scholarly journals Long-Term Efficiency of Two Organic Corrosion Inhibitors for Reinforced Concrete

2010 ◽  
Vol 636-637 ◽  
pp. 1059-1064 ◽  
Author(s):  
E.V. Pereira ◽  
R.B. Figueira ◽  
Manuela M. Salta ◽  
I.T.E. Fonseca
Keyword(s):  
Reinforced Concrete ◽  
Environmental Conditions ◽  
Corrosion Inhibitors ◽  
Electrochemical Techniques ◽  
Concrete Structures ◽  
Concrete Slabs ◽  
Reinforced Concrete Structures ◽  
Reinforcement Corrosion ◽  
Organic Corrosion Inhibitors

In this paper the efficiency of two organic corrosion inhibitors, a migratory and an admixture inhibitor, was evaluated by electrochemical techniques in solutions simulating the interstitial electrolyte of concrete and on concrete slabs exposed to natural environmental conditions over a five-year period. From obtained results, the usefulness of the two products is discussed aiming its application in new structures to prevent chlorides induced corrosion and as a curative method for repairing reinforced concrete structures contaminated with chlorides and affected by reinforcement corrosion.

scholarly journals Long-Term Durability of Marine Reinforced Concrete Structures

2020 ◽  
Vol 8 (4) ◽  
pp. 290 ◽  
Author(s):  
Robert E Melchers
Keyword(s):  
Reinforced Concrete ◽  
Experimental Work ◽  
Good Condition ◽  
Concrete Structures ◽  
The Other ◽  
Reinforced Concrete Structures ◽  
Reinforcement Corrosion ◽  
Physical Damage ◽  
Analysis And Design

The sustainability of reinforced concrete is critical, particularly for structures exposed to marine environments. Chlorides are implicated in causing or accelerating reinforcement corrosion and potentially earlier expensive repairs, yet there are many older reinforced concrete structures in good condition for many decades despite very high chloride levels at the reinforcement. The reasons for this are reviewed briefly, together with recent experimental work that better defines the role of chlorides. One is initiation of reinforcement corrosion but only through localized pitting at air-voids in concrete at the interface with the steel reinforcement. These tend to be small or negligible for high quality well-compacted concretes. The other role for chlorides has been shown, in experimental work, to accelerate the long-term loss of concrete alkali material. On the other hand, a review of practical experience shows that what has been termed chloride-induced reinforcement corrosion often is not that at all, but is the end-product of factors that impair the protective nature of the concrete. As reviewed herein, these include poor compaction, physical damage to concrete cover, concrete shrinkage, and alkali-aggregate reactions. The various observations presented are important for the proper understanding, analysis, and design of durable reinforced concrete structures exposed to chloride-rich environments.

Improvement Of Curvilinear Diagrams Of Concrete Deformation

2019 ◽  
pp. 99-104
Keyword(s):  
Reinforced Concrete ◽  
Peak Load ◽  
Experimental Studies ◽  
Concrete Structures ◽  
Deformation Model ◽  
Reinforced Concrete Structures ◽  
Significant Difference ◽  
Deformation Diagrams

Problems when calculating reinforced concrete structures based on the concrete deformation under compression diagram, which is presented both in Russian and foreign regulatory documents on the design of concrete and reinforced concrete structures are considered. The correctness of their compliance for all classes of concrete remains very approximate, especially a significant difference occurs when using Euronorm due to the different shape and sizes of the samples. At present, there are no methodical recommendations for determining the ultimate relative deformations of concrete under axial compression and the construction of curvilinear deformation diagrams, which leads to limited experimental data and, as a result, does not make it possible to enter more detailed ultimate strain values into domestic standards. The results of experimental studies to determine the ultimate relative deformations of concrete under compression for different classes of concrete, which allowed to make analytical dependences for the evaluation of the ultimate relative deformations and description of curvilinear deformation diagrams, are presented. The article discusses various options for using the deformation model to assess the stress-strain state of the structure, it is concluded that it is necessary to use not only the finite values of the ultimate deformations, but also their intermediate values. This requires reliable diagrams "s–e” for all classes of concrete. The difficulties of measuring deformations in concrete subjected to peak load, corresponding to the prismatic strength, as well as main cracks that appeared under conditions of long-term step loading are highlighted. Variants of more accurate measurements are proposed. Development and implementation of the new standard GOST "Concretes. Methods for determination of complete diagrams" on the basis of the developed method for obtaining complete diagrams of concrete deformation under compression for the evaluation of ultimate deformability of concrete under compression are necessary.

DEVELOPMENT OF EMBEDDED MINI-SENSOR FOR DIAGNOSIS OF CORROSION OF STEEL REINFORCEMENT IN CONCRETE NONDESTRUCTIVELY

2016 ◽  
Vol 3 (2) ◽  
Author(s):  
Mohamed A. Ismail ◽  
Han-Seung Lee ◽  
Mohd Warid Hussin
Keyword(s):  
Reinforced Concrete ◽  
Polarization Resistance ◽  
Concrete Structures ◽  
Steel Reinforcement ◽  
Reinforced Concrete Structures ◽  
Chloride Ingress ◽  
Reinforcement Corrosion ◽  
Maintenance And Rehabilitation ◽  
Corrosion Of Steel ◽  
Non Destructive

Corrosion of steel reinforcement embedded in concrete is one of the main causes of degradation of reinforced concrete structures. Degradation occurs in reinforced concrete structures from corrosion caused by the Chloride ingress into concrete. That degradation has a severe impact on the structure in terms of maintenance and rehabilitation costs. Therefore, early detection of reinforcement corrosion is important for efficient maintenance, repair and planning. Meanwhile, the evaluation of the corrosion of reinforcement by non-destructive measurements have been used a lot. In particular CM-II (corrosion meter) is used to measure the polarization resistance, but has some disadvantages. Embedded mini-sensor has been developed in order to overcome these disadvantages. In this study, measurement of corrosion by using the mini-sensor is compared with the measured results by CM-II to verify the validity of the newly developed mini senor. Results show that there are agreement in trends of the parameters measured and as such the developed mini sensor has a promising start to be used.

Sign in / Sign up

Export Citation Format

Share Document