High Speed Roll Casting of Aluminum Alloy Strip

2005 ◽  
Vol 475-479 ◽  
pp. 343-348 ◽  
Author(s):  
Ryoji Nakamura ◽  
Hisaki Watari ◽  
Shinji Kumai
Keyword(s):  
Mechanical Properties ◽  
High Speed ◽  
The Other ◽  
Alloy Strip ◽  
Cast Ingot ◽  
Cast Strip ◽  
Cooling Slope ◽  
Roll Casting ◽  
Twin Roll Caster ◽  
Twin Roll

Two kinds of roll casters, which were suitable for high speed roll casting, were devised. One was a vertical type twin roll caster, and the other was an unequal diameter twin roll caster. The semisolid roll casting using a cooling slope was adopted to these roll casters. The solid fraction was smaller than 5%. 3 mm thickness of 6111 strip was cast at 60 m/min by the vertical type twin roll caster, and 5 mm thickness of 6111 strip was cast at 30 m/min by the unequal diameter twin roll caster. The microstructure of the as-cast strip was equiaxed and spherical, not columnar. The mechanical properties of the strip rolled from roll-cast strip were almost as same as that of the strip made from cast ingot.

Roll Casting of Al-SiCp Composite Strip

2010 ◽  
Vol 139-141 ◽  
pp. 481-484
Author(s):  
Ryoji Nakamura ◽  
Teppei Nakamura ◽  
Ryoji Nakamura ◽  
Hideto Harada ◽  
Shinji Kumai ◽  
...  
Keyword(s):  
Cold Rolling ◽  
High Speed ◽  
Alloy Strip ◽  
Thickness Direction ◽  
Composite Alloy ◽  
Cast Strip ◽  
Roll Casting ◽  
Twin Roll Caster ◽  
Twin Roll ◽  
Steel Rolls

Roll casting of Al-SiCp composite alloy strip was tried using a vertical type high speed twin roll caster equipped with mild steel rolls. The Al-20vol% SiCp and Al-30vol%SiCp alloy could be roll-cast to the strip. The casting speed was 30m/min. The thickness of as-cast strip was thinner than 2.5mm. The SiCp powder was dispersed uniformly at the thickness direction. The as-cast strip could be thin down to 1mm by the hot rolling and the cold rolling without broken.

scholarly journals High Speed Roll Caster for Aluminum Alloy

Metals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 520
Author(s):  
Toshio Haga
Keyword(s):  
Thermal Conductivity ◽  
Aluminum Alloy ◽  
Copper Alloy ◽  
High Speed ◽  
The Other ◽  
Center Line ◽  
Cast Strip ◽  
Roll Casting ◽  
Twin Roll Caster ◽  
Twin Roll

Two types of high-speed twin-roll casters and a single-roll caster equipped with a scraper were proposed. One of the twin-roll casters is a vertical-type high-speed twin-roll caster, and the other twin-roll caster is an unequal-diameter twin-roll caster. The vertical-type high-speed twin-roll caster can cast strip at speeds of up to 120 m/min. The unequal-diameter twin-roll caster casts strip at speeds up to 60 m/min. The unequal-diameter twin-roll caster is superior to the vertical-type high-speed twin-roll caster at the point of conveyance of the cast strip. A single-roll caster equipped with a scraper can cast strip without center-line segregation at speeds of up to 40 m/min. The use of a copper alloy roll and the non-use of a parting material enable high-speed roll casting. Since the roll loads of these casters are smaller than 0.1 kN/mm, soft copper alloy roll can be used. The strip does not stick to the roll without the parting material because of the use of the copper alloy roll with high thermal conductivity and the small roll load. The cooling rate near the surface is higher than 2000 °C/s.

