mm x 10 mm x2.5 mm (length x width x thickness respectively). The prepared specimens were tested by three-point flexural strength utilizing Instron Universal Testing Machine (WDW, Layree Technology Co.), Shore D hardness tester used to measure hardness test. Statistical analysis used student T- test, mean and standard deviation. Results: The result of PA2HEME group showed high significant reduction comparing to the control group for both transverse strength and hardness test. Conclusion: Mixing 15% of PA2HEME with 85% methyl methacrylate (MMA) can reduce the mechanical properties of new modified polymethyl methacrylate (PMMA) acrylic resin.

Effect of 180 Days of Water Storage on the Transverse Strength of Acetal Resin Denture Base Material

2010 ◽  
Vol 19 (1) ◽  
pp. 47-51 ◽  
Author(s):  
Ayla Arıkan ◽  
Yasemin Kulak Ozkan ◽  
Tugberk Arda ◽  
Buket Akalın
Keyword(s):  
Water Storage ◽  
Base Material ◽  
Denture Base ◽  
Transverse Strength

scholarly journals The effect of polyamide microparticles addition on some mechanical prop-erties of light-cured acrylic resin

2019 ◽  
Vol 10 (2) ◽  
pp. 1464-1469
Author(s):  
Adnan R. Al Assal ◽  
Abdalbaset A Fatalla ◽  
Mohammed Moudhaffar ◽  
Ghasak H Jani
Keyword(s):  
Tensile Strength ◽  
Impact Strength ◽  
Base Material ◽  
Acrylic Resin ◽  
Strength Test ◽  
Control Group ◽  
Denture Base ◽  
Mean Values ◽  
Transverse Strength ◽  
Transverse Tensile

The general upgrading of polymer denture base material and research continuously looking for ideal restorative dental material with better properties, adequate esthetic properties, less expensive and easier to handle material to develop photo polymerization dental materials. This study was conducted to evaluate the effect of addition polyamide on mechanical microparticle properties light cure denture base material. One hindered sixty specimens from light-cured acrylic resin (Aurora). The divided mainly into four groups according to test used (Transverse strength test, impact strength test, hardness test and tensile strength test) with 40 specimens for each group. The results show an increase in Transverse strength, impact strength, hardness and tensile strength in all experimental group when compared to control group the highest mean values for all tests included in the study appeared in group B 1% polyamide. The addition of polyamide microparticle improves transverse, tensile, impact strength and hardness properties of denture base material.

scholarly journals The transversal strength comparison between polyethylene and glass fiber as an acrylic resin denture plate repair material

2019 ◽  
Vol 1 (1) ◽  
pp. 35
Author(s):  
Pramudya Aditama ◽  
Erwan Sugiatno ◽  
Sabdayana Sabdayana
Keyword(s):  
Glass Fiber ◽  
Glass Fibers ◽  
Testing Machine ◽  
Base Material ◽  
Acrylic Resin ◽  
Repair Material ◽  
Denture Base ◽  
Transverse Strength ◽  
Group I ◽  
Denture Plate

Acrylic resin is the most commonly used denture base material. However, it has a shortage of being easily broken. One way to resolve this problem is by adding polyethylene (PE) or glass fibers. The purpose of this research is to compare the transversal strength of PE and glass fibers from denture plate acrylic resin repair material. The experiment involved 32 plates of heat cure acrylic with the dimensions of 65 mm x 10 mm x 2.5 mm. The speciments were prepared to create a 3 mm gap and 45° bevel. Subjects were divided into 2 groups, each group containing 16 plates. Group I was reinforced with PE fiber and Group II was reinforced with glass fiber. All plates were soaked in distillation water for one day at 37 °C. Plates were tested for transverse strength with universal testing machine and all data were analyzed with independent t-tes at 95% confidence level. Macro photo analysis was used to observed the bond failure on fiber and resin. The mean of transverse strength (MPa) denture plate acrylic resin repair material reinforced with PE fiber was (67.38 ± 4.31) MPa, while glass fiber was (93.61 ± 6.14) MPa. Independent t-tes showed that type of fiber had a significant effect (p<0.05). Thus, it is possible to conclude that addition of glass fibers in denture plate acrylic resin repair material increased the transverse strength and made it stronger than those added with PE fibers.

