In order to improve the corrosion resistance of shock absorber for ships, the alumina ceramic coatings are carried out on the surface of aluminum alloy shock absorber by micro arc oxidation (MAO) technology. The microstructure and anti-corrosion performance of the MAO coatings were investigated experimentally. This paper mainly focuses on the experimental work to determine the effect of current density on the structural characteristics and corrosion resistance of MAO coatings. The results show that the current density has a significant influence on the preparation of MAO coating during the process. The surface of the coating becomes more compact and smooth with the cathode voltage of 7 A.dm-2. Furthermore, the anti-corrosion performance of the MAO coatings can effectively be improved at the current density of 7 A.dm-2.


CORROSION ◽  
2012 ◽  
Vol 68 (4) ◽  
pp. 045003-1-045003-10 ◽  
Author(s):  
M. Akhoondan ◽  
A.A. Sagüés

The extent of the oxygen reduction reaction in concrete was evaluated for ~9% Cr rebar approaching the ASTM A1035 specification and compared to that of conventional carbon steel rebar, at ages of up to ~1 year. Cathodic strength was measured by the cathodic current density developed at −0.35 V vs. copper/copper sulfate (Cu/CuSO4 [CSE]) and −0.40 VCSE in cyclic cathodic potentiodynamic polarization tests, both in the as-received condition with mill scale and with scale removed by glass bead surface blasting. In both conditions the ~9% Cr alloy was a substantially weaker cathode, by a factor of several fold, than carbon steel. Within each material, the surface-blasted condition yielded also much lower cathodic current density than the as-received condition. For a small anode-large cathode system with a given anode polarization function, and no important oxygen reduction concentration polarization, the corrosion current was projected to be significantly lower if the cathodic region were ~9% Cr instead of plain steel rebar with comparable surface condition. There was strong correlation between the charge storage capability of the interface and the extent of cathodic reaction of oxygen. The result cannot be ascribed solely to differences in effective surface area between the different materials and conditions.


2015 ◽  
Vol 180 ◽  
pp. 313-330 ◽  
Author(s):  
Geraint Williams ◽  
Nick Birbilis ◽  
H. Neil McMurray

The early stages of localised corrosion affecting magnesium (Mg) surfaces when immersed in aqueous sodium chloride (NaCl) solutions involves the propagation of dark regions, within which both anodic metal dissolution and cathodic hydrogen evolution occur. For nominally “pure” Mg, these dark areas can either take the form of discs which expand radially with time, or filiform-like tracks which lengthen with time. For Mg surfaces which display disc-form corrosion features in concentrated NaCl electrolyte, a transition to filiform corrosion (FFC) is observed as the concentration is decreased, indicating ohmic constraints on radial propagation. A similar effect is observed when Mg specimens of different iron impurity are immersed in a fixed, high concentration NaCl solution, where disc-form corrosion is observed on samples having ≥280 ppm Fe, but FFC predominates at ≤80 ppm Fe. An in situ scanning vibrating electrode technique (SVET) is used to determine current density distributions within the propagating corrosion features. Cathodic current density values of between −100 and −150 A m−2 measured in central areas of disc-like features are sufficient to sustain the radial growth of a local anode at the perimeter of the discs. However, for high purity Mg specimens (≤80 ppm Fe), cathodic current densities of −10 A m−2 or less are measured over FFC affected regions, indicating that linear propagation arises when there is insufficient cathodic current produced on the corroded surface to sustain radial growth. The results are consistent with surface control of localised corrosion propagation in concentrated electrolyte, but ohmic control in dilute, lower conductivity NaCl solution.


2006 ◽  
Vol 15-17 ◽  
pp. 816-821 ◽  
Author(s):  
Geert Mertens ◽  
Lode Duprez ◽  
Bruno C. De Cooman ◽  
Marc Verhaege

The presence of hydrogen in steel decreases its toughness and formability leading to hydrogen embrittlement. To understand the failure mechanisms of steel due to the presence of hydrogen, a profound insight in the hydrogen household of the steel is needed. This includes a study of the solubility, the diffusion and the trapping of hydrogen. Next, the absorption and desorption behavior during and after electrolytic charging must be well determined. This was investigated in this research for steels with various types of traps, e.g. dislocations, microcracks, grain boundaries and precipitates such as TiC and Ti4C2S2. The samples were cathodically charged at three different current densities: 0.8mA/cm2; 8.3mA/cm2 and 62.5mA/cm2. It was noticed that the cathodic current density used for hydrogen loading had a great influence on the results. Observation of the samples by scanning electron microscopy (SEM) showed that at the highest current density major damage of the surface had occurred. Hence it was decided to study more systematically the influence of charging current density on the resulting surface aspect and on hydrogen absorption and desorption. The hydrogen charging kinetics, maximum hydrogen solubility and hydrogen desorption behavior have also been evaluated for the different current densities during charging.