An Overview of Cu Wire Intermetallic Compound Formation and a Corrosion Failure Mechanism

2012 ◽  
Author(s):  
Dongmei Meng ◽  
Laura Buck ◽  
James Cargo
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Corrosion Mechanism ◽  
Fundamental Study ◽  
Corrosion Failure ◽  
Transmission Electron ◽  
Intermetallic Compound Formation ◽  
Scanning Transmission ◽  
Low K

Abstract Cu needs a higher level of ultrasound combined with bonding force to be bonded to the Al pad properly, not just because Cu is harder than Au, but it is also harder to initiate intermetallic compounds (IMC) formation during bonding. This increases the chances of damaging the metal/low k stack under the bondpad. This paper presents a fundamental study of IMC as well as one example of a failure mode of Cu/Al bonded devices, all based on detailed analysis using scanning electron microscopy, scanning transmission electron microscopy, energy dispersive spectrometers, and transmission electron microscopy. It presents a case study showing a corrosion mechanism of Cu/Al ballbond after 168hr UHAST stress. It is observed that all Cu9Al4 was consumed, while very little copper aluminide remained after 168 hours of UHAST stressing.

High-Voltage Scanning Electron Microscopy

1970 ◽  
Vol 28 ◽  
pp. 6-7
Author(s):  
J. M. Cowley
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Scanning Transmission Electron Microscopy ◽  
Wave Optics ◽  
Contrast Effects ◽  
Transmission Electron ◽  
Mode Of Operation ◽  
Scanning Transmission ◽  
Types Of Information ◽  
Voltage Scanning

The comparison of scanning transmission electron microscopy (STEM) with conventional transmission electron microscopy (CTEM) can best be made by means of the Reciprocity Theorem of wave optics. In Fig. 1 the intensity measured at a point A’ in the CTEM image due to emission from a point B’ in the electron source is equated to the intensity at a point of the detector, B, due to emission from a point A In the source In the STEM. On this basis it can be demonstrated that contrast effects In the two types of instrument will be similar. The reciprocity relationship can be carried further to include the Instrument design and experimental procedures required to obtain particular types of information. For any. mode of operation providing particular information with one type of microscope, the analagous type of operation giving the same information can be postulated for the other type of microscope. Then the choice between the two types of instrument depends on the practical convenience for obtaining the required Information.

Magnesium and sulfur in mast cell and basophil granules of lower vertebrates in relation with histamine

1992 ◽  
Vol 50 (2) ◽  
pp. 1596-1597
Author(s):  
Kenichi Takaya
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Mast Cell ◽  
Mast Cells ◽  
Tree Frog ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Transmission ◽  
Fresh Frozen ◽  
Ultrathin Sections

Mast cell and basophil granules of the vertebrate contain heparin or related sulfated proteoglycans. Histamine is also present in mammalian mast cells and basophils. However, no histamine is detected in mast cell granules of the amphibian or fish, while it is shown in those of reptiles and birds A quantitative x-ray microanalysis of mast cell granules of fresh frozen dried ultrathin sections of the tongue of Wistar rats and tree frogs disclosed high concentrations of sulfur in rat mast cell granules and those of sulfur and magnesium in the tree frog granules. Their concentrations in tree frog mast cell granules were closely correlated (r=0.94).Fresh frozen dried ultrathin sections and fresh air-dried prints of the tree frog tongue and spleen and young red-eared turtle (ca. 6 g) spleen and heart blood were examined by a quantitative energy-dispersive x-ray microanalysis (X-650, Kevex-7000) for the element constituents of the granules of mast cells and basophils. The specimens were observed by transmission electron microscopy (TEM) (80-200 kV) and followed by scanning transmission electron microscopy (STEM) under an analytical electron microscope (X-650) at an acceleration voltage of 40 kV and a specimen current of 0.2 nA. A spot analysis was performed in a STEM mode for 100 s at a specimen current of 2 nA on the mast cell and basophil granules and other areas of the cells. Histamine was examined by the o-phthalaldehyde method.

