Influence of Low-Level Laser Modification and Adhesive Application Mode on the Bonding Efficiency of Universal Adhesives to Er:YAG Laser-Ablated Dentin

Introduction: Erbium laser ablation as a method of tooth preparation and conditioning has shown promising results. Although previous studies have adopted various combinations of different laser parameters and several dentin adhesive systems, very few have investigated combining high-level and low-level ER:YAG lasers with Universal adhesives. This study aimed to assess the impact of using low-energy irradiation on the surface micro-topography and shear bond strength (SBS) of universal adhesive (UA) to the erbium:yttrium-aluminum-garnet (Er:YAG) laser-ablated dentin substrate, bonded in etch-and-rinse or self-etch adhesive mode. Methods: Eighty-seven extracted molars were sectioned to expose flat occlusal dentin surface; 60 teeth were divided equally into three groups according to the surface treatment; bur-cutting (B), Er:YAG high-energy laser cutting (L1 - 200 mJ, 20 Hz, 50 μs pulse), or L1 followed by low-energy laser modification (L1 /L2 - 80 mJ, 10 Hz, 50 μs pulse). Then each group was equally divided into two groups (n=10) according to the mode of application of the universal adhesive; either etch-and-rinse (ER) or self-etching (SE). The samples were subjected to thermocycling (5000 cycle between 5°C and 55°C), and SBS was tested. Two-way ANOVA and Tukey post hoc test were used to analyze the results. The remaining 27 samples were used to investigate the effect of the treatment on the topography of the treated dentin surfaces using a scanning electron microscope (SEM). Results: B/SE recorded the highest SBS (25.48 ± 2.6 MPa) followed by B/ER (23.20 ± 6.8 MPa) and L1 /L2 /SE (22.94 ± 4.1 MPa) and with no statistically significant difference between these groups (P >0.05). The lowest SBS results (P<0.05) were recorded for L1/SE (12.22 ± 3 MPa). No statistical differences were found between the SBS of L1 /L2 /ER and L1 /ER groups or between the SBS of L1 /L2 / ER and L1 /L2 /SE groups. Conclusion: A subsequent treatment of the Er:YAG laser-ablated dentin with low-energy laser modification mode (LMM) enhances the SBS of the tested UA when applied in SE mode.

Download Full-text

Does Erbium:Yttrium–Aluminum–Garnet Laser to Enamel improve the Performance of Etch-and-rinse and Universal Adhesives?

The Journal of Contemporary Dental Practice ◽

10.5005/jp-journals-10024-2252 ◽

2018 ◽

Vol 19 (3) ◽

pp. 278-282 ◽

Cited By ~ 1

Author(s):

Rudys Rodolfo de Jesus Tavarez ◽

Carlos RG Torres ◽

Leily M Firoozmand ◽

Lorrany LC Rodrigues ◽

Ana C Diniz ◽

...

Keyword(s):

Yttrium Aluminum Garnet ◽

Er:Yag Laser ◽

Artificial Saliva ◽

Adhesive Systems ◽

Universal Adhesive ◽

Etch And Rinse ◽

Yttrium Aluminum ◽

Universal Adhesives ◽

Microshear Bond Strength ◽

Previous Irradiation

ABSTRACT Aim This study aims to evaluate the effect of erbium: Yttrium–aluminum–garnet (Er:YAG) laser irradiation on the enamel microshear bond strength (µSBS), followed by the utilization of etch-and-rinse and universal adhesive systems. Materials and methods A total of 32 molars were sectioned in the mesiodistal direction producing 64 samples that were randomized into two groups (n = 32): single bond 2 (SB2) (etch-and-rinse system; 3M), SB universal (SBU) (universal etching system; The SB2 and SBU groups were then divided into two subgroups (n = 16): (i) enamel was irradiated with an Er:YAG laser (λ = 2.94 μm, 60 mJ, 10 Hz), and (ii) enamel served as a control. The samples were restored with TPH3 (Dentsply), stored in artificial saliva for 24 hours, and subjected to a microshear test. Results Kruskal–Wallis (p < 0.05) and Mann–Whitney U tests indicated no significant differences in μSBS between the groups, and the fractures were predominately at the resin–enamel interface. Conclusion The previous irradiation of enamel with Er:YAG laser does not interfere with the performance of simplified two-step etch-and-rinse and universal adhesive systems. Clinical significance The increasing use of Er:YAG laser is important to evaluate the influence of this irradiation on the adhesion of restorative materials. Thus, to obtain the longevity of the restorative procedures, it is necessary to know the result of the association of the present adhesive systems to the irradiated substrate. How to cite this article De Jesus Tavarez RR, Rodrigues LLC, Diniz AC, Lage LM, Torres CRG, Bandeca MC, Firoozmand LM. Does Erbium:Yttrium–Aluminum–Garnet Laser to Enamel improve the Performance of Etch-and-rinse and Universal Adhesives? J Contemp Dent Pract 2018;19(3):278-282.