6000 Series Aluminium Alloy Strip Casting Using a Vertical Type Twin Roll Caster

2016 ◽  
Vol 877 ◽  
pp. 45-50
Author(s):  
He Chen ◽  
Yong Li ◽  
Jia Dong Li ◽  
Guang Jun Gao ◽  
Zhao Dong Wang
Keyword(s):  
Mechanical Properties ◽  
Aluminium Alloy ◽  
Casting Speed ◽  
Strip Casting ◽  
Alloy Strip ◽  
Cast Ingot ◽  
Cast Strip ◽  
Cast Aluminium ◽  
Twin Roll Caster ◽  
Twin Roll

A vertical type twin roll caster with two side dams was used to cast aluminium alloy strip with a thickness of about 5mm at speed higher than 10m/min. The characteristics of the twin roll caster with two side dams are as follows: The diameter of the copper roll is 500mm, the width of the copper roll is 110mm and the thickness of the copper roll sleeve is 25mm.The maximum casting speed is up to 60m/min. Using the vertical type twin roll caster, a 4.5mm thickness of 6111 strip could be cast at a speed of 30m/min. The microstructure of the as-cast strip was equiaxed and spherical, not columnar. The mechanical properties of the strip casted from the vertical type twin roll caster were almost as same as that of the strip made from the conventional cast ingot.

Inline Rolling of 5182 Aluminum Alloy Strip Cast by a Vertical Type High Speed Twin Roll Caster

2010 ◽  
Vol 139-141 ◽  
pp. 477-480
Author(s):  
Ryoji Nakamura ◽  
Shuya Hanada ◽  
Shinji Kumai ◽  
Hisaki Watari
Keyword(s):  
Aluminum Alloy ◽  
High Speed ◽  
Rolling Speed ◽  
Center Line ◽  
Alloy Strip ◽  
Ripple Mark ◽  
Roll Casting ◽  
Strip Cast ◽  
Twin Roll Caster ◽  
Twin Roll

An inline hot rolling was operated on 5182 aluminum alloy strip cast using a vertical type high speed caster (VHSTRC) at the speed of 60 m/min. A porosity existing at center line of the thickness and a ripple mark on the surface, these are typical defects of the strip cast by the VHSTRC, could be improved by the inline rolling. The rolling speed was as same as the roll-casting-speed of 60m/min. The temperature of the strip, when the inline rolling was operated, was 450oC. The reduction of the strip of the inline rolling was 35%.

Roll Casting of Al-SiCp Strip

2011 ◽  
Vol 675-677 ◽  
pp. 811-814 ◽  
Author(s):  
Toshio Haga ◽  
Teppei Nakamura ◽  
S. Kumai ◽  
H. Watari
Keyword(s):  
Hot Rolling ◽  
High Speed ◽  
Strip Casting ◽  
Cast Strip ◽  
Fine Grain ◽  
Roll Casting ◽  
Speed Up ◽  
Cold Rolled ◽  
Twin Roll Caster ◽  
Twin Roll

The strip casting of Al-SiCp alloy was operated by a high speed twin roll caster. The content of SiCp was 20Vol% and 30Vol%. Both of Al-20Vol%SiCp and Al-30Vol%SiCp strips could be cast continuously at the speed up to 90m/min. The SiCp particle distributed uniformly. This was the effect of fine grain of the strip. The as-cast strip of Al-20Vol%SiCp could be cold rolled after homogenization. The as-cast strip of Al-30Vol%SiCp could be cold rolled after once hot rolling and annealing. The as-cast strip of Al-20Vol%SiCp could be coiled at the diameter of 460mm.

Semisolid Roll Casting of Aluminum Alloy Strip and Its Properties

2006 ◽  
Vol 116-117 ◽  
pp. 379-382 ◽  
Author(s):  
Ryoji Nakamura ◽  
Hideki Inui ◽  
Hisaki Watari ◽  
Shinji Kumai
Keyword(s):  
Tension Test ◽  
Semisolid Slurry ◽  
Alloy Strip ◽  
Proof Stress ◽  
Cooling Slope ◽  
Roll Casting ◽  
Heat Treated ◽  
Cold Rolled ◽  
Twin Roll Caster ◽  
Twin Roll

A356 was cast into the strip by the semisolid strip casting using an unequal diameter twin roll caster. This process was one of the rheocasting. The semisolid slurry was made by a cooling slope. Solid fraction was about 5%. The casting speed was 20 m/min, and the thickness was 4.4 mm. The as-cast strip could be cold rolled down to 1 mm. The result of tension test of 1mm-thickness-T4 heat-treated strip was as below. Tensile stress was 223 MPa, 0.2 proof stress was 123 MPa and elongation was 21.8%. Deep drawing could be operated to 1 mm-thickness T4 sheet, and L.D.R was attained to 2.0. In some condition, 180 degrees bending could be operated without crack at outer surface. These results mean that semisolid roll cast A356 strip may be able to use for press forming.