Scanning Transmission Electron Microscopy of Polyethylene Crystals

1980 ◽  
Vol 38 ◽  
pp. 242-245
Author(s):  
F. Khoury ◽  
L. H. Bolz
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Crystallization Temperature ◽  
Scanning Transmission Electron Microscopy ◽  
Growth Habit ◽  
Lateral Growth ◽  
Scanning Transmission Electron ◽  
Transmission Electron ◽  
Scanning Transmission ◽  
Growth Habits

The lateral growth habits and non-planar conformations of polyethylene crystals grown from dilute solutions (<0.1% wt./vol.) are known to vary depending on the crystallization temperature.1-3 With the notable exception of a study by Keith2, most previous studies have been limited to crystals grown at <95°C. The trend in the change of the lateral growth habit of the crystals with increasing crystallization temperature (other factors remaining equal, i.e. polymer mol. wt. and concentration, solvent) is illustrated in Fig.l. The lateral growth faces in the lozenge shaped type of crystal (Fig.la) which is formed at lower temperatures are {110}. Crystals formed at higher temperatures exhibit 'truncated' profiles (Figs. lb,c) and are bound laterally by (110) and (200} growth faces. In addition, the shape of the latter crystals is all the more truncated (Fig.lc), and hence all the more elongated parallel to the b-axis, the higher the crystallization temperature.

scholarly journals Revisiting the Bøggild Intergrowth in Iridescent Labradorite Feldspars: Ordering, Kinetics, and Phase Equilibria

Minerals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 727
Author(s):  
Shiyun Jin ◽  
Huifang Xu ◽  
Seungyeol Lee
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Atom Probe ◽  
Phase Region ◽  
Two Phase ◽  
Subsolidus Phase ◽  
Plagioclase Feldspar ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Transmission

The enigmatic Bøggild intergrowth in iridescent labradorite crystals was revisited in light of recent work on the incommensurately modulated structures in the intermediated plagioclase. Five igneous samples and one metamorphic labradorite sample with various compositions and lamellar thicknesses were studied in this paper. The lamellar textures were characterized with conventional transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM). The compositions of individual lamellae were analyzed with high-resolution energy-dispersive X-ray spectroscopy (EDS) mapping and atom probe tomography (APT). The average structure states of the studied samples were also compared with single-crystal X-ray diffraction data (SC-XRD). The Na-rich lamellae have a composition of An44–48, and the Ca-rich lamellae range from An56 to An63. Significant differences between the lamellar compositions of different samples were observed. The compositions of the Bøggild intergrowth do not only depend on the bulk compositions, but also on the thermal history of the host rock. The implications on the subsolidus phase relationships of the plagioclase feldspar solid solution are discussed. The results cannot be explained by a regular symmetrical solvus such as the Bøggild gap, but they support an inclined two-phase region that closes at low temperature.

Intergrowth of niobium tungsten oxides of the tetragonal tungsten bronze type

2020 ◽  
Vol 75 (11) ◽  
pp. 913-919
Author(s):  
Frank Krumeich
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Tungsten Bronze ◽  
Structural Complexity ◽  
Dark Field ◽  
Tetragonal Tungsten Bronze ◽  
Tungsten Oxides ◽  
Transmission Electron ◽  
Scanning Transmission

AbstractSince the 1970s, high-resolution transmission electron microscopy (HRTEM) is well established as the most appropriate method to explore the structural complexity of niobium tungsten oxides. Today, scanning transmission electron microscopy (STEM) represents an important alternative for performing the structural characterization of such oxides. STEM images recorded with a high-angle annular dark field (HAADF) detector provide not only information about the cation positions but also about the distribution of niobium and tungsten as the intensity is directly correlated to the local scattering potential. The applicability of this method is demonstrated here for the characterization of the real structure of Nb7W10O47.5. This sample contains well-ordered domains of Nb8W9O47 and Nb4W7O31 besides little ordered areas according to HRTEM results. Structural models for Nb4W7O31 and twinning occurring in this phase have been derived from the interpretation of HAADF-STEM images. A remarkable grain boundary between well-ordered domains of Nb4W7O31 and Nb8W9O47 has been found that contains one-dimensionally periodic features. Furthermore, short-range order observed in less ordered areas could be attributed to an intimate intergrowth of small sections of different tetragonal tungsten bronze (TTB) based structures.

Sign in / Sign up

Export Citation Format

Share Document