PENGARUH MINUMAN TEH HITAM TERHADAP KEKUATAN TRANSVERSAL RESIN AKRILIK POLIMERISASI PANAS

2015 ◽  
Vol 3 (2) ◽  
pp. 68-73
Author(s):  
Riezka Hanafiah Putri ◽  
Zulkarnain Agus ◽  
Eni Rahmi
Keyword(s):  
Immersion Time ◽  
Testing Machine ◽  
Base Material ◽  
Acrylic Resin ◽  
Black Tea ◽  
Bending Test ◽  
Control Group ◽  
Denture Base ◽  
Transverse Strength ◽  
Acrylic Resins

Heat-polymerized  acrylic  resins  is  the  most  used  denture  base  material  in  prosthodontics.  One  of  mechanical properties of acrylic resins is transverse strength. It represents the masticatory pressure that is applied to denture base. Black tea is the second largest consumed beverage in the world. The aim of this study was to investigate the effect of black tea beverage on transverse strength of heat-polymerized acrylic resins. A total of 24 heat-polymerized acrylic resin plates (65×10×2,5 mm) were immersed in black tea beverage for 1, 4, and 20 days as treatment group and in aquadest for 1, 4, and 20 days as control group. The transverse strength of  acrylic samples were measured by three–point bending test by universal testing machine. Data were statistically analyzed using Independent t test. The transverse strength values of acrylic resin immersed in black tea beverage had no significant differences to the transverse strength values of acrylic resin immersed in aquadest with similar immersion time (p>0,05). There was no effect of black tea beverage on transverse strength of heat-polymerized acrylic resins. Immersion time decrease the transverse strength of heat-polymerized acrylic resins due to water sorption. Keywords: Heat-polymerized acrylic resins, black tea, transverse strength

Impact of phosphate ester addition on the cytotoxicity of heat cured denture base material

2021 ◽  
Vol 42 ◽  
pp. 2025-2030
Author(s):  
Basima Mohammed Ali Hussein ◽  
Zahraa S. Abed Karkosh ◽  
Ihab Nabeel Safi ◽  
Alyaa Saad KarKosh
Keyword(s):  
Base Material ◽  
Phosphate Ester ◽  
Denture Base

scholarly journals A comparison between the effect of LASER and WATER BATH on heat-cured acrylic denture base material vitro study

2020 ◽  
Vol 11 (4) ◽  
pp. 7370-7375
Author(s):  
Mithaq R Mohammed ◽  
Aedah Z Alkaisy
Keyword(s):  
Diode Laser ◽  
Laser Light ◽  
Base Material ◽  
T Test ◽  
Water Bath ◽  
Vitro Study ◽  
Denture Base ◽  
Transverse Strength ◽  
Heat Curing

Curing stage by utilizing Water Bath (W.B.) one of the stages of making a denture, in this investigation, we assess the influence of utilizing W.B. and diode laser light of frequency (1064nm) with force 50mW on samples of heat-curing acrylic (PMMA) on transverse strength of this material. We utilized a sample with dimension (8x 0.8x0.3) cm. 40 samples utilized in this investigation, 20 illuminated by laser with deferent span time of light, and the staying 20 samples prepared by regular W.B. procedure. We estimated the samples' dimension when prepared by the two procedures. From a correlation on the influence of these two procedures on the quality of the samples by utilizing t-test, we reason that the samples that illuminated with laser become more quality and when we increment the term time (p>1), while there are no concedes between the samples that rewarded with ordinary W.B. (p>0.05). We presumed that utilizing laser be more accomplishment in improving the quality of heat-curing acrylic material that utilized for denture base.

Sign in / Sign up

Export Citation Format

Share Document