Abstract
The materials used previously for steam generator tubes around the world have been replaced and will be replaced by Alloy 690 given its improved corrosion resistance relative to that of Alloy 600. However, studies of the high- temperature creep and creep-rupture characteristics of steam generator tubes made of Alloy 690 are insufficient compared to those focusing on Alloy 600. In this study, several creep tests were conducted using half tube shape specimens of the Alloy 690 material at temperatures ranging from 650 to 850C and stresses in the range of 30 to 350 MPa, with failure times to creep rupture ranging from 3 to 870 hours. Based on the creep test results, creep life predictions were then made using the well-known Larson Miller Parameter method. Steam generator tube rupture tests were also conducted under the conditions of a constant temperature and pressure ramp using steam generator tube specimens. The rupture test equipment was designed and manufactured to simulate the transient state (rapid temperature and pressure changes) in the event of a severe accident condition. After the rupture test, the damage to the steam generator tubes was predicted using a creep rupture model and a flow stress model. A modified creep rupture model for Alloy 690 steam generator tube material is proposed based on the experimental results. A correction factor of 1.7 in the modified creep rupture model was derived for the Alloy 690 material. The predicted failure pressure was in good agreement with the experimental failure pressure.
Evaluation of Surface Oxidation Mechanism of Alloy 600 in a Simulated Primary Water of Pressurized Water Reactors using Analytical Transmission Electron Microscopy