Casting of Al-25%Si Strip Using a Vertical Type Twin Roll Caster

2011 ◽  
Vol 239-242 ◽  
pp. 1944-1947
Author(s):  
Toshio Haga ◽  
Hideto Harada ◽  
Shinji Kumai ◽  
Hisaki Watari
Keyword(s):  
High Speed ◽  
Strip Casting ◽  
Cast Strip ◽  
Roll Casting ◽  
Twin Roll Caster ◽  
Roll Gap ◽  
Hot Rolled ◽  
Semisolid Casting ◽  
Twin Roll

Strip casting of Al-25%Si was tried using the vertical type high speed twin roll caster. Some devices were adopted to enable the strip casting of Al-25%Si. Control of the roll gap, semisolid casting and non-use of the lubricant were useful devices to cast Al-25%Si strip. Roll-casting-ability of the Al-25%Si was discussed. The strip could be cast at 20m/min and 40m/min. As-cast strip was hot rolled down to 1mm by one pass. Bulging was tried at 550°C and it was able.

Roll Casting of Recycled AA5182

2011 ◽  
Vol 121-126 ◽  
pp. 4667-4670
Author(s):  
Toshio Haga ◽  
Kosuke Komeda ◽  
Kenta Mtsuoka ◽  
Shinji Kumai ◽  
Hisaki Watari
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
High Speed ◽  
Model Alloy ◽  
Drawing Ratio ◽  
Roll Speed ◽  
Roll Casting ◽  
Twin Roll Caster ◽  
Twin Roll ◽  
Fe Addition

Roll casting of the model alloy of recycled AA5182 aluminum alloy was investigated. Fe up to 0.6% was added to the AA5182 to make the model alloys of recycled AA5182. Increase of 0.6% of Fe means that the recycle was three times operated. A vertical type high speed twin roll caster was used. Some devices were operated on the twin roll caster to increase the cooling rate in order to make impurity fine. The roll speed could be increased up to 80m/min. The roll-castability did not become worse by the addition of the Fe. The LDR (limiting Drawing Ratio) was 1.9 when the Fe addition was 0.6. The deterioration of the mechanical properties by the addition of impurity Fe was very small.

Roll Casting and Die Casting of Si-Added Al-Mg Alloy

2020 ◽  
Vol 1007 ◽  
pp. 12-17
Author(s):  
Toshio Haga ◽  
Shinichiro Imamura ◽  
Hiroshi Fuse ◽  
Hisaki Watari ◽  
Shinichi Nishida
Keyword(s):  
High Speed ◽  
Die Casting ◽  
Sheet Forming ◽  
Mg Alloy ◽  
Tension Tests ◽  
Roll Casting ◽  
Cold Rolled ◽  
Twin Roll Caster ◽  
Si Content ◽  
Twin Roll

Si ranging from 0.2 mass% to 2.0 mass% was added to Al-5%Mg alloy (5182) and strip was cast by a vertical type high-speed twin-roll caster at a speed of 80 m/min. The as-cast strip was cold-rolled down to 1 mm thickness and annealed. The mechanical properties were investigated using cup tests and tension tests. The limiting draw ratio (LDR) of the 5182 alloy was 2.0 and the LDR became smaller as the Si content increased. When the Si content was 2.0 mass%, the LDR was 1.8, which shows that Si-added 5182 can be used for sheet forming, if the Si content is less than 2.0 mass%. The tensile strength and elongation were almost constant when the Si content was less than 1 mass%, but decreased at 2.0 mass% Si. However, the elongation was greater than 20% at 2.0 mass% Si. For die casting, 2.0 mass% Si was determined as the appropriate content from the results of the tension tests. When the Si content is in the range from 1.0 mass% to 2.0 mass%, then the Si added Al-5%Mg has the ability to be used for both die casting and sheet forming.